Mechanische eigenschappen roestvrij staal
Volgens ASME SA213/SA213M, ASTM A370, ASME SA789 / SA789M Mechanische eigenschappen roestvrij staal
| Rang | Treksterkte min. ksi [MPa] | Opbrengststerkte min. ksi [MPa] | Rek in 2in of 50mm lengte % (min) | Hardheid (Max) ASTM E18 Brinell | Hardheid (Max) ASTM E18 Rockwell |
| 201 | 95 [655] | 38 [260] | 35 | 219 HBW | 95 HRB |
| 304 | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 304L | 70 [485] | 25 [170] | 35 | 192 HBW | 90 HRB |
| 304H | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 304N | 80 [550] | 35 [240] | 35 | 192 HBW | 90 HRB |
| 309S | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 309H | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 310S | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 310H | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 316 | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 316L | 70 [485] | 25 [170] | 35 | 192 HBW | 90 HRB |
| 316H | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 316Ti | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 317 | 75 [515] | 30 [205] | 34 | 192 HBW | 90 HRB |
| 317L | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 321 | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 321H | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| 347 | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| TP347H | 75 [515] | 30 [205] | 35 | 192 HBW | 90 HRB |
| N08904 | 71 [490] | 31 [215] | 35 | 192 HBW | 90 HRB |
| N08020 | 80 [550] | 35 [240] | 30 | 217 HBW | 95 HRB |
| 800 N08800 Koud werk | 75 [515] | 30 [205] | 30 | 192 HBW | 90 HRB |
| 800H N08810 | 65 [450] | 25 [170] | 30 | 192 HBW | 90 HRB |
| 800HT N08811 | 65 [450] | 25 [170] | 30 | 192 HBW | 90 HRB |
| N10276 | 100 [690] | 41 [283] | 40 | ||
| N06022 | 100 [690] | 45 [310] | 45 | ||
| S31803 | 90 [620] | 65 [450] | 25 | 290 HBW | 30 HRC |
| S31803 | 90 [620] | 65 [450] | 25 | 290 HBW | 30 HRC |
| S32101 | 101 [700] Wand≤0,187 in. [5,00 mm] | 77 [530] Wand≤0,187 in. [5,00 mm] | 30 | 290 HBW | 30 HRC |
| S32205 | 95 [655] | 70 [485] | 25 | 290 HBW | 30 HRC |
| S32550 | 110 [760] | 80 [550] | 15 | 297 HBW | 31 HRC |
| S32304 | 100 [690] OD 1 in. [25 mm] en lager 87 [600] OD meer dan 1 in. [25 mm] | 65 [450] OD 1 in. [25 mm] en lager 58 [400] OD meer dan 1 in. [25 mm] | 25 25 | … 290 HBW | … 30 HRC |
| S32750 | 116 [800] | 80 [550] | 15 | 300 HBW | 32 HRC |
| S32760 | 109 [750] | 80 [550] | 25 | 300 HBW | … |
1Mpa=144,55psi
Hardheid | Hardheidsconversie berekenen | Hardheid testen | Hardheidstestmethoden | Brinellhardheid | Rockwell hardheid | Vickers hardheid | Oppervlakkige Rockwell hardheid | Shore Durometer-test | Hardheidsconversietabel | Brinell Rockwell hardheidsconversie | Koolstofstaal Gietstaal Hardheidsconversie | Rockwell oppervlakkige Brinell Vickers Shore hardheidsconversie | Hardere Weegschaal Equivalent | Zachtere schalen Equivalent | Figuur Hardheidsschalen vergelijken | Componententabel met relevante waarden voor oppervlaktehardheid | O-ring installatie drukbelasting vs hardheid Shore A schaal | De hardheid van roestvrij staal detecteren
Roestvrij Staal Mechanische Eigenschappen Specificatie:
| ASTM E10 | Standaard testmethoden voor Brinell-hardheid van metalen | |
| ASTM E18 | Standaard testmethoden voor Rockwell hardheid van metalen | |
| ASTM E112 | Standaard testmethoden voor het bepalen van de gemiddelde korrelgrootte | |
| ASTM E213 | Standaardpraktijk voor het ultrasoon testen van metalen buizen en pijpen | |
| ASTM E426 | Standaardpraktijk voor elektromagnetisch (wervelstroom) onderzoek van naadloze en gelaste buisproducten, titanium, austenitisch roestvast staal en soortgelijke legeringen | |
| ASTM A262 | Standaardpraktijken voor het detecteren van gevoeligheid voor interkristallijne aantasting in Austenitisch roestvast staal | |
| ASTM A370 | Standaard testmethoden en definities voor het mechanisch testen van staalproducten | |
| ASTM A999 | Standaardspecificatie voor algemene vereisten voor gelegeerde en roestvrij stalen buizen | |
| ASTM A1016 | Standaardspecificatie voor algemene vereisten voor buizen van ferritisch gelegeerd staal, Austenitisch gelegeerd staal en roestvrij staal |