Diagrama compoziției chimice a oțelului inoxidabil
Conform ASTM A213, ASTM A269, ASTM A312, ASME SA376, ASTM A511, ASTM A789, ASTM A790
Aliaje pe bază de nichel:
Aliaj 20 (UNS N08020), Monel 200 (UNS 02200), Monel 400 (UNS N04400), Incoloy 800 (UNS N08800), Incoloy 800H (UNS N08810), Incoloy 800HT (UNS N08811), Incoloy 825 (UNS N08825), Inconel 600 (UNS N06600), 4J29, 4J36, GH3030, GH3039, C276 (UNS N10276)
| Grad | C | Si | Mn | P | S | Cr | Ni | Mo | N | Cu | Ti | Nb | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | min | maxim | |||
| A312 | TP304 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A312 | TP304H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A312 | TP304L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 13.00 | |||||||||||
| A312 | TP310S | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 24.00 | 26.00 | 19.00 | 22.00 | 0.00 | 0.75 | |||||||||
| A312 | TP316 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A312 | TP316H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 11.00 | 15.00 | 2.00 | 3.00 | |||||||||
| A312 | TP316L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A312 | TP317 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 10.00 | 14.00 | 3.00 | 4.00 | |||||||||
| A312 | TP317L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 11.00 | 15.00 | 3.00 | 4.00 | |||||||||
| A312 | TP321 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 5×(C+N) | 0.70 | |||||||||
| A312 | TP321H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 4×(C+N) | 0.70 | |||||||||
| A312 | TP347 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 13.00 | 10×C | 1.00 | |||||||||
| A312 | TP347H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 13.00 | 8×C | 1.00 | |||||||||
| A213 | TP304 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A213 | TP304H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A213 | TP304L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 12.00 | |||||||||||
| A213 | TP310S | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 24.00 | 26.00 | 19.00 | 22.00 | |||||||||||
| A213 | TP316 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A213 | TP316L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A213 | TP317 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 11.00 | 15.00 | 3.00 | 4.00 | |||||||||
| A213 | TP317L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 11.00 | 15.00 | 3.00 | 4.00 | |||||||||
| A213 | TP321 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 5×C | 0.70 | |||||||||
| A213 | TP347 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 20.00 | 9.00 | 13.00 | 10×C | 1.10 | |||||||||
| A213 | TP347H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 20.00 | 9.00 | 13.00 | 8×C | 1.10 | |||||||||
| A269 | TP304 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A269 | TP304L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 12.00 | |||||||||||
| A269 | TP316 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A269 | TP316L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 15.00 | 2.00 | 3.00 | |||||||||
| A269 | TP317 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 11.00 | 15.00 | 3.00 | 4.00 | |||||||||
| A269 | TP321 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 5×C | 0.70 | |||||||||
| A269 | TP347 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 10×C | 1.10 | |||||||||
| A511 | MT304 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A511 | MT304L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 13.00 | |||||||||||
| A511 | MT310S | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 24.00 | 26.00 | 19.00 | 22.00 | |||||||||||
| A511 | MT316 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 16.00 | 18.00 | 11.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A511 | MT316L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 15.00 | 2.00 | 3.00 | |||||||||
| A511 | MT317 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 11.00 | 14.00 | 3.00 | 4.00 | |||||||||
| A511 | MT321 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 17.00 | 20.00 | 9.00 | 13.00 | 5×C | 0.60 | |||||||||
| A511 | MT347 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 17.00 | 20.00 | 9.00 | 13.00 | 10×C | 1.00 | |||||||||
| A213 | UNS N08904 | 0.00 | 0.020 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.03 | 19.00 | 23.00 | 23.00 | 28.00 | 4.00 | 5.00 | 1.00 | 2.00 | |||||||
| A376 | TP304 | 0.00 | 0.080 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A376 | TP304H | 0.040 | 0.100 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A376 | TP316 | 0.00 | 0.080 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 11.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A376 | TP316H | 0.040 | 0.100 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 11.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A376 | TP321 | 0.00 | 0.080 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 13.00 | 5×C | 0.70 | |||||||||
| A376 | TP321H | 0.040 | 0.100 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 13.00 | 4×C | 0.70 | |||||||||
| A376 | TP347 | 0.00 | 0.080 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 13.00 | 10×C | 1.10 | |||||||||
| A376 | TP347H | 0.040 | 0.100 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 1900 | 9.00 | 13.00 | 8×C | 1.10 | |||||||||
| A790 | S31803 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.030 | 0.00 | 0.020 | 21.00 | 23.00 | 4.50 | 6.50 | 2.50 | 3.50 | 0.08 | 0.20 | |||||||
| A789 | S31803 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.030 | 0.00 | 0.020 | 21.00 | 23.00 | 4.50 | 6.50 | 2.50 | 3.50 | 0.08 | 0.20 |
Diagrama compoziției oțelului inoxidabil
Compoziția chimică a oțelului inoxidabil BS 970
BS 3100 Compoziția chimică a oțelului inoxidabil
BS 6744 Compoziția și mecanica oțelului inoxidabil
EN 10088-2 Compoziție chimică Oțel inoxidabil
Compoziția chimică a aliajului Hastelloy
Compoziția chimică a aliajului de nichel Monel
EN 10302 Compoziția chimică a oțelurilor rezistente la fluaj
EN 10028-7 Compoziția chimică a oțelului inoxidabil plat
EN 10283 Compoziția chimică a oțelului inoxidabil turnat
EN 10095 Compoziția chimică a oțelurilor rezistente la căldură
EN 10269 Compoziția chimică a oțelului inoxidabil
EN 10296-2 Compoziția chimică a oțelului inoxidabil
BS 3146-2 Compoziția chimică a oțelului inoxidabil
Compoziția chimică a oțelului inoxidabil rezistent la căldură AISI și UNS
EN 10216-5 Compoziția chimică a oțelurilor inoxidabile
Diagrama compoziției chimice JIS G3459 G3463
DIN 17456 17458 Diagrama compoziției chimice