Tipi di acciaio inossidabile austenitico
Tipi di acciaio inossidabile austenitico
| Cina GB | Codice digitale unificato ISO | Grado ASTM / ASME | Codice UNS | Codice IT | Azienda di grado commerciale |
| 06Cr19Ni10 | S30408 | 304 | S30400 | 1.4301 | - |
| 07Cr19Ni10 | S30409 | 304H | S30409 | 1.4948 | - |
| 022Cr19Ni10 | S30403 | 304L | S30403 | 1.4307 | - |
| 022Cr19Ni10N | S30453 | 304LN | S30453 | 1.4311 | - |
| - | - | Super304 | S30432 | - | Super304H (NSSMC) |
| 06Cr18Ni11Ti | S32168 | 321 | S32100 | 1.4541 | - |
| 07Cr18Ni11Ti | S32169 | 321H | S32109 | 1.494 | - |
| 06Cr17Ni12Mo2 | S31608 | 316 | S31600 | 1.4401 | - |
| 022Cr17Ni12Mo2 | S31603 | 316L | S31603 | 1.4404 | - |
| 022Cr17Ni12Mo2N | S31653 | 316LN | S31653 | 1.4406 | - |
| 06Cr17Ni12Mo3Ti | S31668 | 316Ti | S31635 | 1.4571 | - |
| 00Cr17Ni14Mo2 | 316LMoD/316LUG | S31603 | 1.4435 | - | |
| 022Cr19Ni13Mo3 | S31703 | 317L | S31703 | 1.4438 | - |
| 022Cr19Ni16Mo5N | S31723 | 317LMN | S31725 | 1.4439 | - |
| 06Cr25Ni20 | S31008 | 310S | S31008 | 1.4845 | - |
| 00Cr19Ni11 | - | 304L | S30403 | 1.4307 | 3RE12(Sandvik) |
| - | - | 310L | S31002 | 1.4335 | 2RE10(Sandvik) |
| 20Cr25Ni20 | S31020 | 310H | S31009 | 1.4821 | |
| 16Cr25Ni20Si2 | S38340 | 314 | - | 1.4841 | |
| 022Cr25Ni22Mo2N | S31053 | 310MoLN | S31050 | 1.4466 | 2RE69(Sandvik) |
| - | - | 310HCbN | S31042 | - | HR3C(NSSMC) |
| 07Cr18Ni11Nb | S34749 | 347H | S34709 | 1.4942 | - |
| - | - | 347HFG | S34710 | - | - |
| 015Cr21Ni26M5Cu2 | S31782 | 904L | N08904 | 1.4539 | 2RK65(Sandvik) |
| 015Cr20Ni18Mo6CuN | S31252 | S31254 | S31254 | 1.4547 | 254SMO (Sandvik) |
| 00Cr20Ni24Mo6N | - | N08367 | N08367 | - | AL6XN, AL6XN plus (ATI) |
| 00Cr21Ni25Mo6CuN | - | N08926 | N08926 | 1.4529 | - |
| 015Cr24Ni22Mo8Mn3CuN | S32652 | S32654 | S32654 | 1.4652 | 654SMO(Outokumpu) |
| 00Cr22Ni27Mo7CuN | - | S31277 | S31277 | - | - |
Composizione dell'acciaio inossidabile austenitico
| ASME | AISI UNS | IT | JIS | Cmax | Cr | Ni | Mo | Cu | Altri |
| TP 304 | S30400 | 1.4301 | SUS 304 | 0.08 | 18.0 | 8.0 | |||
| TP 304 L | S30403 | 1.4307 | SUS 304L | 0.035 | 18.0 | 8.0 | |||
| TP 304H | S30403 | 1.4948 | SUS 304H | 0.04-0.1 | 18.0 | 8.0 | |||
| TP 321 | S32100 | 1.4541 | SUS 321 | 0.080 | 17.0 | 9.0 | 5(C+N)<Ti< 0.7 | ||
| TP 321H | S32100 | 1.4878 | SUS 321 | 0.04-0.1 | 17.0 | 9.0 | 4(C+N)<Ti< 0.7 | ||
| TP 347 | S3470 | 1.4550 | SUS 347 | 0.08 | 17.0 | 9.0 | 10×C<Nb<1,10 | ||
| TP 347H | S34709 | SUS 347 | 0.04-0.1 | 17.0 | 9.0 | 8×C<Nb<1,10 | |||
| TP 316 | S31600 | 1.4401 | SUS 316 | 0.08 | 16.0 | 10.0 | 2.0 | ||
| TP 316L | S31603 | 1.4404 | SUS 316L | 0.035 | 16.0 | 10.0 | 2.0 | ||
| TP 316H | S31609 | SUS 316H | 0.04-0.1 | 16.0 | 10.0 | 2.0 | |||
| TP 316 Ti | S31635 | 1.4571 | SUS 316Ti | 0.08 | 16.0 | 10.0 | 2.0 | N:0,10 min 5(C+N)<Ti< 0,7 | |
| TP 317 | S31700 | 1.4438 | SUS 317L | 0.08 | 18.0 | 11.0 | 3.0 | ||
| TP 317L | 31703 | 1.4438 | SUS 317L | 0.035 | 18.0 | 11.0 | 3.0 | ||
| TP 309S | S30908 | 1.4833 | SUS 309S | 0.08 | 22.0 | 12.0 | |||
| TP 310 | S31000 | 1.4841 | SUS 310 | 0.08 | 24.0 | 19.0 | |||
| TP 310S | S31008 | 1.4845 | SUS 310S | 0.08 | 24.0 | 19.0 | |||
| TP 310H | S31009 | 1.4845 | SUS 310H | 0.04-0.10 | 24.0 | 19.0 | |||
| TP 904L | N08904 | 1.4539 | SUS 904L | 0.020 | 19.0> | 23.0 | 4.0 | 1.00-2.00 |
Riferimenti correlati:
Acciaio inossidabile austenitico
Acciaio inossidabile superaustenitico
Tipi di acciaio inossidabile austenitico
Acciaio inossidabile austenitico per fissaggi in legno
Proprietà magnetiche dell'acciaio inossidabile austenitico
Tabella comparativa dei gradi di acciaio inossidabile austenitico
Tempra superficiale di acciaio inossidabile austenitico con azoto
Effetto della composizione austenitica dell'acciaio e del trattamento termico
Resistenza e vulnerabilità degli acciai austenitici e duplex a confronto
Trattamento termico antistress per l'acciaio inossidabile austenitico
Misurazione del meccanismo di indurimento in lavoro dell'acciaio austenitico
Effetto della composizione sulla permeabilità magnetica degli acciai austenitici
Effetto del lavoro a freddo e del trattamento termico dell'acciaio inossidabile austenitico