DIN 17459 specifies technical delivery conditions for seamless circular tubes made from high temperature austenitic stainless steel as specified in table. 1. Such stainless steel tube are intended primarily to be used in high-pressure applications where elevated temperature and high mechanical stresses are involved (e.g. in the construction of pressure boilers, pressure vessels, pipelines, and in the chemical industry). Material Chemical composition (%) degignation number C Si Mn P S Ni Cr Mo Ni others X 6 CrNi 18 11 1.4948 0.04 to 0.08 ≤0.75 ≤2.0 0.035 0.015 17.0 to 19.0 – 10.0 to 12.0   X 3 CrNiN 18 11 1.4949 ≤0.04 ≤0.75 ≤2.0 0.035 0.015 0.10 to 0.18 17.0 to 19.0 0.50 to 0.60 9.5 to 11.5   X 8 CrNiTi 18 10 1.4941 0.04 to 0.10 ≤0.75 ≤2.0 0.035 0.015 17.0 to 18.5 – 9.5 to 11.5 Ti: ≥5 x %Cto ≤  0.80B: 0.0015 to 0.0050 X6CrNiMo 17 13 1.4919 0.04 to 0.08 ≤0.75 ≤2.0 0.035…

The table shown is based on the reference data presented in EN 10088-1. Only a sample of the information available is shown. This is intended to show the scope of information available through representative figures for the most commonly used stainless steel tube types. A separate table indicates some of the grades that have been grouped together.Physical Properties Table Steel Types (AISI) Density Modulus Expansion Conductivity Specific Heat Resistivity . . 20C 400C . . . . Ferritic stainless steels 410S 7700 220 195 10.5 30 460 0.60 430 7700 220 195 10.0 25 460 0.70 444 7700 220 195 10.4 23 430 0.8 Martensitic and precipitation hardening stainless steels 410 7700 215 190 10.5 30 460 0.60 440 7700 215 190 10.4 15 430 0.8 630 7800 200 170 10.9 16 500 0.71 Austenitic stainless steel 304 7900 200 172 16.0 15 500 0.73 316 8000 200 172 16.0 15 500 0.75 ‘6%Mo’ 8000…

ASTM A595 Standard Specification for Steel Tubes, Low-Carbon or High-Strength Low-Alloy, Tapered for Structural Use covers three grades of seam-welded, round, tapered steel tubes for structural use. Grades A and B are of low-carbon steel or high-strength low-alloy steel composition and Grade C is of weather-resistance steel composition. The tube steel shall be hot-rolled aluminum-semikilled or fine-grained killed sheet or plate manufactured by one or more of the following processes: open-hearth, basic-oxygen, or electric-furnace. The tubes shall be made from trapezoidal sheet or plate that is preformed and then seam welded. They shall be brought to final size and properties by roll compressing cold on a hardened mandrel. A tensile test shall be done to determine the yield strength and the ultimate tensile strength of the tubes. 1.1 This specification covers three grades of seam-welded, round, tapered steel tubes for structural use. Grades A and B are of low-carbon steel or high-strength low-alloy steel composition and Grade C…

ASTM A790 acoperă țevile din oțel inoxidabil duplex ferritic/austenitic sudate fără sudură și cu cusătură dreaptă pentru servicii corozive generale, cu accent deosebit pe rezistența la fisurarea prin coroziune sub tensiune. Țeava trebuie să fie fabricată prin procedeul de sudare fără sudură sau automat, fără adăugarea de metal de adaos în operația de sudare. Trebuie efectuată o analiză termică pentru a determina procentajele elementelor specificate. Încercările la tracțiune, încercările de întărire, încercările de aplatizare, încercările hidrostatice și încercările electrice nedistructive trebuie să fie efectuate în conformitate cu cerințele specificate. Acest rezumat este un scurt rezumat al standardului la care se face referire. Este doar informativ și nu constituie o parte oficială a standardului; pentru utilizarea și aplicarea acestuia trebuie să se facă trimitere la textul integral al standardului. Prezenta specificație se referă la țevile din oțel inoxidabil ferritic/austenitic sudate fără sudură și cu cusătură dreaptă, destinate serviciilor corozive generale, cu accent deosebit pe rezistența la fisurarea prin coroziune sub tensiune. Aceste oțeluri sunt susceptibile la fragilizare dacă sunt utilizate pentru perioade prelungite la temperaturi ridicate. Cerințe suplimentare opționale...

DSTU B A.3.2-12:2009 SSBP. Sisteme de ventilație. Zagalni vimogi DSTU GOST 166:2009 (ISO 3599-76) Calibre. Specificații tehnice ( GOST 166-89 (ISO 3599-76), IDT) DSTU EN 473:2012 Control neinvaziv. Calificarea și certificarea personalului. Dispoziții generale ( EN 473 :2008, IDT) DSTU 2680-94 Țevi laminate fără sudură din oțel și aliaje. Terminologia și identificarea defectelor de suprafață DSTU 2841-94 ( GOST 27809-95 ) Chavun i oțel. Metode de analiză spectrografică DSTU 3124-95 Țevi din oțel și aliaje. Legătura și pregătirea probelor pentru depozitul chimic. Dispoziții de bază DSTU 4179-2003 Benzi vibratoare metalice. Competențe tehnice ( GOST 7502-98 , MOD) DSTU GOST 6507:2009 Micrometre. Specificații DSTU 7238:2011 Sistem de standarde de siguranță. Crearea unui zakhist colectiv pentru oamenii muncii. Zagalni vimogi ta clasificare DSTU 7239:2011 Sistem de standarde de siguranță. Atribuirea unui zakhist individual. Zagalni vimogi ta clasificare DSTU ISO 7438:2005 Materiale metalice. Încercare pentru zgin (ISO 7438:1985, IDT) DSTU ISO 8496-2002 Materiale metalice. Trompetă. Încercări pentru smulgerea inelelor cu două tije paralele (ISO 8496:1988, IDT) DSTU GOST 12344:2005 Oțeluri aliate și înalt aliate. Metode pentru proiectarea vugletsiu ( GOST 12344-2003 ,...

Inspecția suprafeței exterioare a țevilor se efectuează vizual, fără utilizarea de mijloace de mărire. Suprafața interioară a conductelor cu un diametru interior de 70 mm sau mai mare se inspectează cu ajutorul unui periscop sau al unor sisteme videoscopice. Este permisă inspectarea suprafeței interioare a țevilor fără utilizarea de instrumente, folosind dispozitive de iluminare la ambele capete ale țevii împotriva luminii. Pentru țevile cu un diametru interior mai mic de 70 mm, precum și pentru țevile cu un diametru interior de 70 mm sau mai mare care nu au fost inspectate cu un periscop, producătorul garantează că suprafața interioară a țevilor îndeplinește cerințele prezentelor specificații pe baza rezultatelor satisfăcătoare ale inspecției cu ultrasunete 100%. Clasificarea defectelor este efectuată în conformitate cu DSTU 2680 (OST 14-82 [ 18 ]). Adâncimea defectelor este verificată după limare și măsurarea ulterioară. Peretele...

În domeniul oțelului inoxidabil, de obicei 304 este numit TP304, 304L este numit 304L, 316L este numit TP316L. De exemplu: ASTM A312 TP304, ASME SA213 TP304L, ASME SA213 TP316L. Deci, ce înseamnă "TP"? TP înseamnă tip. Motivul este că AISI (American Iron and Steel Institute) clasifică oțelul inoxidabil în funcție de tip. Din același motiv, uneori 304, 304, L316L, vor fi numite AISI 304, AISI 304L, AISI 316L.

OD: 17.15 - 508mm (3/8 INCH la 20 INCH)WT: 0.5 - 60 mm, Schedule 10s, 20, 40s, 40, 60, 80s, 80, 100, 120, 140, 160, XXH.Capacitatea de producție: 500 MT / lună Guanyu Tube este producător specializat de ASTM A312 TP304, ASTM A312 TP304L, ASTM A312 TP316, ASTM A312 TP316L, ASTM A312 TP321, ASTM A312 TP310S, ASTM A312 TP304 TP304L TP304H TP316 TP316L TP317L TP321 TP316Ti TP347 TP347H TP310S TP309S Furnizor de țevi din oțel inoxidabil. Acesta este emis sub denumirea fixă ASTM A312; numărul imediat următor denumirii indică anul adoptării inițiale sau, în caz de revizuire, anul ultimei revizuiri. Un număr în paranteze indică anul ultimei reaprobări. Un epsilon superscript indică o modificare editorială de la ultima revizuire sau reaprobare. Aceasta se referă la țevile din oțel inoxidabil austenitic sudate fără sudură, cu cusătură dreaptă și puternic prelucrate la rece, pentru temperaturi ridicate și servicii corozive generale. Atunci când criteriul de încercare la impact pentru un serviciu la temperatură scăzută ar fi...

Compoziția chimică a ASTM A213 / ASME SA 213 317 317L 317LM 317LMN Grade de oțel inoxidabil C Mn P Sulf Si Cr Nichel Mo N Cu Greutate % 317 S31700 18.00 11.00 3.00 Min. 0.08 2.00 0.045 0.030 1.00 20.00 15.00 4.00 Max. 317L S31703 18.00 11.00 3.00 Min. 0.035 2.00 0.045 0.030 1.00 20.00 15.00 4.00 Max. 317LM S31725 18.00 13.50 4.00 Min. 0.03 2.00 0.045 0.030 1.00 20.00 17.50 5.00 0.20 0.75 Max 317LMN S31726 17.00 13.50 4.00 0.10 Min. 0.03 2.00 0.045 0.030 1.00 20.00 17.50 5.00 0.20 0.75 Max. EN 10216-5 1.4439 16.50 12.50 4.00 Min. 0.030 2.00 0.040 0.015 1.00 18.50 14.50 5.00 Max. EN 10217-7 1.4438 17.50 13.00 3.00 Min. 0.030 2.00 0.045 0.030 1.00 19.50 16.00 4.00 Max. Proprietăți mecanice ale tuburilor din oțel inoxidabil 317 317L Tensiune...

Compoziția chimică a ASME SA213 304 304L 304H și EN 10216-5 1.4301 1.4307 1.4948 Grad - C Mn Si P S Cr Mo Ni N 304/S30400 min.max. -0.08 -2.0 -1.00 -0.045 -0.030 18.0-20.0 - 8.0-11.0 - EN 10216-5 1.4301 min.max. -0.07 -2.0 -1.00 -0.040 -0.015 17.00-19.5 - 8.0-10.5 -0.11 304L/S30403 min.max. -0.035 -2.0 -1.00 -0.045 -0.030 18.0-20.0 - 8.0-12.0 - EN 10216-5 1.4307 min.max. -0.030 -2.0 -1.00 -0.040 -0.015 17.5-19.5 - 8.0-10.0 -0.11 304H /S30409 min.max. 0.04-0.10 -2.0 -1.00 -0.045 -0.030 18.0-20.0 - 8.0-11.0 - EN 10216-5 1.4948 min.max. 0.04-0.08 -2.0 -1.00 -0.035 -0.015 17.0-19.0 - 8.0-11.0 -0.11 TP304L Proprietăți generaleTP304L Compoziție chimicăTP304L Rezistență la coroziuneTP304L Proprietăți fiziceTP304L Proprietăți mecaniceTP304L SudareTP304L Tratament termicTP304L Curățare304304/304L/304LN/304H Tuburi și țevi304/304L Tuburi din oțel inoxidabil

Suntem producător specializat de ASME SA249 ASTM A249 TP304, ASTM A249 TP304L, ASTM A249 TP304H, ASTM A249 TP316, ASTM A249 TP316L, ASTM A249 TP316H, ASTM A249 TP316Ti, ASTM A249 TP321 TP321H, ASTM A249 TP309H TP309S, ASTM A249 TP310S TP 310H, ASTM A249 TP347 tuburi sudate și ASTM A249 țevi sudate. Ce este ASTM A249 ASME SA249? ASTM A249 este o specificație standard pentru tuburi sudate cu grosime nominală a peretelui și tuburi sudate puternic prelucrate la rece fabricate din oțel austenitic cu diferite grade destinate utilizării ca cazan, supraîncălzitor, schimbător de căldură sau tuburi condensatoare. Analiza termică și a produselor trebuie să fie conformă cu cerințele privind compoziția chimică pentru carbon, mangan, fosfor, sulf, siliciu, crom, nichel, molibden, azot, cupru și altele. Toate materialele trebuie să fie furnizate în stare tratată termic în conformitate cu temperatura de soluție și metoda de călire necesare. ASTM A249 Tubing Test Items Când tratamentul termic final este într-un cuptor continuu, numărul...

Standard de testare PT Organizația Internațională de Standardizare (ISO) ISO 3059, Testare nedistructivă - Testare prin penetrare și testare cu particule magnetice - Condiții de vizualizare ISO 3452-1, Testare nedistructivă. Încercarea prin penetrare. Partea 1. Principii generale. Principii generale ISO 3452-2, Încercări nedistructive - Încercări prin penetrare - Partea 2: Încercarea materialelor penetrante ISO 3452-3, Încercări nedistructive - Încercări prin penetrare - Partea 3: Blocuri de încercare de referință ISO 3452-4, Încercări nedistructive - Încercări prin penetrare - Partea 4: ISO 3452-5, Încercări nedistructive - Încercări prin penetrare - Partea 5: Încercări prin penetrare la temperaturi mai mari de 50 °C ISO 3452-6, Încercări nedistructive - Încercări prin penetrare - Partea 6: Încercări prin penetrare la temperaturi mai mici de 10 °C ISO 10893-4: Încercarea nedistructivă a tuburilor de oțel. Controlul prin penetrare cu lichid al tuburilor de oțel fără sudură și sudate pentru detectarea imperfecțiunilor de suprafață. ISO 12706, Încercări nedistructive - Încercări prin penetrare - Vocabular ISO 23277, Încercări nedistructive ale sudurilor - Încercări prin penetrare ale sudurilor - Niveluri de acceptare Comitetul European de Standardizare (CEN) EN 1371-1, Fundare - Inspecție prin penetrare cu lichid...

Ce este ASTM A269 și ASTM A312 / ASME SA312? ASTM A269 / A269M Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General Service ASTM A312 / A312M Standard Specification for Seamless, Welded, și puternic prelucrate la rece din oțel inoxidabil austenitic StandardItem ASTM A213 ASTM A269 ASTM A312 Grad 304 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H 304 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H 304 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H Rezistența la rupere (Mpa) ≥170；≥205 ≥170；≥205 ≥170；≥205 Rezistența la tracțiune (Mpa) ≥485；≥515 ≥485；≥515 ≥485；≥515 Alungire(%) ≥35 ≥35 ≥35 Test hidrostatic OD(mm) Presiune max(MPa) OD(mm) Presiune max(MPa) OD(mm) Presiune max(MPa) D<25.4, 7Mpa D<25.4, 7Mpa D≤88.9, 17MPa 25.4≤D<38.1, 10Mpa 25.4≤D<38.1, 10Mpa 38.1≤D<50.8, 14Mpa 38.1≤D<50.8, 14Mpa 50.8≤D<76.2， 17MPa 50.8≤D88.9, 19MPa 76.2≤D<127， 24MPa 76.2≤D<127， 24MPa D≥127, 31Mpa D≥127, 31Mpa P=220.6t/D...

C C Si Si Mn Mn P P S S Cr Cr Ni Ni Mo Mo N N Cu Cu Ti Ti Nb Nb min max min max min max min max min max min max min max min max min max min max min max min max min max DIN 17456 1.4301 0.00 0.070 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.00 8.00 10.50 DIN 17456 1.4306 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 18.00 20.00 10.00 12.00 DIN 17456 1.4311 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.50 8.50 11.50 DIN 17456 1.4541 0.00 0.080 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.00 9.00 12.00...

C C Si Si Mn Mn P P S S Cr Cr Ni Ni Mo Mo N N Cu Cu Ti Ti Nb Nb min max min max min max min max min max min max min max min max min max min max min max min max min max min max J3459 SUS304TP 0.00 0.080 0.00 1.00 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20.00 8.00 11.00 J3459 SUS304HP 0.040 0.100 0.00 0.00.75 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20.00 8.00 11.00 J3459 SUS304LTP 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20.00 9.00 13.00 J3459 SUS310STP 0.00 0.080 0.00 1.50 0.00 2.00 0.00 0.040 0.00 0.030 24.00 26.00 19.00 22.00 ...

ASTM B111 Specificație standard pentru tuburi de condensator fără sudură din cupru și aliaj de cupru și stoc de viroleASTM A213/A213M Specificație standard pentru tuburi fără sudură din oțeluri feritice și austenitice aliate pentru cazane, supraîncălzitoare, and Heat-Exchanger TubesASTM A269/A269M Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General ServiceASTM A249 - A249/A249M Specification fors Welded Austenitic Steel Boiler, Superheater, Heat Exchanger, and Condenser TubesASTM A179 - A179/A179M - Specification for Seamless Cold-Drawn Low-Carbon Steel Heat Exchanger Tubes and Condenser TubesASTM A214 - A214/A214M Specification for Electric-Resistance-Welded Carbon Steel Heat-Exchanger and Condenser TubesASTM A851 - A851 Specification for High-Frequency Induction Welded, Tuburi de condensator din oțel austenitic, neintoxicat Tub de condensatorAvantajul tubului din oțel inoxidabil în condensatorASTM Standard for Heat-Exchanger and Condenser TubesCondenser Tube SpecificationsDezvantajul tubului din oțel inoxidabil în condensatorDe ce condensatorul trebuie să utilizeze tuburi din oțel inoxidabil?Condensatoare mari pentru sisteme cu abur

Grad EN / UNS Dimensiuni Toleranțe Testare 1.4749/S44600 EN ISO 1127Metric: Nu este standardizat=NSI/ASME B 36.19 EN ISO 1127 ASTM A213/A 450 1.4959/N08811 / N08810 ANSI/ASME B 36.19 Finisat la rece: ASTM B 407 Finisat la cald: ASTM A999 Finisat la rece: ASTM B 407 Finisat la cald: ASTM B 407 1.4835/S30815/253MA1.4854/S35315/353MA ANSI/ASME B 36.19 ASTM A999 ASTM A312/A 999

Oțelurile inoxidabile sunt aliaje pe bază de fier care conțin de obicei cel puțin 11,5% crom. Alte elemente, nichelul fiind cel mai important, pot fi adăugate în combinație cu cromul pentru a obține proprietăți speciale. În general, rezistența la coroziune și la oxidare crește progresiv, deși nu proporțional, cu creșterea conținutului de crom. Țevile și tuburile din oțel inoxidabil sunt utilizate din diverse motive: pentru a rezista la coroziune și oxidare, pentru a rezista la temperaturi ridicate, pentru curățenie și costuri reduse de întreținere și pentru a menține puritatea materialelor care vin în contact cu inoxul. Caracteristicile inerente ale tuburilor din oțel inoxidabil permit proiectarea de sisteme de conducte cu pereți subțiri, fără teama de defectare timpurie din cauza coroziunii. Utilizarea sudurii prin fuziune pentru îmbinarea acestor conducte elimină necesitatea filetării. Oțelul inoxidabil de tip 304 este cea mai răspândită analiză utilizată pentru aplicații generale de tuburi și țevi rezistente la coroziune, este utilizat în...

Standarde EN: EN European Standard for Stainless Steel European EN Standard Grade Summary European Dimensional Tolerance Standard for Stainless Steel EN 10090 Chemical Composition of Valve Steel BS 970 Stainless Steel Chemical Composition BS 3100 1991 Cast Steel Chemical Composition BS 3100 Chemical Composition of Stainless Steel BS 1449-2 Chemical Composition of Stainless Steel BS Aerospace S100 Chemical Composition Mechanical Properties BS Aerospace S500 Chemical Composition Mechanical Properties EN 10204 Test Certificates for Stainless Steel EN 10302 Chemical Composition of Creep Resisting Steel EN 10302 Mechanical Properties of Creep Resisting Steel Tolerance to EN 10296-2 Tuburi sudate din oțel inoxidabil EN 10296-2 Compoziția chimică a oțelului inoxidabil EN 10296-2 Tuburi sudate din oțel inoxidabil Proprietăți mecanice Compoziția chimică a oțelului inoxidabil conform EN 10297-2 EN 10297-2 Proprietăți mecanice ale tuburilor din oțel inoxidabil Toleranțe conform EN 10297-2 pentru tuburi din oțel inoxidabil fără sudură EN 10269 Proprietăți mecanice ale oțelului inoxidabil la temperatura camerei EN 10269...

Standarde ASTM: ASTM Standard pentru țevi din oțel inoxidabil Țevi din oțel carbon Standard ASTM BS DIN Suedia ASTM B265 Proprietăți ale aliajului de titan ASTM B265 Compoziție chimică a aliajului de titan ASTM A48 Specificație standard pentru piese turnate din fontă cenușie ASTM A53 Țeavă din oțel standard Țeavă din oțel neagră acoperită cu zinc la cald ASTM A53 Țeavă ASME SA53 Țeavă din oțel Presiune maximă de lucru-ASTM A53 B Țevi din oțel carbon ASTM A 53 & ASTM A 106. Țevi negre sudate și fără sudură Țevi fără sudură din oțel carbon destinate funcționării la temperaturi ridicate ASTM A105 Standard pentru țevi forjate din oțel carbon ASTM A106 Țevi din oțel carbon pentru temperaturi ridicate ASTM A106 / A106M - 08 Specificație standard pentru țevi fără sudură din oțel carbon pentru temperaturi ridicateTemperature Service ASTM A134 Standard for Steel Pipe Electric-Fusion Arc-Welded ASTM A134 Specification for Steel Pipe Electric-Fusion Arc-Welded ASTM A135 Standard for Electric-Resistance-Welded Steel Pipe ASTM A139 Specification of Electric-Fusion-Welded Steel Pipe ASTM A139 Standard Electric-Fusion Arc-Welded Steel Pipe ASTM A148...

Guanyu Tube este producător specializat de ASTM A269 TP304, ASTM A269 TP304L, ASTM A269 TP316, ASTM A269 TP316L, ASTM A269 Tubing în China. Condiția de livrare în Bright Annealing sau Annealing Pickling și lustruire suprafață exterioară. Tuburile ASTM A269 includ în principal ASTM A269 TP316 Tuburi de instrumente din oțel inoxidabil, ASTM A269 TP316L Tuburi de instrumente din oțel inoxidabil, Tuburi hidraulice din oțel inoxidabil. ASTM A269 este emis sub denumirea fixă ASTM A269, numărul imediat următor denumirii indică anul adoptării inițiale sau, în caz de revizuire, anul ultimei revizuiri. Un număr în paranteze indică anul ultimei reaprobări. Un epsilon superscript indică o modificare editorială de la ultima revizuire sau reaprobare. Această specificație acoperă clasele de tuburi din oțel inoxidabil cu grosimea nominală a peretelui, pentru servicii generale de rezistență la coroziune și la temperaturi joase sau înalte, așa cum sunt desemnate în tabelul 1. Dimensiunile și grosimea tuburilor furnizate de obicei conform acestei specificații sunt de 1⁄4 in. (6,4 mm) în diametru interior și...

ASTM A269 și ASTM A249 sunt ambele aplicabile pentru țevi și tuburi sudate din oțel inoxidabil. ASTM A249 / A249M Specificație standard pentru tuburi sudate din oțel austenitic pentru cazane, supraîncălzitoare, schimbătoare de căldură și condensatoare. ASTM A269 / A269M Specificație standard pentru tuburi din oțel inoxidabil austenitic fără sudură și sudate pentru servicii generale. ASTM A249 ASTM A269 Diagrama comparativă Specificațiile ASTM A249 și ASTM A269 sunt două standarde pentru tuburile din oțel inoxidabil austenitic, există aceleași cerințe tehnice, dar și unele diferențe. Specificație ASTM A249 ASTM 269 Fabricarea tuburilor sudate sudate și fără sudură Aplicație CazanSupraîncălzitorSchimbător de căldurăCondensator Serviciul general Dimensiuni OD: maxim 304.8 mmSpaterea peretelui: 0.4 - 8.1 mm Diametru interior: minim 3.4 mm Grosimea peretelui: 0,51 mm ASTM / ASME ASTM A249 / A249MASME SA249 ASTM A269 / A269M Test de flanșă Test de flanșă Test de flanșă A249 VS A269 Domeniul de aplicare Tuburile sudate ASTM A249 sunt pentru cazan, supraîncălzitor, schimbător de căldură, sistem condensator,...

ASTM A789 ASME SA 789 S31803 S32205 S32101 S32750 S32760 S32304 S31500 S31260 Tuburi fără sudură Producător

ASTM A213 ASME SA213 TP304 TP304L TP309S TP310S TP316L TP316Ti TP321 TP317L TP347H Tub schimbător de căldură

Specificații pentru tuburi din oțel inoxidabil Table of Contents： Specificații ASTM pentru tuburi din oțel inoxidabil: Produse din fier și oțel Țevi din oțel, tuburi din oțel, fitinguri ASTM A1016 Specificație standard pentru cerințe generale pentru tuburi din oțel aliat ferritic, oțel aliat austenitic și oțel inoxidabil ASTM A999 Specificație standard pentru cerințe generale pentru țevi din oțel aliat și inoxidabil A 213 / A 213M Țevi fără sudură din oțel aliat ferritic și austenitic pentru cazane, supraîncălzitoare și schimbătoare de căldură SA 240 / SA 240M Specificație standard pentru plăci, tablă și plăci din oțel inoxidabil cu crom și crom-nichel, SA 249 / SA 249M Standard Specification for Welded Austenitic Steel Boiler, Superheater, Heat Exchanger, and Condenser Tubes A 268 / A268M Tuburi fără sudură și sudate din oțel inoxidabil ferritic și martensitic pentru uz general A 269 / A 269M Tuburi fără sudură și sudate din oțel inoxidabil austenitic pentru uz general A 270 / A 270M Tuburi fără sudură și sudate...

ASTM B163 N02200 N02201 N04400 N06600 N06601 N06690 N08800 N08810 N08811 N08825 N08020 N06025 U Bend Tuburi din aliaj de nichel

Standarde pentru tuburi și țevi din oțel inoxidabil fără sudură: Standard Catagorie HidraulicăInstrumentațieSchimbătoare de căldurăȚevi ASME / ANSIISO și metriceTemperatură înaltăSpecificații standarde pentru tuburi schimbătoare de căldurăASME - American Society of Mechanical EngineersASME Specificații Oțel inoxidabilSpecificații pentru țevi din oțel inoxidabilSpecificații pentru țevi din oțel inoxidabil Duplex Specificații pentru țevi din oțel inoxidabil Standard | Abrevierea termenului tehnic | Glosar oțel inoxidabil | World Society Shipping | Numărul internațional de telefon al țării | Numele complet al standardelor mondiale | Glosar metal oțel | Formatul documentelor standard | Glosar metale și termeni tehnici | Glosar galvanizare la cald Standard: ASTM A269 vs A312 Diferența dintre ASTM A269 și A312 Diferența dintre ASTM A213 și ASTM A269 Diferența dintre ASTM A213 și ASTM A312 Specificația Incoloy 825 UNS N08825 Tuburi fără sudură OCTG Cuplaj pentru carcasă NACE MR0175 și MR0103 Standarde Țevi din oțel carbon Standard ASTM BS DIN Suedia EN 10095 Proprietăți mecanice ale oțelului inoxidabil EN 10088-3 Întăritură mecanică martensitică și prin precipitare EN 10088-3 Proprietăți mecanice ale oțelurilor inoxidabile feritice EN 10088-2 Proprietăți mecanice ale oțelurilor inoxidabile martensitice EN 10088-2 Proprietăți mecanice ale oțelurilor inoxidabile feritice...