ASTM A660 Centrifugally Cast Carbon Steel Pipe
ASTM A660 Standard Specification for Centrifugally Cast Carbon Steel Pipe for High-Temperature Service covers carbon steel pipe made by the centrifugal casting process intended for use in high-temperature, high-pressure service. This pipe shall be suitable for fusion welding, bending, and other forming operations. Grades for carbon steel shall conform to the required chemical composition for carbon, manganese, phosphorous, sulfur, and silicon. Manufacturing of the material shall be done by machining and heat treatment. Pyrometers shall be used to control the furnace temperatures. Tensile strength properties shall conform to the required values for tensile strength, elongation, and reduction of area. Mechanical properties shall conform to the following: transverse or longitudinal tension test; flattening test; and hydrostatic test.
This specification covers carbon steel pipe made by the centrifugal casting process intended for use in high-temperature, high-pressure service. Pipe ordered under this specification shall be suitable for fusion welding, bending, and other forming operations.
Several grades of carbon steels are covered. Their compositions are given in Table 1.
Supplementary requirements (S1 to S9) of an optional nature are provided. The supplementary requirements call for additional tests to be made, and when desired shall be so stated in the order, together with the number of such tests required.
The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of each other. Combining values from the two systems may result in nonconformance with the specification.
ASTM Standards
ASTM A530/A530M Specification for General Requirements for Specialized Carbon and Alloy Steel Pipe
ASTM E94 Guide for Radiographic Examination
ASTM E114 Practice for Ultrasonic Pulse-Echo Straight-Beam Contact Testing
ASTM E125 Reference Photographs for Magnetic Particle Indications on Ferrous Castings
ASTM E142 Method for Controlling Quality of Radiographic Testing
ASTM E186 Reference Radiographs for Heavy-Walled (2 to 412-in. (50.8 to 114-mm)) Steel Castings
ASTM E381 Method of Macroetch Testing Steel Bars, Billets, Blooms, and Forgings
ASTM E446 Reference Radiographs for Steel Castings Up to 2 in. (50.8 mm) in Thickness
ANSI Standards
B46.1 Surface Texture
|