DIN 17459 specifies technical delivery conditions for seamless circular tubes made from high temperature austenitic stainless steel as specified in table. 1. Such stainless steel tube are intended primarily to be used in high-pressure applications where elevated temperature and high mechanical stresses are involved (e.g. in the construction of pressure boilers, pressure vessels, pipelines, and in the chemical industry). Material Chemical composition (%) degignation number C Si Mn P S Ni Cr Mo Ni others X 6 CrNi 18 11 1.4948 0.04 to 0.08 ≤0.75 ≤2.0 0.035 0.015 17.0 to 19.0 – 10.0 to 12.0   X 3 CrNiN 18 11 1.4949 ≤0.04 ≤0.75 ≤2.0 0.035 0.015 0.10 to 0.18 17.0 to 19.0 0.50 to 0.60 9.5 to 11.5   X 8 CrNiTi 18 10 1.4941 0.04 to 0.10 ≤0.75 ≤2.0 0.035 0.015 17.0 to 18.5 – 9.5 to 11.5 Ti: ≥5 x %Cto ≤  0.80B: 0.0015 to 0.0050 X6CrNiMo 17 13 1.4919 0.04 to 0.08 ≤0.75 ≤2.0 0.035…

The table shown is based on the reference data presented in EN 10088-1. Only a sample of the information available is shown. This is intended to show the scope of information available through representative figures for the most commonly used stainless steel tube types. A separate table indicates some of the grades that have been grouped together.Physical Properties Table Steel Types (AISI) Density Modulus Expansion Conductivity Specific Heat Resistivity . . 20C 400C . . . . Ferritic stainless steels 410S 7700 220 195 10.5 30 460 0.60 430 7700 220 195 10.0 25 460 0.70 444 7700 220 195 10.4 23 430 0.8 Martensitic and precipitation hardening stainless steels 410 7700 215 190 10.5 30 460 0.60 440 7700 215 190 10.4 15 430 0.8 630 7800 200 170 10.9 16 500 0.71 Austenitic stainless steel 304 7900 200 172 16.0 15 500 0.73 316 8000 200 172 16.0 15 500 0.75 ‘6%Mo’ 8000…

ASTM A595 Standard Specification for Steel Tubes, Low-Carbon or High-Strength Low-Alloy, Tapered for Structural Use covers three grades of seam-welded, round, tapered steel tubes for structural use. Grades A and B are of low-carbon steel or high-strength low-alloy steel composition and Grade C is of weather-resistance steel composition. The tube steel shall be hot-rolled aluminum-semikilled or fine-grained killed sheet or plate manufactured by one or more of the following processes: open-hearth, basic-oxygen, or electric-furnace. The tubes shall be made from trapezoidal sheet or plate that is preformed and then seam welded. They shall be brought to final size and properties by roll compressing cold on a hardened mandrel. A tensile test shall be done to determine the yield strength and the ultimate tensile strength of the tubes. 1.1 This specification covers three grades of seam-welded, round, tapered steel tubes for structural use. Grades A and B are of low-carbon steel or high-strength low-alloy steel composition and Grade C…

ASTM A790 heeft betrekking op naadloze en rechtnaadgelaste ferritisch/austenitisch duplex roestvrijstalen buizen voor algemeen corrosief gebruik, waarbij de nadruk ligt op de weerstand tegen spanningscorrosiescheuren. De pijp wordt naadloos of automatisch gelast, zonder toevoeging van toevoegmateriaal tijdens het lassen. Er moet een warmteanalyse worden uitgevoerd om de percentages van de gespecificeerde elementen te bepalen. Spanningstests, hardingstests, afvlakkingstests, hydrostatische tests en niet-destructieve elektrische tests moeten worden uitgevoerd om aan de gespecificeerde eisen te voldoen. Deze samenvatting is een korte samenvatting van de norm waarnaar verwezen wordt. Het is slechts informatief en geen officieel onderdeel van de norm; de volledige tekst van de norm zelf moet worden geraadpleegd voor gebruik en toepassing. Deze specificatie heeft betrekking op naadloze en rechte naad gelaste ferritisch/ austenitisch roestvast stalen pijpen bedoeld voor algemeen corrosief gebruik, met bijzondere nadruk op weerstand tegen spanningscorrosie. Deze staalsoorten zijn gevoelig voor verbrossing bij langdurig gebruik bij hoge temperaturen. Optionele aanvullende eisen...

DSTU B A.3.2-12:2009 SSBP. Ventilatiesystemen. Zagalni vimogi DSTU GOST 166:2009 (ISO 3599-76) Remklauwen. Technische specificaties ( GOST 166-89 (ISO 3599-76), IDT) DSTU EN 473:2012 Niet-invasieve controle. Kwalificatie en certificering van personeel. Algemene bepalingen ( EN 473 :2008, IDT) DSTU 2680-94 Naadloze gewalste buizen van staal en legeringen. Terminologie en identificatie van oppervlaktedefecten DSTU 2841-94 ( GOST 27809-95 ) Chavun i staal. Methoden voor spectrografische analyse DSTU 3124-95 Buizen van staal en legeringen. Binden en voorbereiden van monsters voor het chemisch magazijn. Basisbepalingen DSTU 4179-2003 Metalen trilbanden. Technische vaardigheden ( GOST 7502-98 , MOD) DSTU GOST 6507:2009 Micrometers. Specificaties DSTU 7238:2011 Systeem van veiligheidsnormen. Creëer een collectieve zakhist voor de werkende mensen. Zagalni vimogi ta classificatie DSTU 7239:2011 Systeem van veiligheidsnormen. Een individuele zakhist toewijzen. Zagalni vimogi ta classificatie DSTU ISO 7438:2005 Metalen materialen. Testen voor zgin (ISO 7438:1985, IDT) DSTU ISO 8496-2002 Metalen materialen. Trompet. Beproeving voor het uittrekken van de ringen met twee parallelle staven (ISO 8496:1988, IDT) DSTU GOST 12344:2005 Gelegeerd en hooggelegeerd staal. Methoden voor het ontwerpen van vugletsiu ( GOST 12344-2003,...

Inspectie van het buitenoppervlak van pijpen wordt visueel uitgevoerd zonder gebruik van vergrootglazen. Het inwendige oppervlak van pijpen met een inwendige diameter van 70 mm of meer wordt geïnspecteerd met behulp van een periscoop of videoscopische systemen. Het is toegestaan om het binnenoppervlak van pijpen te inspecteren zonder gebruik te maken van instrumenten, met behulp van verlichtingsapparaten aan beide uiteinden van de pijp tegen het licht. Voor leidingen met een inwendige diameter van minder dan 70 mm, evenals voor leidingen met een inwendige diameter van 70 mm of meer die niet met een periscoop zijn geïnspecteerd, garandeert de fabrikant dat het inwendige oppervlak van de leidingen voldoet aan de vereisten van deze specificaties op basis van bevredigende resultaten van 100% ultrasone inspectie. De classificatie van defecten wordt uitgevoerd in overeenstemming met DSTU 2680 (OST 14-82 [ 18 ]). De diepte van de defecten wordt gecontroleerd na het vijlen en vervolgens meten. De wand...

Op het gebied van roestvrij staal wordt 304 meestal TP304 genoemd, 304L wordt 304L genoemd, 316L wordt TP316L genoemd. Bijvoorbeeld: ASTM A312 TP304, ASME SA213 TP304L, ASME SA213 TP316L. Dus wat betekent "TP"? TP staat voor Type. De reden hiervoor is dat AISI (American Iron and Steel Institute) roestvast staal indeelt in typen. Om dezelfde reden, soms 304, 304, L316L, zal worden genoemd AISI 304, AISI 304L, AISI 316L.

OD: 17.15 - 508mm (3/8 INCH tot 20 INCH)WT: 0.5 - 60 mm, Schema 10s, 20, 40s, 40, 60, 80s, 80, 100, 120, 140, 160, XXH.Productiecapaciteit: 500 MT/maand Guanyu Tube is gespecialiseerd fabrikant van ASTM A312 TP304, ASTM A312 TP304L, ASTM A312 TP316, ASTM A312 TP316L, ASTM A312 TP321, ASTM A312 TP310S, ASTM A312 TP304 TP304L TP304H TP316 TP316L TP317L TP321 TP316Ti TP347 TP347H TP310S TP309S Stainless Steel Pipe Supplier. Deze wordt uitgegeven onder de vaste benaming ASTM A312; het nummer onmiddellijk na de benaming geeft het jaar van de oorspronkelijke vaststelling aan of, in geval van herziening, het jaar van de laatste herziening. Een getal tussen haakjes geeft het jaar van de laatste hergoedkeuring aan. Een epsilon in superscript geeft een redactionele wijziging aan sinds de laatste herziening of hergoedkeuring. Dit heeft betrekking op naadloze, rechte naad en zwaar koud gelaste austenitische roestvast stalen buizen voor hoge temperatuur en algemeen corrosief gebruik. Wanneer het kerfslagbeproevingscriterium voor gebruik bij lage temperatuur...

Chemische Samenstelling van ASTM A213 / ASME SA 213 317 317L 317LM 317LMN Roestvrij staal Grade C Mn P Zwavel Si Cr Nikkel Mo N Cu Gewicht % 317 S31700 18,00 11,00 3,00 Min. 0,08 2,00 0,045 0,030 1,00 20,00 15,00 4,00 Max. 317L S31703 18,00 11,00 3,00 Min. 0,035 2,00 0,045 0,030 1,00 20,00 15,00 4,00 Max. 317LM S31725 18,00 13,50 4,00 Min. 0,03 2,00 0,045 0,030 1,00 20,00 17,50 5,00 0,20 0,75 Max 317LMN S31726 17,00 13,50 4,00 0,10 Min. 0,03 2,00 0,045 0,030 1,00 20,00 17,50 5,00 0,20 0,75 Max. EN 10216-5 1.4439 16.50 12.50 4.00 Min. 0,030 2,00 0,040 0,015 1,00 18,50 14,50 5,00 Max. EN 10217-7 1.4438 17.50 13.00 3.00 Min. 0,030 2,00 0,045 0,030 1,00 19,50 16,00 4,00 Max. Mechanische eigenschappen van 317 317L roestvast stalen buizen...

Checmical Samenstelling van ASME SA213 304 304L 304H en EN 10216-5 1.4301 1.4307 1.4948 Grade - C Mn Si P S Cr Mo Ni N 304/S30400 min.max. -0,08 -2,0 -1,00 -0,045 -0,030 18,0-20,0 - 8,0-11,0 - EN 10216-5 1.4301 min.max. -0,07 -2,0 -1,00 -0,040 -0,015 17,00-19,5 - 8,0-10,5 -0,11 304L/S30403 min.max. -0.035 -2.0 -1.00 -0.045 -0.030 18.0-20.0 - 8.0-12.0 - EN 10216-5 1.4307 min.max. -0,030 -2,0 -1,00 -0,040 -0,015 17,5-19,5 - 8,0-10,0 -0,11 304H /S30409 min.max. 0,04-0,10 -2,0 -1,00 -0,045 -0,030 18,0-20,0 - 8,0-11,0 - EN 10216-5 1.4948 min.max. 0,04-0,08 -2,0 -1,00 -0,035 -0,015 17,0-19,0 - 8,0-11,0 -0,11 TP304L Algemene eigenschappenTP304L Chemische samenstellingTP304L CorrosiebestendigheidTP304L Fysische eigenschappenTP304L Mechanische eigenschappenTP304L LassenTP304L WarmtebehandelingTP304L ReinigenTP304L/304L/304LN/304H Buizen en pijpen/304L Roestvast stalen buizen

Wij zijn gespecialiseerd fabrikant van ASME SA249 ASTM A249 TP304, ASTM A249 TP304L, ASTM A249 TP304H, ASTM A249 TP316, ASTM A249 TP316L, ASTM A249 TP316H, ASTM A249 TP316Ti, ASTM A249 TP321 TP321H, ASTM A249 TP309H TP309S, ASTM A249 TP310S TP 310H, ASTM A249 TP347 gelaste buizen en ASTM A249 gelaste pijp. Wat is ASTM A249 ASME SA249? ASTM A249 is specificeert standaard specificatie voor nominale wanddikte gelaste buizen en zwaar koud bewerkt gelaste buizen gemaakt van austenitisch staal met verschillende kwaliteiten bedoeld voor gebruik als een ketel, oververhitter, warmtewisselaar of condensor buizen. Warmte- en productanalyse moeten voldoen aan de eisen met betrekking tot de chemische samenstelling voor koolstof, mangaan, fosfor, zwavel, silicium, chroom, nikkel, molybdeen, stikstof, koper en andere stoffen. Alle materialen moeten worden geleverd in warmtebehandelde toestand volgens de vereiste oplossingstemperatuur en afschrikmethode. ASTM A249 Tubing Test Items Wanneer de laatste warmtebehandeling in een continu-oven plaatsvindt, wordt het aantal...

PT Beproevingsnorm Internationale Organisatie voor Normalisatie (ISO) ISO 3059, Niet-destructief onderzoek - Penetratie en magnetisch deeltjesonderzoek - Kijkcondities ISO 3452-1, Niet-destructief onderzoek. Penetrant onderzoek. Deel 1. Algemene principes ISO 3452-2, Niet-destructief onderzoek - Penetrant onderzoek - Deel 2: Testen van penetrant materialen ISO 3452-3, Niet-destructief onderzoek - Penetrant onderzoek - Deel 3: Referentie testblokken ISO 3452-4, Niet-destructief onderzoek - Penetrant onderzoek - Deel 4: Uitrusting ISO 3452-5, Niet-destructief onderzoek - Penetrant onderzoek - Deel 5: Penetrant onderzoek bij temperaturen hoger dan 50 °C ISO 3452-6, Niet-destructief onderzoek - Penetrant onderzoek - Deel 6: Penetrant onderzoek bij temperaturen lager dan 10 °C ISO 10893-4: Niet-destructief onderzoek van stalen buizen. Penetrant onderzoek van naadloze en gelaste stalen buizen voor de detectie van oppervlakte onvolkomenheden. ISO 12706, Niet-destructief onderzoek - Penetrant onderzoek - Woordenlijst ISO 23277, Niet-destructief onderzoek van lassen - Penetrant onderzoek van lassen - Acceptatieniveaus Europees Comité voor Normalisatie (CEN) EN 1371-1, Fundering - Vloeibaar penetrant onderzoek...

Wat is ASTM A269 en ASTM A312 / ASME SA312? ASTM A269 / A269M Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General Service ASTM A312 / A312M Standard Specification for Seamless, Welded, en zwaar koudvervormde Austenitische roestvrij stalen buizen StandaardItem ASTM A213 ASTM A269 ASTM A312 Grade 304 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H 304 304L 304H 304N 304LN 316N316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H Opbrengststerkte (Mpa) ≥170；≥205 ≥170；≥205 ≥170；≥205 Treksterkte (Mpa) ≥485；≥515 ≥485；≥515 ≥485；≥515 Verlenging (%) ≥35 ≥35 ≥35 Hydrostatische Test OD (mm) Druk max (MPa) OD (mm) Druk max (MPa) OD (mm) Druk max (MPa) D<25.4, 7Mpa D<25.4, 7Mpa D≤88.9, 17MPa 25.4≤D<38.1, 10Mpa 25.4≤D<38.1, 10Mpa 38.1≤D<50.8, 14Mpa 38.1≤D<50.8, 14Mpa 50.8≤D<76.2， 17MPa 50.8≤D88.9, 19MPa 76.2≤D<127， 24MPa 76.2≤D<127， 24MPa D≥127, 31Mpa D≥127, 31Mpa P=220.6t/D...

C Si Si Mn Mn P S Cr Cr Ni Mo Mo N Cu Ti Nb Nb min max min max min max min max min max min max min max min max min max min max DIN 17456 1.4301 0.00 0.070 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.00 8.00 10.50 DIN 17456 1.4306 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 18.00 20.00 10.00 12.00 DIN 17456 1.4311 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.50 8.50 11.50 DIN 17456 1.4541 0.00 0.080 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.00 9.00 12.00...

C Si Si Mn Mn P S Cr Cr Ni Mo Mo N Cu Ti Nb Nb min max min max min max min max min max min max min max min max min max min max J3459 SUS304TP 0,00 0,080 0,00 1,00 0,00 2,00 0,00 0,040 0,00 0,030 18,00 20,00 8,00 11,00 J3459 SUS304HP 0,040 0,100 0,00 0.75 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20.00 8.00 11.00 J3459 SUS304LTP 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20,00 9,00 13,00 J3459 SUS310STP 0,00 0,080 0,00 1,50 0,00 2,00 0,00 0,040 0,00 0,030 24,00 26,00 19,00 22,00 ...

ASTM B111 Standard Specification for Copper and Copper-Alloy Seamless Condenser Tubes and Ferrule Stock (standaardspecificatie voor koper en koperlegering naadloze condensorbuizen en hulsmateriaal)ASTM A213/A213M Standard Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, en warmtewisselaarbuizenASTM A269/A269M Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General ServiceASTM A249 - A249/A249M Specification fors Welded Austenitic Steel Boiler, Superheater, Heat Exchanger, en condensorbuizenASTM A179 - A179/A179M - Specificatie voor naadloze koudgetrokken buizen voor warmtewisselaars en condensorbuizen van laag koolstofstaalASTM A214 - A214/A214M Specificatie voor elektrisch-weerstand-gelaste buizen voor warmtewisselaars en condensors van koolstofstaalASTM A851 - A851 Specificatie voor hoogfrequent inductielassen, Unannealed, Austenitic Steel Condenser Tubes Condenser TubeAdvantage of Stainless Steel tube in CondenserWaarom moet de condensor roestvrij stalen buizen gebruiken?Condensors voor grote stoomsystemen

Kwaliteit EN / UNS Maten Toleranties Testen 1.4749/S44600 EN ISO 1127Metrisch: Niet gestandaardiseerd=NSI/ASME B 36.19 EN ISO 1127 ASTM A213/A 450 1.4959/N08811 / N08810 ANSI/ASME B 36.19 Koud afgewerkt: ASTM B 407Hot finished: ASTM A999 Koud afgewerkt: ASTM B 407Hot afgewerkt: ASTM B 407 1.4835/S30815/253MA1.4854/S35315/353MA ANSI/ASME B 36.19 ASTM A999 ASTM A312/A 999

Roestvast staal zijn legeringen op ijzerbasis die meestal minstens 11,5% chroom bevatten. Andere elementen, waarvan nikkel het belangrijkste is, kunnen in combinatie met chroom worden toegevoegd om speciale eigenschappen te verkrijgen. Roestvrij staal is zeer goed bestand tegen corrosie en oxidatie bij hoge temperaturen. Over het algemeen nemen de corrosiebestendigheid en oxidatiebestendigheid geleidelijk toe, hoewel niet evenredig, met de toename van het chroomgehalte. Roestvrijstalen buizen en pijpen worden om verschillende redenen gebruikt: om corrosie en oxidatie te weerstaan, om hoge temperaturen te weerstaan, voor netheid en lage onderhoudskosten en om de zuiverheid te handhaven van materialen die in contact komen met roestvrij staal. De inherente eigenschappen van roestvaststalen buizen maken het mogelijk om dunwandige leidingsystemen te ontwerpen zonder bang te hoeven zijn voor vroegtijdig falen door corrosie. Het gebruik van fusielassen om dergelijke leidingen te verbinden elimineert de noodzaak voor schroefdraad. Type 304 roestvast staal is de meest gebruikte analyse voor algemene corrosiebestendige buizen en pijptoepassingen, het wordt...

EN Normen: EN Europese norm voor roestvast staal Europese EN norm Grade Summary Europese norm voor maattoleranties voor roestvast staal EN 10090 Chemische samenstelling van ventielstaal BS 970 roestvast staal Chemische samenstelling BS 3100 1991 Gietstaal Chemische samenstelling BS 3100 Chemische samenstelling van roestvast staal BS 1449-2 Chemische samenstelling van roestvast staal BS Aerospace S100 Chemische samenstelling Mechanische eigenschappen BS Aerospace S500 Chemische samenstelling Mechanische eigenschappen EN 10204 Testcertificaten voor roestvast staal EN 10302 Chemische samenstelling van kruipbestendig staal EN 10302 Mechanische eigenschappen van kruipbestendig staal Tolerantie tot EN 10296-2 gelaste buizen van roestvast staal EN 10296-2 chemische samenstelling van gelaste buizen van roestvast staal Mechanische eigenschappen chemische samenstellingen van roestvast staal volgens EN 10297-2 EN 10297-2 mechanische eigenschappen van roestvast stalen buizen toleranties volgens EN 10297-2 voor naadloze buizen van roestvast staal EN 10269 Mechanische eigenschappen van roestvast staal bij kamertemperatuur EN 10269...

ASTM-normen: ASTM Standaard voor roestvrij staal Koolstofstaalpijp Standaard ASTM BS DIN Zweden ASTM B265 Titanium Alloy Eigenschappen ASTM B265 Titanium Alloy Chemische Samenstelling ASTM A48 Standaardspecificatie voor gietstukken van grijs ijzer ASTM A53 Standaard stalen pijp Zwart Hot-Dipped Zinc-Coated ASTM A53 Pipe ASME SA53 stalen pijp Maximale Werkdruk-ASTM A53 B Koolstofstaalpijpen ASTM A 53 & ASTM A 106. Gelaste en naadloze zwarte pijpen Naadloze pijp van koolstofstaal bedoeld voor gebruik bij hoge temperaturen ASTM A105 Standard for Forgins Carbon Steel Piping ASTM A106 Koolstofstalen pijp voor gebruik bij hoge temperaturen ASTM A106 / A106M - 08 Standaard specificatie voor naadloze koolstofstalen pijp voor gebruik bij hoge temperaturen ASTM A134 Standard for Seamless Carbon Steel Pipe for High- Temperature Service.Gebruik bij hoge temperaturen ASTM A134 Standaard voor stalen buizen elektrisch-gelast ASTM A134 Specificatie voor stalen buizen elektrisch-gelast ASTM A135 Standaard voor elektrisch-weerstand-gelaste stalen buizen ASTM A139 Specificatie voor elektrisch-gelaste stalen buizen ASTM A139 Standaard elektrisch-gelaste stalen buizen ASTM A148...

Guanyu Tube is gespecialiseerd fabrikant van ASTM A269 TP304, ASTM A269 TP304L, ASTM A269 TP316, ASTM A269 TP316L, ASTM A269 Buizenstelsel in China. Leveringsvoorwaarde in het Heldere Ontharden of het Ontharden het Beitsen en Buitenoppervlakte Oppoetsen. Het Buizenstelsel ASTM A269 omvat hoofdzakelijk ASTM A269 TP316 Buizenstelsel van het Roestvrij staalinstrumentatie, ASTM A269 TP316L Buizenstelsel van het Roestvrij staalinstrument, Hydraulisch Buizenstelsel van het Roestvrij staal. ASTM A269 wordt uitgegeven onder de fixed aanduiding ASTM A269, het nummer direct na de aanduiding geeft het jaar van de oorspronkelijke vaststelling of, in het geval van herziening, het jaar van de laatste herziening. Een getal tussen haakjes geeft het jaar van de laatste hergoedkeuring aan. Een epsilon in superscript geeft een redactionele wijziging aan sinds de laatste herziening of hernieuwde goedkeuring. Deze specificatie heeft betrekking op roestvaststalen buizen met een nominale wanddikte voor algemene corrosiebestendige toepassingen bij lage of hoge temperaturen, zoals aangegeven in tabel 1. De buisdiameters en -diktes die gewoonlijk volgens deze specificatie worden geleverd, hebben een binnendiameter van 6,4 mm (1⁄4 in...

ASTM A269 en ASTM A249 zijn beide geschikt voor gelaste roestvrij stalen buizen en pijpen. ASTM A249 / A249M Standard Specification for Welded Austenitic Steel Boiler, Superheater, Heat-Exchanger, and Condenser Tubes. ASTM A269 / A269M Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General Service. ASTM A249 ASTM A269 Vergelijkingstabel ASTM A249 en ASTM A269 specificaties zijn twee standaarden voor Austenitische roestvrij stalen buizen, er zijn dezelfde eisen in technische, ook hebben ze een aantal verschillen. Specificatie ASTM A249 ASTM 269 buis Fabricage Gelast Gelast en naadloos Toepassing BoilerSuperheaterWarmtewisselaarCondensator Algemene dienst Maten OD: maximaal 304,8 mmWanddikte: 0,4 - 8,1 mm Binnendiameter: minium 3 .4 mmMuurdikte: 0,51 mm ASTM / ASME ASTM A249 / A249MASME SA249 ASTM A269 / A269M Test Flens Test Flens Test A249 VS A269 Toepassingsgebied ASTM A249 gelaste buizen zijn voor ketel, superverwarmer, warmtewisselaar, condensor...

ASTM A789 ASME SA 789 S31803 S32205 S32101 S32750 S32760 S32304 S31500 S31260 Naadloze Buizen Fabrikant

ASTM A213 ASME SA213 TP304 TP304L TP309S TP310S TP316L TP316Ti TP321 TP317L TP347H Warmtewisselaarbuis

Specificaties roestvrijstalen buizen Inhoudsopgave: ASTM Specificaties roestvrijstalen buizen: IJzer- en staalproducten Stalen pijpleidingen, stalen buizen, hulpstukken ASTM A1016 Standard Specification for General Requirements for Ferritic Alloy Steel, Austenitic Alloy Steel, and Stainless Steel Tubes ASTM A999 Standard Specification for General Requirements for Alloy and Stainless Steel Pipe A 213 / A 213M Naadloze ferritische en austenitische gelegeerde stalen ketel-, oververhitter- en warmtewisselaarbuizen SA 240 / SA 240M Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, SA 249 / SA 249M Standard Specification for Welded Austenitic Steel Boiler, Superheater, Heat Exchanger, and Condenser Tubes A 268 / A 268M Naadloze en gelaste ferritische en martensitische roestvrij stalen buizen voor algemeen gebruik A 269 / A 269M Naadloze en gelaste austenitische roestvrij stalen buizen voor algemeen gebruik A 270 / A 270M Naadloze en gelaste...

ASTM B163 N02200 N02201 N04400 N06600 N06601 N06690 N08800 N08810 N08811 N08825 N08020 N06025 Buig Buizen van de Nikkellegering

Normen voor naadloze roestvrijstalen buizen en pijpen: Standaard Catagorie HydraulischeInstrumentatieWarmtewisselaarsBuis ASME / ANSIISO & metrischHoge temperatuurSpecificatie normen voor warmtewisselaar buizenASME - American Society of Mechanical EngineersASME Specificaties Roestvrij staalRoestvrij stalen buis SpecificatieDuplex roestvrij stalen buis Specificatie Standaard | Technische term afkorting | Woordenlijst Roestvrij staal | World Society Shipping | International Phone Country Number | World Standards Full Name | Staalmetalen Woordenlijst | Standaard Documenten Formaat | Metalen en Engineering termen Woordenlijst | Thermisch verzinken Woordenlijst Standaard: ASTM A269 vs A312 Verschil tussen ASTM A269 en A312 Verschil tussen ASTM A213 en ASTM A269 Verschil tussen ASTM A213 en ASTM A312 Specificatie van Incoloy 825 UNS N08825 Naadloze buizen OCTG Casing Koppeling NACE MR0175 en MR0103 Normen Koolstofstalen pijpen Standaard ASTM BS DIN Zweden EN 10095 Mechanische eigenschappen van roestvast staal EN 10088-3 Mechanische martensitische en precipitatieharding EN 10088-3 Mechanische eigenschappen van ferritisch roestvast staal EN 10088-2 Mechanische eigenschappen van martensitisch roestvast staal EN 10088-2 Mechanische eigenschappen van ferritisch roestvast staal...