DIN 17456 17458 Diagrama compoziției chimice
| C | C | Si | Si | Mn | Mn | P | P | S | S | Cr | Cr | Ni | Ni | Mo | Mo | N | N | Cu | Cu | Ti | Ti | Nb | Nb | ||
| min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | ||
| DIN 17456 | 1.4301 | 0.00 | 0.070 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 17.00 | 19.00 | 8.00 | 10.50 | ||||||||||
| DIN 17456 | 1.4306 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 18.00 | 20.00 | 10.00 | 12.00 | ||||||||||
| DIN 17456 | 1.4311 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 17.00 | 19.50 | 8.50 | 11.50 | ||||||||||
| DIN 17456 | 1.4541 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 17.00 | 19.00 | 9.00 | 12.00 | 5*C | 0.70 | ||||||||
| DIN 17456 | 1.4550 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 17.00 | 19.00 | 9.00 | 12.00 | 10*C | 1.00 | ||||||||
| DIN 17456 | 1.4401 | 0.00 | 0.070 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 16.50 | 18.50 | 10.00 | 13.00 | 2.00 | 2.50 | ||||||||
| DIN 17456 | 1.4404 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 16.50 | 18.50 | 10.00 | 13.00 | 2.00 | 2.50 | ||||||||
| DIN 17456 | 1.4571 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 16.50 | 18.50 | 10.50 | 13.50 | 2.00 | 2.50 | 5*C | 0.70 | ||||||
| DIN 17456 | 1.4429 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 16.50 | 18.50 | 11.00 | 14.00 | 2.50 | 3.00 | ||||||||
| DIN 17458 | 1.4301 | 0.00 | 0.070 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 8.50 | 10.50 | ||||||||||
| DIN 17458 | 1.4306 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 10.00 | 12.50 | ||||||||||
| DIN 17458 | 1.4311 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 8.50 | 11.50 | 0.12 | 0.22 | ||||||||
| DIN 17458 | 1.4541 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 5*C | 0.80 | ||||||||
| DIN 17458 | 1.4550 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.50 | 12.00 | 10*C | 1.00 | ||||||||
| DIN 17458 | 1.4401 | 0.00 | 0.070 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.50 | 18.50 | 10.50 | 13.50 | 2.00 | 2.50 | ||||||||
| DIN 17458 | 1.4404 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.50 | 18.50 | 11.00 | 14.00 | 2.00 | 2.50 | ||||||||
| DIN 17458 | 1.4571 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.50 | 18.50 | 10.50 | 13.50 | 2.00 | 2.50 | 5*C | 0.80 | ||||||
| DIN 17458 | 1.4429 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.025 | 16.50 | 18.50 | 11.50 | 14.50 | 2.50 | 3.00 | 0.14 | 0.22 |
Diagrama compoziției oțelului inoxidabil
Compoziția chimică a oțelului inoxidabil BS 970
BS 3100 Compoziția chimică a oțelului inoxidabil
BS 6744 Compoziția și mecanica oțelului inoxidabil
EN 10088-2 Compoziție chimică Oțel inoxidabil
Compoziția chimică a aliajului Hastelloy
Compoziția chimică a aliajului de nichel Monel
EN 10302 Compoziția chimică a oțelurilor rezistente la fluaj
EN 10028-7 Compoziția chimică a oțelului inoxidabil plat
EN 10283 Compoziția chimică a oțelului inoxidabil turnat
EN 10095 Compoziția chimică a oțelurilor rezistente la căldură
EN 10269 Compoziția chimică a oțelului inoxidabil
EN 10296-2 Compoziția chimică a oțelului inoxidabil
BS 3146-2 Compoziția chimică a oțelului inoxidabil
Compoziția chimică a oțelului inoxidabil rezistent la căldură AISI și UNS
EN 10216-5 Compoziția chimică a oțelurilor inoxidabile
Diagrama compoziției chimice JIS G3459 G3463