Composizione chimica dell'acciaio inossidabile 304
Tabella 1. Intervalli di composizione per ASME SA 213 304 304L 304H e EN 10216-5 1.4301 1.4307 1.4948
| Grado | – | C | Mn | Si | P | S | Cr | Mo | Ni | N |
| 304/S30400 | min.max. | -0.08 | -2.0 | -1.00 | -0.045 | -0.030 | 18.0-20.0 | – | 8.0-11.0 | – |
| EN 10216-5 1.4301 | min.max. | -0.07 | -2.0 | -1.00 | -0.040 | -0.015 | 17.00-19.5 | – | 8.0-10.5 | -0.11 |
| 304L/S30403 | min.max. | -0.035 | -2.0 | -1.00 | -0.045 | -0.030 | 18.0-20.0 | – | 8.0-12.0 | – |
| EN 10216-5 1.4307 | min.max. | -0.030 | -2.0 | -1.00 | -0.040 | -0.015 | 17.5-19.5 | – | 8.0-10.0 | -0.11 |
| 304H /S30409 | min.max. | 0.04-0.10 | -2.0 | -1.00 | -0.045 | -0.030 | 18.0-20.0 | – | 8.0-11.0 | – |
| EN 10216-5 1.4948 | min.max. | 0.04-0.08 | -2.0 | -1.00 | -0.035 | -0.015 | 17.0-19.0 | – | 8.0-11.0 | -0.11 |
Data are typical and should not be construed as maximum or minimum values for specification or for final design. Data on any particular piece of material may vary from those shown herein