Austenitische roestvast staalsoorten
Austenitisch roestvast staal
| China GB | ISO Unified Digital Code | ASTM / ASME Rang | UNS-code | EN-code | Bedrijf Commerciële kwaliteit |
| 06H19N10 | S30408 | 304 | S30400 | 1.4301 | - |
| 07H19N10 | S30409 | 304H | S30409 | 1.4948 | - |
| 022H19N10 | S30403 | 304L | S30403 | 1.4307 | - |
| 022H19N10N | S30453 | 304LN | S30453 | 1.4311 | - |
| - | - | Super304 | S30432 | - | Super304H (NSSMC) |
| 06H18N11T | S32168 | 321 | S32100 | 1.4541 | - |
| 07H18N11T | S32169 | 321H | S32109 | 1.494 | - |
| 06H17N12M2 | S31608 | 316 | S31600 | 1.4401 | - |
| 022H17N12M2 | S31603 | 316L | S31603 | 1.4404 | - |
| 022H17N12M2N | S31653 | 316LN | S31653 | 1.4406 | - |
| 06H17N12M3T | S31668 | 316Ti | S31635 | 1.4571 | - |
| 00H17N14M2 | 316LMvD/316LUG | S31603 | 1.4435 | - | |
| 022H19N13M3 | S31703 | 317L | S31703 | 1.4438 | - |
| 022H19N16M5N | S31723 | 317LMN | S31725 | 1.4439 | - |
| 06H25N20 | S31008 | 310S | S31008 | 1.4845 | - |
| 00H19N11 | - | 304L | S30403 | 1.4307 | 3RE12 (Sandvik) |
| - | - | 310L | S31002 | 1.4335 | 2RE10 (Sandvik) |
| 20H25N20 | S31020 | 310H | S31009 | 1.4821 | |
| 16H25N20S2 | S38340 | 314 | - | 1.4841 | |
| 022H25N22M2N | S31053 | 310MoLN | S31050 | 1.4466 | 2RE69 (Sandvik) |
| - | - | 310HCbN | S31042 | - | HR3C (NSSMC) |
| 07H18N11Nb | S34749 | 347H | S34709 | 1.4942 | - |
| - | - | 347HFG | S34710 | - | - |
| 015H21N26M5H2 | S31782 | 904L | N08904 | 1.4539 | 2RK65 (Sandvik) |
| 015H20N18M6KN | S31252 | S31254 | S31254 | 1.4547 | 254SMO (Sandvik) |
| 00H20N24M6N | - | N08367 | N08367 | - | AL6XN, AL6XN plus (ATI) |
| 00H21N25M6HN | - | N08926 | N08926 | 1.4529 | - |
| 015H24N22M8Mn3HN | S32652 | S32654 | S32654 | 1.4652 | 654SMO (Outokumpu) |
| 00H22N27M7KN | - | S31277 | S31277 | - | - |
Austenitisch roestvast staal Samenstelling
| ASME | AISI UNS | NL | JIS | Cmax | Cr | Ni | Mo | Cu | Anderen |
| TP 304 | S30400 | 1.4301 | SUS 304 | 0.08 | 18.0 | 8.0 | |||
| TP 304 L | S30403 | 1.4307 | SUS 304L | 0.035 | 18.0 | 8.0 | |||
| TP 304H | S30403 | 1.4948 | SUS 304H | 0.04-0.1 | 18.0 | 8.0 | |||
| TP 321 | S32100 | 1.4541 | SUS 321 | 0.080 | 17.0 | 9.0 | 5(C+N)<Ti< 0.7 | ||
| TP 321H | S32100 | 1.4878 | SUS 321 | 0.04-0.1 | 17.0 | 9.0 | 4(C+N)<Ti< 0.7 | ||
| TP 347 | S3470 | 1.4550 | SUS 347 | 0.08 | 17.0 | 9.0 | 10×C<Nb<1,10 | ||
| TP 347H | S34709 | SUS 347 | 0.04-0.1 | 17.0 | 9.0 | 8×C<Nb<1,10 | |||
| TP 316 | S31600 | 1.4401 | SUS 316 | 0.08 | 16.0 | 10.0 | 2.0 | ||
| TP 316L | S31603 | 1.4404 | SUS 316L | 0.035 | 16.0 | 10.0 | 2.0 | ||
| TP 316H | S31609 | SUS 316H | 0.04-0.1 | 16.0 | 10.0 | 2.0 | |||
| TP 316 Ti | S31635 | 1.4571 | SUS 316Ti | 0.08 | 16.0 | 10.0 | 2.0 | N:0.10 min 5(C+N)<Ti< 0,7 | |
| TP 317 | S31700 | 1.4438 | SUS 317L | 0.08 | 18.0 | 11.0 | 3.0 | ||
| TP 317L | 31703 | 1.4438 | SUS 317L | 0.035 | 18.0 | 11.0 | 3.0 | ||
| TP 309S | S30908 | 1.4833 | SUS 309S | 0.08 | 22.0 | 12.0 | |||
| TP 310 | S31000 | 1.4841 | SUS 310 | 0.08 | 24.0 | 19.0 | |||
| TP 310S | S31008 | 1.4845 | SUS 310S | 0.08 | 24.0 | 19.0 | |||
| TP 310H | S31009 | 1.4845 | SUS 310H | 0.04-0.10 | 24.0 | 19.0 | |||
| TP 904L | N08904 | 1.4539 | SUS 904L | 0.020 | 19.0> | 23.0 | 4.0 | 1.00-2.00 |
Verwante referenties:
Austenitisch roestvast staal
Superaustenitisch roestvast staal
Austenitische roestvast staalsoorten
Austenitisch roestvast staal voor houtbevestigingen
Magnetische eigenschappen van Austenitisch roestvast staal
Vergelijkingstabel Austenitisch roestvast staal
Oppervlakteharden van Austenitisch roestvast staal met stikstof
Effect van Austenitische staalsamenstelling en warmtebehandeling
Vergeleken Austenitisch en Duplex staalsterkte en kwetsbaarheid
Spanningsverminderende warmtebehandeling voor Austenitisch roestvast staal
Mechanismemeting van werkharding van Austenitisch staal
Effect van samenstelling op magnetische permeabiliteit van austenitisch staal
Effect van koudvervormen en warmtebehandeling van Austenitisch roestvast staal