Tabla de composición química del acero inoxidable
Según ASTM A213, ASTM A269, ASTM A312ASME SA376, ASTM A511, ASTM A789, ASTM A790
Aleaciones base níquel:
Aleación 20 (UNS N08020), Monel 200 (UNS 02200), Monel 400 (UNS N04400), Incoloy 800 (UNS N08800), Incoloy 800H (UNS N08810), Incoloy 800HT (UNS N08811), Incoloy 825 (UNS N08825), Inconel 600 (UNS N06600), 4J29, 4J36, GH3030, GH3039, C276 (UNS N10276)
| Grado | C | Si | Mn | P | S | Cr | Ni | Mo | N | Cu | Ti | Nb | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| min | max | min | max | min | max | min | max | min | max | min | max | min | max | min | max | min | max | min | max | min | max | min | max | |||
| A312 | TP304 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A312 | TP304H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A312 | TP304L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 13.00 | |||||||||||
| A312 | TP310S | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 24.00 | 26.00 | 19.00 | 22.00 | 0.00 | 0.75 | |||||||||
| A312 | TP316 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A312 | TP316H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 11.00 | 15.00 | 2.00 | 3.00 | |||||||||
| A312 | TP316L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A312 | TP317 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 10.00 | 14.00 | 3.00 | 4.00 | |||||||||
| A312 | TP317L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 11.00 | 15.00 | 3.00 | 4.00 | |||||||||
| A312 | TP321 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 5×(C+N) | 0.70 | |||||||||
| A312 | TP321H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 4×(C+N) | 0.70 | |||||||||
| A312 | TP347 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 13.00 | 10×C | 1.00 | |||||||||
| A312 | TP347H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 13.00 | 8×C | 1.00 | |||||||||
| A213 | TP304 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A213 | TP304H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A213 | TP304L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 12.00 | |||||||||||
| A213 | TP310S | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 24.00 | 26.00 | 19.00 | 22.00 | |||||||||||
| A213 | TP316 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A213 | TP316L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A213 | TP317 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 11.00 | 15.00 | 3.00 | 4.00 | |||||||||
| A213 | TP317L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 11.00 | 15.00 | 3.00 | 4.00 | |||||||||
| A213 | TP321 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 5×C | 0.70 | |||||||||
| A213 | TP347 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 20.00 | 9.00 | 13.00 | 10×C | 1.10 | |||||||||
| A213 | TP347H | 0.040 | 0.100 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 20.00 | 9.00 | 13.00 | 8×C | 1.10 | |||||||||
| A269 | TP304 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A269 | TP304L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 12.00 | |||||||||||
| A269 | TP316 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A269 | TP316L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 15.00 | 2.00 | 3.00 | |||||||||
| A269 | TP317 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 11.00 | 15.00 | 3.00 | 4.00 | |||||||||
| A269 | TP321 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 5×C | 0.70 | |||||||||
| A269 | TP347 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 12.00 | 10×C | 1.10 | |||||||||
| A511 | MT304 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A511 | MT304L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 13.00 | |||||||||||
| A511 | MT310S | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 24.00 | 26.00 | 19.00 | 22.00 | |||||||||||
| A511 | MT316 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 16.00 | 18.00 | 11.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A511 | MT316L | 0.00 | 0.035 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 16.00 | 18.00 | 10.00 | 15.00 | 2.00 | 3.00 | |||||||||
| A511 | MT317 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 18.00 | 20.00 | 11.00 | 14.00 | 3.00 | 4.00 | |||||||||
| A511 | MT321 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 17.00 | 20.00 | 9.00 | 13.00 | 5×C | 0.60 | |||||||||
| A511 | MT347 | 0.00 | 0.080 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.030 | 17.00 | 20.00 | 9.00 | 13.00 | 10×C | 1.00 | |||||||||
| A213 | UNS N08904 | 0.00 | 0.020 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.040 | 0.00 | 0.03 | 19.00 | 23.00 | 23.00 | 28.00 | 4.00 | 5.00 | 1.00 | 2.00 | |||||||
| A376 | TP304 | 0.00 | 0.080 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A376 | TP304H | 0.040 | 0.100 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 18.00 | 20.00 | 8.00 | 11.00 | |||||||||||
| A376 | TP316 | 0.00 | 0.080 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 11.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A376 | TP316H | 0.040 | 0.100 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 16.00 | 18.00 | 11.00 | 14.00 | 2.00 | 3.00 | |||||||||
| A376 | TP321 | 0.00 | 0.080 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 13.00 | 5×C | 0.70 | |||||||||
| A376 | TP321H | 0.040 | 0.100 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 13.00 | 4×C | 0.70 | |||||||||
| A376 | TP347 | 0.00 | 0.080 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 19.00 | 9.00 | 13.00 | 10×C | 1.10 | |||||||||
| A376 | TP347H | 0.040 | 0.100 | 0.00 | 0.75 | 0.00 | 2.00 | 0.00 | 0.045 | 0.00 | 0.030 | 17.00 | 1900 | 9.00 | 13.00 | 8×C | 1.10 | |||||||||
| A790 | S31803 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.030 | 0.00 | 0.020 | 21.00 | 23.00 | 4.50 | 6.50 | 2.50 | 3.50 | 0.08 | 0.20 | |||||||
| A789 | S31803 | 0.00 | 0.030 | 0.00 | 1.00 | 0.00 | 2.00 | 0.00 | 0.030 | 0.00 | 0.020 | 21.00 | 23.00 | 4.50 | 6.50 | 2.50 | 3.50 | 0.08 | 0.20 |
Tabla de composición del acero inoxidable
Composición química del acero inoxidable BS 970
BS 3100 Composición química del acero inoxidable
BS 6744 Composición y mecánica del acero inoxidable
EN 10088-2 Composición química Acero inoxidable
Composición química de la aleación Hastelloy
Composición química de la aleación de níquel y monel
EN 10302 Composición química del acero resistente a la fluencia
EN 10028-7 Composición química del acero inoxidable plano
EN 10283 Composición química de la fundición de acero inoxidable
EN 10095 Composición química del acero refractario
EN 10269 Composiciones químicas del acero inoxidable
Composición química del acero inoxidable EN 10296-2
BS 3146-2 Composición química del acero inoxidable
Composición química de los aceros inoxidables resistentes al calor AISI y UNS
EN 10216-5 Composiciones químicas de los aceros inoxidables
JIS G3459 G3463 Tabla de composición química
DIN 17456 17458 Tabla de composición química