S32304 1.4362 Mechanical Properties
Tensile Strength Properties (Minimum Values)
| °C |
Rp 0.2
MPa |
Rp 1.0
MPa |
Rm
MPa |
| 20 |
400 |
440 |
600 |
| 100 |
330 |
365 |
570 |
| 200 |
280 |
310 |
530 |
| 300 |
230 |
260 |
490 |
| °F |
Yiled Strength 0.2%
KSI |
Yiled Strength 1.0%
KSI
|
UTS
KSI |
Elongation
% |
| 68 |
58 |
64 |
87 |
25 |
| 212 |
48 |
53 |
83 |
25 |
| 392 |
41 |
45 |
77 |
20 |
| 572 |
33 |
38 |
71 |
20 |
Values obtained for hot rolled plates (wall thickness ≤ 2”). Alloy 2304 must not be used for a long time at temperatures higher than 300°C (572°F), where precipitation hardening phenomenon occurs.
Toughness Values (KCV Minimum Values)
| Temp. |
|
-50°C |
+20°C |
|
-60°F |
+70°F |
| Single |
|
75 J/cm |
90 J/cm |
|
54 ft.lbs |
65 ft. lbs |
| Average (5) |
|
90 J/cm |
150 J/cm |
|
65 ft.lbs |
87 ft.lbs |
Hardness (Typical Values)
| Average (5) |
HV10 180-230 |
HB : 180-230 |
HRC _ 20 |
S32304 Stainless Steel Tubes
S32304 S31803 S32205 S32750 Mechanical Properties
Brinell and Rockwell Hardness Conversion Chart
Hardness Testing General
Brinell Hardness Testing
Rockwell Hardness Testing
Vickers Hardness Testing
Carbon Low Alloy Steel and Cast Steel Hardness Conversion Table
Rockwell Rockwell Superficial Brinell Vickers Shore Hardness Conversion Table
General Properties
Application
Standards
Resistance to Corrosion
Physical Properties
Mechanical Properties
Structure
Welding
Processing
Machinability
ASTM A789/A789M
ASTM A 790/A 790M
Duplex Stainless Steel Pipe
LDX 2101 S32101 1.4162 Duplex Stainless Steel Tubing Pipe
S32205 S31803 1.4462 Duplex Stainless Steel Tubing Pipe
S32304 1.4362 Duplex Stainless Steel Tubing Pipe
S32760 1.4501 Stainless Steel Tube Pipe
2507 S32750 1.4410 Duplex Stainless Steel Tube Pipe
Super-Duplex Stainless Steels and their characteristics
|