Tubi senza saldatura della lega di Hastelloy C4 ASTM B619 B622 B626 N06455 N06455

Lega Hastelloy C4 ASTM B619 B622 B626 N06455 alloy is a nickel-chromium-molybdenum alloy with outstanding ad alta temperatura stability as evidenced by high ductility and resistenza alla corrosione even after aging in the 1200 to 1900°F (649 to 1038°C) range. This alloy resists the formation of grain-boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in the as saldato condition. C-4 alloy also has excellent resistance to fessurazione da stress-corrosione and to oxidizing atmospheres up to 1900°F (1038°C).

Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 lega has exceptional resistance to wide variety of chemical process environments. These include hot contaminated mineral acids, solvents, chlorine nd chlorine contaminated media (organic and inorganic), dry chlorine, acido formico e acido acetico, acetic anhydride, and acqua di mare and brine solutions.

Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 N06455 alloy can be forged, hot-upset, and impact extruded. Although the alloy tends to temprare il lavoro, it can be successfully deep-drawn, spun, press formed or punched. All of the common methods of welding can be used to weld Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 N06455 alloy, although the oxy-acetylene and submerged arc processes are not recommended when the fabricated item is intended for use in corrosione service. Special precautions should be taken to avoid excessive calore input.

Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 N06455 Applications
This alloy is used to manufacture chemical process equipment, especially for process use at high temperatures where stainless steel do not have adequate strength and/or resistenza alla corrosione.

Hastelloy C4 Alloy Machinability
Machinable by conventional techniques.

Hastelloy C4 Alloy Forming
Readily formed by conventional methods.

Hastelloy C4 Alloy Welding
All of the common methods of welding apply to this alloy. However excessive heat input should be avoided and submerged arc or oxy-acetylene welding should not be used as they can degrade corrosion resistance.

Hastelloy C4 Alloy Heat Treatment
Solution annealed at 1950 F and rapid quench. This is the normal condition in which product forms are supplied.

Hastelloy C4 Alloy Forging
The alloy can be hot forged at temperatures of 2150 F to 1750 F.

Hastelloy C4 Alloy Hot Working
Can be hot worked or hot extruded similar to stainless steels.

Hastelloy C4 Alloy Cold Working
Readily cold worked by conventional means.

Hastelloy C4 Alloy Annealing
Solution anneal at 1950 F followed by rapid quench.

Hastelloy C4 Alloy Aging
May be aged (after solution heat treatment) at 1200 F for 10 hours to somewhat improve duttilità e resistenza allo snervamento without adversely affecting the ultimate tensile strength.

Hastelloy C4 Alloy Hardening
Hardened by cold working only, but normally used in the solution annealed condition .