DIN 17456 17458 Tabella di composizione chimica
| C | C | Si | Si | Mn | Mn | P | P | S | S | Cr | Cr | Ni | Ni | Mo | Mo | N | N | Cu | Cu | Ti | Ti | Nb | Nb | ||
| min | massimo | min | massimo | min | massimo | min | massimo | min | massimo | min | massimo | min | massimo | min | massimo | min | massimo | min | massimo | min | massimo | min | massimo | ||
| DIN 17456 | 1.4301 | 0.00 | 0.070 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 17.00 | 19.00 | 8.00 | 10.50 | ||||||||||
| DIN 17456 | 1.4306 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 18.00 | 20.00 | 10.00 | 12.00 | ||||||||||
| DIN 17456 | 1.4311 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 17.00 | 19.50 | 8.50 | 11.50 | ||||||||||
| DIN 17456 | 1.4541 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 17.00 | 19.00 | 9.00 | 12.00 | 5*C | 0.70 | ||||||||
| DIN 17456 | 1.4550 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 17.00 | 19.00 | 9.00 | 12.00 | 10*C | 1.00 | ||||||||
| DIN 17456 | 1.4401 | 0.00 | 0.070 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 16.50 | 18.50 | 10.00 | 13.00 | 2.00 | 2.50 | ||||||||
| DIN 17456 | 1.4404 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 16.50 | 18.50 | 10.00 | 13.00 | 2.00 | 2.50 | ||||||||
| DIN 17456 | 1.4571 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 16.50 | 18.50 | 10.50 | 13.50 | 2.00 | 2.50 | 5*C | 0.70 | ||||||
| DIN 17456 | 1.4429 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.015 | 16.50 | 18.50 | 11.00 | 14.00 | 2.50 | 3.00 | ||||||||
| DIN 17458 | 1.4301 | 0.00 | 0.070 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 8.50 | 10.50 | ||||||||||
| DIN 17458 | 1.4306 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 10.00 | 12.50 | ||||||||||
| DIN 17458 | 1.4311 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 8.50 | 11.50 | 0.12 | 0.22 | ||||||||
| DIN 17458 | 1.4541 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 5*C | 0.80 | ||||||||
| DIN 17458 | 1.4550 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.50 | 12.00 | 10*C | 1.00 | ||||||||
| DIN 17458 | 1.4401 | 0.00 | 0.070 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.50 | 18.50 | 10.50 | 13.50 | 2.00 | 2.50 | ||||||||
| DIN 17458 | 1.4404 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.50 | 18.50 | 11.00 | 14.00 | 2.00 | 2.50 | ||||||||
| DIN 17458 | 1.4571 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.50 | 18.50 | 10.50 | 13.50 | 2.00 | 2.50 | 5*C | 0.80 | ||||||
| DIN 17458 | 1.4429 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.025 | 16.50 | 18.50 | 11.50 | 14.50 | 2.50 | 3.00 | 0.14 | 0.22 |
Tabella di composizione dell'acciaio inossidabile
Composizione chimica dell'acciaio inossidabile BS 970
BS 3100 Composizione chimica dell'acciaio inossidabile
BS 6744 Composizione e meccanica dell'acciaio inossidabile
EN 10088-2 Composizione chimica acciaio inox
Composizione chimica della lega Hastelloy
Composizione chimica della lega di nichel Monel
EN 10302 Composizione chimica degli acciai resistenti al creep
EN 10028-7 Composizione chimica dell'acciaio inossidabile piatto
EN 10283 Composizione chimica delle fusioni in acciaio inossidabile
EN 10095 Composizione chimica degli acciai resistenti al calore
EN 10269 Composizioni chimiche dell'acciaio inossidabile
Composizione chimica dell'acciaio inossidabile EN 10296-2
BS 3146-2 Composizione chimica dell'acciaio inossidabile
Composizione chimica degli acciai inossidabili resistenti al calore AISI e UNS
EN 10216-5 Composizioni chimiche degli acciai inossidabili
Tabella di composizione chimica JIS G3459 G3463