ASTM A268 TP410S ASME SA268 TP410S Stainless Steel Tubing

ASTM A268 TP410S Stainless Steel Tubing and S41008 1.4000 Pipes

Guanyu Tube Can Manufacturing both Seamless and Welded ASTM A268 TP410S, OD Range 6 – 530mm Thickness range 0.5 – 30mm, Maximum Length in 25000mm. Please send your inquiry to us for more details. We have a large quanity of 410 410S Stainless Steel Tubes and Pipes Stock in China to support urgent projects.

ASTM A268 TP 410S ASME SA268 TP410S stainless steel is Contains lower carbon than Type 410, offers improved weldability but lower hardenability. Type 410S Stainless Steel is a general purpose corrosion and heat resisting chromium steel recommended for corrosion resisting applications. The low carbon and a small alloy addition minimize austenite formation at high temperature which restricts the ability of 410S to harden. 410S remains soft and ductile even when rapidly cooled from elevated temperature. This helps prevent cracking when the alloy is exposed to high temperature or during welded. 410S is completely ferritic in the annealed condition.

A268 TP410S is not hardenable by heat treatment. It is annealed in the 1600 – 1650°F (871 – 899°C) range and then air cooled, mainly to relieve cold working strains. 410S stainless steel can be easily formed by drawing, spinning, bending and roll forming. This non-hardening characteristic helps prevent cracking when the alloy is exposed to high temperatures or welded. It exhibits adequate corrosion resistance similar to 410 and good oxidation resistance.

A small titanium addition minimizes austenite formation at high temperature, thereby restricting the alloy’s ability to harden. This non-hardening characteristic retards formation of hardening cracks when the steel is welded. 410S is Ferro-magnetic.

Because 410S cools from elevated temperatures without hardening, it is particularly useful for annealing boxes, quenching racks, oxidation resistant partitions and other high-temperature units. It also is used in the petrochemical industry for tower packing and distillation trays. A268 410S is generally considered to be weldable by the common fusion and resistance techniques. Special consideration is required to avoid brittle weld fracture.Type 410S provides adequate resistance to atmospheric corrosion, fresh water, mild acids and alkalies, and some other chemicals.

Applications
Standard
Chemical Analysis
Corrosion Resistance
Oxidation Resistance
Physical Properties
Mechanical Properties
Formability
Welding
Heat Treatment
Surface Preparation
Machining
304/304L/304LN/304H Tubing and Pipe

ASTM A268 410S Stainless Steel Tubing Size range:

Stock of ASTM A268 TP410S TUBE , ASTM A268 410S SS SEAMLESS TUBE

ASME SA268 410S Stainless Steel Export Countries

Related References:
1. Superferritic Stainless Steel
2. Ferritic Ferrite Stainless Steel
3. Ferritic Stainless Steel Grades Comparison Table
4. Compared with the ferritic stainless steel, duplex stainless steel vulnerable