ASTM A790 Standaardspecificatie voor naadloze en gelaste ferritische Austenitische roestvrij staalpijp
ASTM A790 covers seamless and straight-seam welded ferritisch/austenitisch duplex stainless steel pipe for general corrosive service, with particular emphasis on resistance to spanningscorrosie. The pipe shall be made by the seamless or an automatic welding process, with no addition of filler metal in the welding operation. Warmte analysis shall be made to determine the percentages of the elements specified. Tension tests, hardening tests, flattening tests, hydrostatic test and nondestructive electric tests shall be made to conform to the specified requirements.
This abstract is a brief summary of the referenced standaard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. This specification covers seamless and straight-seam welded ferritisch/ austenitic stainless steel pip intended for general corrosive service, with particular emphasis on resistance to spanningscorrosie. These steel are susceptible to embrittlement if used for prolonged periods at elevated temperatures.
Optional supplementary requirements are provided for pipe when a greater degree of testing is desired. These supplementary requirements call for additional tests to be made and, when desired, one or more of these may be specified in the order.
Appendix X1 of this specification lists the dimensions of welded and stainless steel seamless pipe as shown in ANSI B36.19. Pipe having other dimensions may be furnished provided such pipe complies with all other requirements of this specification.
The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification. The inch-pound units shall apply unless the M designation of this specification is specified in the order.
The dimensionless designator Nominale pijpmaat (nominal pipe size) has been substituted in this standard for such traditional terms as nominal diameter, size, and nominal size.
Documenten waarnaar wordt verwezen
ASTM A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A923 Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stainless Steel
ASTM A941 Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys
ASTM A999/A999M Specification for General Requirements for Alloy and Stainless Steel Pipe
ASTM E213 Practice for Ultrasonic Examination of Metal Pipe and Tubing
ASTM E309 Practice for Eddy-Current Examination of Steel Tubular Products Using Magnetic Saturation
ASTM E381 Method of Macroetch Testing Steel Bars, Billets, Blooms, and Forgings
ASTM E426 Practice for Electromagnetic (Eddy-Current) Examination of Seamless and Welded Tubular Products, Austenitic Stainless Steel and Similar Alloys
ASTM E527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)
ASTM A5.9 Corrosion-Resisting Chromium and Chromium-Nickel Steel Welding Rods and Electrodes
ASTM B1.20.1 Pipe Threads, General Purpose
ASTM B36.10 Welded and Seamless Wrought Steel Pipe
ASTM B36.19 Stainless Steel Pipe
SAE J 1086
SNT-TC-1A Personal Qualification and Certification in Nondestructive Testing
ASTM A789/A789M | ASTM A790/A 790M | Duplex roestvast stalen buis | Austenitisch-ferritisch roestvast stalen buis | Super-Duplex roestvast staal en hun eigenschappen | 2507 S32750(1.4410) Duplex Steel | S32205 S31803(1.4462) Duplex Steel | S32304 (1.4362) Duplexstaal | S32760 1.4501 Stainless Steel | LDX2101 S32101 1.4162 Duplex Stainless Steel
Index Terms
duplex stainless steel pipe; ferritic/austenitic stainless steel; seamless steel pipe; stainless steel tube; steel pipe; welded steel pipe; Austenitic stainless steel pipe–specifications; Corrosion-resistant steel–specifications; Corrosive service applications–pipe (steel); Duplex stainless steel–specifications; Ferritic steel pipe–specifications; Seamless austenitic steel pipe–specifications; Stainless steel tube–specifications; Welded steel pipe–specifications; ICS Number Code 23.040.10; 23.040.10; 23.040.10
ASTM A790 Standaardspecificatie voor naadloze en gelaste ferritische/ustenitische roestvrij staalpijp
ASME SA790 / 790M Standard Specification for Seamless and Welded Ferritic/Austenitic Stainless Steel Pipe
Duplex-de Specificatie van de Roestvrij staalpijp
| Standaard Item | ASTM A789 | ASTM A790 | EN 10216-5 | |||
| Rang | S31803 S32205 S32750 | S31803 S32205 S32750 | 1.4301 1.4307 1.4948 1.4315 1.4401 1.4404 1.4571 1.4541 1.4941 1.4845 1.4449 1.4438 1.4550 1.4912 1.4462 1.4410 | |||
| Opbrengststerkte (Mpa) | ≥450；≥485；≥550 | ≥450；≥450；≥550 | — | |||
| Treksterkte (Mpa) | ≥620；≥655；≥800 | ≥620；≥655；≥800 | — | |||
| Rek (%) | ≥25；≥25；≥15 | ≥25；≥25；≥15 | — | |||
| Hydrostatische test | De hydrostatische test moet in overeenstemming zijn met ASTM A1016.Zou vervangen kunnen worden door ECT. | De hydrostatische test moet in overeenstemming zijn met ASTM A999.Zou kunnen worden vervangen door ECT. | De hydrostatische test moet worden uitgevoerd bij een testdruk van 7MPa of hoger. bij een testdruk berekend met de volgende formule P=2St/D S=70%Rp0,2 | |||
| Interkristallijne corrosie Test | Gebruik gewoonlijk de putcorrosietest. | Gebruik gewoonlijk de putcorrosietest. | EN ISO 3651-2 (optioneel) | |||
| Wervelstroomtest | Kan worden vervangen door HT. | Kan worden vervangen door HT. | EN 10246-3 | |||
| O.D. tolerantie (mm) | O.D. | O.D.Tolerantie | O.D. | O.D.Tolerantie | O.D. tolerantieklasse | |
| D<12.7 | +/-0.13 | 10.3≤D≤48.3 | +0.40/-0.80 | D3 | +/-0,75% of +/-0,3 mm | |
| 12.7≤D<38.1 | +/-0.13 | 48.3<D≤114.3 | +0.80/-0.80 | |||
| welke het grootst is | ||||||
| 38.1≤D<88.9 | +/-0.25 | 114.3<D≤219.1 | +1.60/-0.80 | D4 | +/-0,5% of +/-0,1 mm | |
| 88.9≤D<139.7 | +/-0.38 | 219.1<D≤457.0 | +2.40/-0.80 | |||
| welke het grootst is | ||||||
| W.T. Tolerantie (mm) | O.D. | W.T.Tolerantie | O.D. | W.T.Tolerantie | W.T. Tolerantieklasse | |
| D<12.7 | +/-15% | 10.3≤D≤73.0 | +20.0%/-12.5% | T3 | +/-10% of +/-0,2 mm | |
| 12.7≤D<38.1 | +/-10% | |||||
| 88.9≤D≤457.0 t/D ≤5% | +22.5%/-12.5% | welke het grootst is | ||||
| 38.1≤D<88.9 | +/-10% | T4 | +/-7.5% of +/-0,15mm | |||
| 88.9≤D≤457.0 t/D >5% | +15.0%/-12.5% | |||||
| 88.9≤D<139.7 | +/-10% | |||||
| welke het grootst is | ||||||
ASTM A789 / ASME SA789 heeft betrekking op kwaliteiten van gemiddelde wanddikte, of, indien gespecificeerd op de order, minimale wanddikte, van roestvaststalen buizen voor toepassingen waarbij algemene corrosiebestendigheid vereist is, met bijzondere nadruk op weerstand tegen spanningscorrosie. Deze staalsoorten zijn gevoelig voor verbrossing bij langdurig gebruik bij hoge temperaturen.
De waarden vermeld in SI-eenheden of inch-pound eenheden moeten afzonderlijk als standaard worden beschouwd. De waarden die in elk systeem worden vermeld, zijn mogelijk niet exact gelijkwaardig; daarom moet elk systeem onafhankelijk van het andere worden gebruikt. Het combineren van waarden uit de twee systemen kan leiden tot niet-conformiteit met de norm. In de tekst worden de SI-eenheden tussen haakjes weergegeven. De inch-pound eenheden zijn van toepassing tenzij de M-aanduiding van deze specificatie in de order is gespecificeerd.
Documenten waarnaar wordt verwezen
ASTM-normen:
A480/A480M Algemene eisen voor vlakgewalste plaat, blad en band van roestvast staal en hittebestendig staal
A1016/A1016M Specificatie voor algemene vereisten voor buizen van ferritisch gelegeerd staal, austenitisch gelegeerd staal en roestvrij staal
E527 Praktijk voor het nummeren van metalen en legeringen in het uniforme nummeringssysteem (UNS)
SAE-norm:
SAE J 1086 Praktijk voor nummering van metalen en legeringen (UNS)
Bestelinformatie
Bestellingen voor producten in het kader van deze specificatie moeten, indien nodig, het volgende bevatten om het gewenste materiaal adequaat te beschrijven:
Hoeveelheid (voet, meter of aantal lengtes),
Naam van het product (naadloze of gelaste buizen),
Rang
Afmetingen (buitendiameter en gemiddelde wanddikte, tenzij een minimale wanddikte is opgegeven),
Lengte (specifiek of willekeurig),
Optionele vereisten (voor productanalyse, zie Paragraaf voor hydrostatische of niet-destructieve elektrische test, zie Paragraaf 10
Testrapport vereist (zie het gedeelte Inspectie van Specificatie A1016/A1016M
Specificatieaanduiding en
Speciale vereisten.
Algemene vereisten
Het in het kader van deze specificatie geleverde product moet voldoen aan de toepasselijke eisen van specificatie A1016/ A1016M, tenzij hierin anders is bepaald.
Vervaardiging
De buizen moeten naadloos of gelast worden gemaakt zonder toevoeging van toevoegmetaal.
Warmtebehandeling
Alle buizen moeten worden geleverd in warmtebehandelde toestand volgens de in tabel 2 aangegeven procedures. Voor naadloze buizen mogen, als alternatief voor de uiteindelijke warmtebehandeling in een continu- of batchoven, de buizen onmiddellijk na het warmvervormen en bij een temperatuur van ten minste de gespecificeerde minimumtemperatuur voor de behandeling van de oplossing, afzonderlijk in water worden afgekoeld of op een andere wijze snel worden afgekoeld.
Tabel.1 ASTM A789 Duplex staal Chemische samenstelling
Het staal moet voldoen aan de chemische eisen in tabel 1.
| UNS | |||||||||||
| Aanwijzing | C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu | Anderen |
| S31200 | 0.030 | 2.00 | 0.045 | 0.030 | 1.00 | 5.5-6.5 | 24.0-26.0 | 1.20-2.00 | 0.14-0.20 | . . . | . . . |
| S31260 | 0.030 | 1.00 | 0.030 | 0.030 | 0.75 | 5.5-7.5 | 24.0-26.0 | 2.5-3.5 | 0.10-0.30 | 0.20 -0.80 | W 0.10 -0.50 |
| S31500 | 0.030 | 1.20 -2.00 | 0.030 | 0.030 | 1.40 -2.00 | 4.3-5.2 | 18.0-19.0 | 2.50-3.00 | 0.05-0.1 | . . . | . . . |
| S31803 | 0.030 | 2.00 | 0.030 | 0.020 | 1.00 | 4.5-6.5 | 21.0-23.0 | 2.5-3.5 | 0.08-0.20 | . . . | . . . |
| S32001 | 0.030 | 4.00 -6.00 | 0.040 | 0.030 | 1.00 | 1.0-3.0 | 19.5-21.5 | 0.60 | 0.05-0.17 | 1.00 | . . . |
| S32003 | 0.030 | 2.00 | 0.030 | 0.020 | 1.00 | 3.0-4.0 | 19.5-22.5 | 1.50-2.00 | 0.14-0.20 | . . . | . . . |
| S32101 | 0.040 | 4.0-6.0 | 0.040 | 0.030 | 1.00 | 1.35-1.70 | 21.0-22.0 | 0.10-0.80 | 0.20-0.25 | 0.10 -0.80 | . . . |
| S32202 | 0.030 | 2.00 | 0.040 | 0.010 | 1.00 | 1.00-2.80 | 21.5-24.0 | 0.45 | 0.18-0.26 | . . . | . . . |
| S32205 | 0.030 | 2.00 | 0.030 | 0.020 | 1.00 | 4.5-6.5 | 22.0-23.0 | 3.0-3.5 | 0.14-0.20 | . . . | . . . |
| S32304 | 0.030 | 2.50 | 0.040 | 0.040 | 1.00 | 3.0-5.5 | 21.5-24.5 | 0.05-0.60 | 0.05-0.20 | 0.05 -0.60 | . . . |
| S32506 | 0.030 | 1.00 | 0.040 | 0.015 | 0.90 | 5.5-7.2 | 24.0-26.0 | 3.0-3.5 | 0.08-0.20 | . . . | W 0.05 -0.30 |
| S32520 | 0.030 | 1.50 | 0.035 | 0.020 | 0.80 | 5.5-8.0 | 23.0-25.0 | 3.-5. | 0.20-0.35 | 0.50 -3.00 | . . . |
| S32550 | 0.04 | 1.50 | 0.040 | 0.030 | 1.00 | 4.5-6.5 | 24.0-27.0 | 2.9-3.9 | 0.10-0.25 | 1.50 -2.50 | . . . |
| S32707 | 0.030 | 1.50 | 0.035 | 0.010 | 0.50 | 5.5-9.5 | 26.0-29.0 | 4.0-5.0 | 0.30-0.50 | 1,0 max | Co 0,5 -2.0 |
| S32750 | 0.030 | 1.20 | 0.035 | 0.020 | 0.80 | 6.0-8.0 | 24.0-26.0 | 3.0-5.0 | 0.24-0.32 | 0.50 | . . . |
| S32760 | 0.030 | 1.00 | 0.030 | 0.010 | 1.00 | 6.0-8.0 | 24.0-26.0 | 3.0-4.0 | 0.20-0.30 | 0.50 -1.00 | W 0.50 -1.00 |
| S32808 | 0.030 | 1.10 | 0.030 | 0.010 | 0.50 | 7.0-8.2 | 27.0-27.9 | 0.80-1.20 | 0.30-0.40 | . . . | W 2.10 -2.50 |
| S32900 | 0.08 | 1.00 | 0.040 | 0.030 | 0.75 | 2.5-5.0 | 23.0-28.0 | 1.00-2.00 | . . . | . . . | . . . |
| S32906 | 0.030 | 0.80 -1.50 | 0.030 | 0.030 | 0.80 | 5.8-7.5 | 28.0 -30.0 | 1.50-2.60 | 0.30-0.40 | 0.80 | . . . |
| S32950 | 0.030 | 2.00 | 0.035 | 0.010 | 0.60 | 3.5-5.2 | 26.0-29.0 | 1.00-2.50 | 0.15-0.35 | . . . | . . . |
| S33207 | 0.030 | 1.50 | 0.035 | 0.010 | 0.80 | 6.0-9.0 | 29.0-33.0 | 3.0-5.0 | 0.40-0.60 | 1.0 | . . . |
| S39274 | 0.030 | 1.00 | 0.030 | 0.020 | 0.80 | 6.0-8.0 | 24.0-26.0 | 2.5-3.5 | 0.24-0.32 | 0.20 -0.80 | W 1.50 -2.50 |
| S39277 | 0.025 | 0.80 | 0.025 | 0.002 | 0.80 | 6.5-8.0 | 24.0-26.0 | 3.00-4.00 | 0.23-0.33 | 1.20 -2.00 | W 0.80 -1.21 |
| S82011 | 0.030 | 2.0 -3.0 | 0.040 | 0.020 | 1.00 | 1.00-2.00 | 20.5-23.5 | 0.10-1.00 | 0.15-0.27 | 0.50 | . . . |
| S82441 | 0.030 | 2.50 -4.00 | 0.035 | 0.005 | 0.70 | 3.0-4.5 | 23.0-25.0 | 1.00-2.00 | 0.20-0.30 | 0.10 -0.80 | |
A Maximum, tenzij een minimum of bereik is aangegeven. Waar ellipsen (...) in deze tabel staan, is er geen minimum en hoeft de analyse voor het element niet bepaald of gerapporteerd te worden.
B Aanduiding vastgesteld in overeenstemming met Praktijk E527 en SAE J1086.
C % Cr + 3,3 × % Mo + 16 × % N $ 41.
D % Cr + 3,3 × % Mo + 16 × % N $ 40.
Productanalyse
1. Van elke warmtebehandeling wordt hetzij één knuppel, hetzij één lengte van gewalst plat materiaal, hetzij één buis geanalyseerd. De aldus bepaalde chemische samenstelling moet voldoen aan de gestelde eisen.
2. Er geldt een productanalysetolerantie (zie de tabel in de bijlage Chemische eisen (productanalysetoleranties) in specificatie A480/A480M). De productanalysetolerantie is niet van toepassing op het koolstofgehalte voor materiaal met een gespecificeerde maximumkoolstof van 0,04 % of minder.
3. Als de oorspronkelijke test voor productanalyse mislukt, worden twee extra knuppels, lengten van gewalste platte producten of buizen opnieuw getest. Beide hertesten voor de elementen in kwestie moeten voldoen aan de eisen van deze specificatie; zo niet, dan wordt al het resterende materiaal in de warmte afgekeurd of, naar keuze van de producent, wordt elke knuppel of buis afzonderlijk getest voor aanvaarding. Knuppels, lengten van gewalste platte producten of buizen die niet aan de eisen van deze specificatie voldoen, worden opnieuw gekeurd.
OPMERKING 1 - Voor flens- en flensvoorschriften geldt de term partij voor alle buizen voorafgaand aan het snijden met dezelfde nominale maat en wanddikte die van dezelfde hitte van staal zijn vervaardigd. Wanneer de laatste warmtebehandeling in een batch-oven plaatsvindt, omvat een partij uitsluitend buizen van dezelfde afmetingen en van dezelfde warmte die in dezelfde ovenlading worden warmtebehandeld. Wanneer de laatste warmtebehandeling in een continu-oven plaatsvindt of wanneer de warmtebehandelde toestand direct door afschrikken na warmvervormen wordt verkregen, wordt het aantal buizen van dezelfde grootte en van dezelfde warmte in een partij bepaald aan de hand van de grootte van de buizen zoals voorgeschreven in tabel 3.
OPMERKING 2 - Voor de eisen van de trek- en hardheidstest is de term partij van toepassing op alle buizen vóór het snijden met dezelfde nominale diameter en wanddikte die van dezelfde warmte zijn vervaardigd. Wanneer de laatste warmtebehandeling in een batch-oven plaatsvindt, omvat een partij uitsluitend buizen van dezelfde afmetingen en met dezelfde warmte die in dezelfde ovenlading worden warmtebehandeld. Wanneer de laatste warmtebehandeling in een continue oven plaatsvindt of wanneer de warmtebehandelde toestand direct wordt verkregen door afschrikken na warmvervormen, omvat een partij alle buizen van dezelfde grootte en warmte, die in dezelfde oven bij dezelfde temperatuur, verwarmingstijd en ovensnelheid zijn warmtebehandeld, of alle buizen van dezelfde grootte en warmte, die in dezelfde productierun warmvervormd en afgekoeld zijn.
Mechanische testen vereist
1. 1.1. Trektests - Voor partijen van niet meer dan 50 buizen moet één trektest op een monster worden uitgevoerd. Voor partijen van meer dan 50 buizen worden trektests uitgevoerd op monsters van twee buizen (zie opmerking 2).
2. Flaringtest (voor naadloze buizen)-Er moet één test worden uitgevoerd op monsters van één uiteinde van één buis uit elke partij (zie noot 1) afgewerkte buizen. De minimale uitzetting van de binnendiameter moet 10 % bedragen.
3. Flenstest (voor gelaste buizen)-Er moet één test worden uitgevoerd op monsters van één uiteinde van één buis uit elke partij (zie opmerking 1) afgewerkte buizen.
4. Hardheidstest-Brinell- of Rockwell-hardheidstests moeten worden uitgevoerd op monsters van twee buizen uit elke partij (zie opmerking 2).
5. Wanneer er sprake is van meer dan één warmtebehandeling, gelden de eisen voor de spanningstest, het uitwaaieren, het ombuigen en de hardheidstest voor elke warmtebehandeling.
6. Omgekeerde afvlakkingstest-Voor gelaste buizen moet één omgekeerde afvlakkingstest worden uitgevoerd op een proefstuk van elke 1500 ft [450 m] afgewerkte buis.
Hydrostatische of niet-destructieve elektrische test
1 Elke buis moet worden onderworpen aan de niet-destructieve elektrische test of de hydrostatische test. De keuze van het type test is aan de fabrikant, tenzij anders gespecificeerd in de aankooporder.
2. De hydrostatische proef moet in overeenstemming zijn met specificatie A1016/A1016M, behalve dat bij de berekening van de hydrostatische proefdruk 64000(441.2) moet worden vervangen door 32000(220.6).
Tabel.2 Warmtebehandeling
| UNS-aanduiding | Temperatuur | Blussen |
| S31803 | 1870-2010 °F [1020-1100°C] | Snelle afkoeling in lucht of water |
| S32205 | 1870-2010 °F [1020-1100°C] | Snelle afkoeling in lucht of water |
| S31500 | 1800-1900 °F [980-1040°C] | Snelle afkoeling in lucht of water |
| S32550 | 1900 °F [1040°C] min. | Snelle afkoeling in lucht of water |
| S31200 | 1920-2010 °F [1050-1100°C] | Snelle afkoeling in water |
| S31260 | 1870-2010 °F [1020-1100°C] | Snelle afkoeling in water |
| S32001 | 1800-1950 °F [982-1066°C] | Snelle afkoeling in lucht of water |
| S32003 | 1850-2050 °F [1010-1120°C] | Snelle afkoeling in lucht of water |
| S32101 | 1870 °F min | Gedoofd in water of op andere wijze snel gekoeld |
| S32202 | 1870-1975 °F [1020-1080°C] | Snelle afkoeling in lucht of water |
| S32506 | 1870-2050 °F [1020-1120°C] | Snelle afkoeling in lucht of water |
| S32304 | 1700-1920 °F [925-1050°C] | Snelle afkoeling in lucht of water |
| S32750 | 1880-2060 °F [1025-1125°C] | Snelle afkoeling in lucht of water |
| S32760 | 2010-2085 °F [1100-1140°C] | Snelle afkoeling in lucht of water |
| S32950 | 1820-1880 °F [990-1025°C] | Snelle afkoeling in water |
| S32520 | 1975-2050 °F [1080-1120°C] | Snelle afkoeling in lucht of water |
Vereisten voor treksterkte en hardheid
11.1 Het materiaal moet voldoen aan de in tabel 4 voorgeschreven trek- en hardheidseigenschappen.
| Rang | Treksterkte, min., ksi [MPa] | Opbrengststerkte, min., ksi [MPa] | Rek in 2 in., of 50 mm, min, % | Hardheid, Max Brinell |
| S31803 | 90 [620] | 65 [450] | 25 | 290 |
| S32205 | 95 [655] | 70 [485] | 25 | 290 |
| S31500 | 92 [630] | 64 [440] | 30 | 290 |
| S32550 | 110 [760] | 80 [550] | 15 | 297 |
| S31200 | 100 [690] | 65 [450] | 25 | 280 |
| S31260 | 100 [690] | 65 [450] | 25 | 290 |
| S32001 | 90 [620] | 65 [450] | 25 | 290 |
| S32304 | 100 [690] | 65 [450] | 25 | 290 |
| S32750 | 116 [800] | 80 [550] | 15 | 310 |
| S32760 | 109 [750] | 80 [550] | 25 | 300 |
| S32950 | 100 [690] | 70 [480] | 20 | 290 |
| S32520 | 112 [770] | 80 [550] | 25 | 310 |
Voor buismateriaal met een buitendiameter van minder dan 12,7 mm gelden de rekwaarden die in tabel 4 voor bandmonsters zijn gegeven. De eisen voor mechanische eigenschappen zijn niet van toepassing op buizen met een buitendiameter kleiner dan 3,2 mm of met wanden dunner dan 0,015 mm.
Vóór A789/A789M-04 waren de waarden voor S32003 90 ksi treksterkte en 65 ksi vloeigrens.
Toelaatbare variaties in afmetingen
1 Afwijkingen in buitendiameter, wanddikte en lengte van de gespecificeerde waarden mogen de in tabel 5 voorgeschreven waarden niet overschrijden.
2 De in tabel 5 gegeven toelaatbare variaties in uitwendige diameter zijn niet voldoende om te voorzien in ovaalheid in dunwandige buizen, zoals gedefinieerd in de tabel. Bij dergelijke buizen mogen de maximum- en minimumdiameter op een doorsnede niet meer dan tweemaal de in tabel 5 aangegeven toelaatbare variatie van de buitendiameter van de nominale diameter afwijken; de gemiddelde diameter op die doorsnede moet echter nog steeds binnen de aangegeven toelaatbare variatie liggen.
Oppervlaktegesteldheid
Alle buizen moeten vrij zijn van overmatige walshuid, geschikt voor inspectie. Een lichte hoeveelheid oxidatie wordt niet beschouwd als walshuid. Eventuele speciale afwerkingsvereisten moeten worden overeengekomen tussen de fabrikant en de koper.
Productmarkering
Naast de in specificatie A1016/A1016M voorgeschreven markering moet de markering aangeven of de buis naadloos of gelast is en wat de wandaanduiding is (gemiddelde wand of minimum wand).
Verwante referenties:
1. Duplex roestvast stalen buis
2. Duplex roestvast staal
3. Super-Duplex Roestvrij Staal
4. Principe van Duplex roestvast staal
5. Hoe het Austeniet Ferriet evenwicht bereikt
6. Corrosiebestendigheid van Duplex roestvast staal
7. Scheuren door spanningscorrosie SCC van Duplex roestvast staal
8. Belemmering voor het gebruik van Duplex roestvast staal
9. Vergelijkingstabel Duplex roestvast staal
10. S32101 | S32205/S31803 | S32304 | S32750 | S32760
11. ASTM A789/A789M
12. ASTM A 790/A 790M
13. Duplex roestvast stalen buis
14. Austenitisch-ferritisch roestvast stalen buis
15. Super-Duplex roestvast staal en hun eigenschappen
16. 2507 S32750 Duplex staalpijp
17. S31803 roestvrij staalpijp
18. S32304 (1.4362) Duplexstaal
19. S32205 roestvrij staalpijp
20. 1.4462 roestvast stalen buis
21. Gebruik van roestvast staal onder hoge temperatuur raadpleeg de tabel
22. ASTM A789 S31803 Duplex Roestvrij staalpijp
23. ASTM A789 S32205 Duplex Roestvrij staalpijp
24. Duplex-de Specificatie van de Roestvrij staalpijp
25. Export ASME SA789 S32750 Stainless Steel Bright Annealing Tube