Aluminium Alloys Chemical Composition
| Grade. |
|
Al |
Mg |
Mn |
Fe |
Si |
Cu |
Zn |
Cr |
Ti |
Rp.
02 |
Rm |
E |
Notes |
| |
|
wt% |
wt% |
wt% |
wt% |
wt% |
wt% |
wt% |
wt% |
wt% |
MPa |
>MPa |
GPa |
|
| AW-2011 |
T3 |
Remain |
|
- |
|
<=0,4 |
5,0 - 6,0 |
<= 0,3 |
- |
- |
290 |
365 |
72,5 |
Screws,
Nuts,
Machined component |
| AW-2011 |
T6 |
Remain |
|
- |
|
<=0,4 |
5,0 - 6,0 |
<= 0,3 |
- |
- |
300 |
395 |
72,5 |
|
| AW-6016 |
0 |
Remain |
0,25
-
0,6 |
<=0,2 |
<=0,5 |
1,0
-
1,5 |
<= 0,2 |
<= 0,20 |
<= 0,1 |
<= 1,15 |
50 |
100 |
69,5 |
Aluminium
Car Body
sheets |
| AW-6016 |
T5 |
Remain |
0,25
-
0,6 |
<=0,2 |
<=0,5 |
1,0
-
1,5 |
<= 0,2 |
<= 0,20 |
<= 0,1 |
<= 1,15 |
185 |
220 |
69,5 |
|
| AW-7020 |
0 |
Remain |
1,0
-
1,4 |
0,05 -0,5 |
<=0,4 |
<=
0,35 |
<=0,2 |
4,0 - 5,0 |
0,1 - 0,35 |
**
0,08
-
0,2 |
80 |
180 |
70 |
Welded
Structural Component
,(**Zr + Ti) |
| AW-7020 |
T5 |
Remain |
1,0
-
1,4 |
0,05 -0,5 |
<= 0,4 |
<= 0,35 |
<= 0,2 |
4,0 - 5,0 |
0,1 - 0,35 |
**
0,08
-
0,2 |
315 |
375 |
70 |
|
Aluminium Alloys Chemical Composition Chart
|
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Other |
Other |
Al |
|
Each |
Total |
Min. |
|
1070 |
0.20 |
>0.25 |
0.04 |
0.03 |
0.03 |
— |
0.04 |
0.03 |
0.03 |
— |
99.70 |
|
1060 |
0.25 |
>0.35 |
0.05 |
0.03 |
0.03 |
— |
0.05 |
0.03 |
0.03 |
— |
99.60 |
|
|
|
1050 |
0.25 |
>0.40 |
0.05 |
0.05 |
0.05 |
— |
0.05 |
0.03 |
0.03 |
— |
99.50 |
|
1350 |
0.10 |
>0.40 |
0.05 |
0.01 |
— |
0.01 |
0.05 |
— |
0.03 |
0.10 |
99.50 |
|
1145 |
0.55 Si + Fe |
0.05 |
0.05 |
0.05 |
— |
0.05 |
0.03 |
0.03 |
— |
99.45 |
|
1100 |
0.95 Si + Fe |
0.05-0.20 |
0.05 |
— |
— |
0.10 |
— |
0.05 |
0.15 |
99.00 |
|
2024 |
>0.50 |
0.50 |
3.8-4.9 |
=0.30-0.9 |
1.2-1.8 |
>0.10 |
>0.25 |
>0.15 |
>0.05 |
>0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
3003 |
0.6 |
0.7 |
0.05-0.20 |
1.0-1.5 |
— |
— |
0.10 |
— |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
3004 |
0.30 |
0.7 |
0.25 |
1.0-1.5 |
0.8-1.3 |
— |
0.25 |
— |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
3005 |
0.6 |
0.7 |
0.30 |
1.0-1.5 |
0.20-0.6 |
0.10 |
0.25 |
0.10 |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
3104 |
0.6 |
0.8 |
0.05-0.25 |
0.8-1.4 |
0.8-1.3 |
— |
0.25 |
0.10 |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
4004 |
9.0-10.5 |
0.8 |
0.25 |
0.10 |
1.0-2.0 |
— |
0.20 |
— |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
4104 |
9.0-10.5 |
0.8 |
0.25 |
0.10 |
1.0-2.0 |
— |
0.20 |
— |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
4043 |
4.5-6.0 |
0.8 |
0.30 |
0.05 |
0.05 |
— |
0.10 |
0.20 |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
4045 |
9.0-11.0 |
0.8 |
0.30 |
0.05 |
0.05 |
— |
0.10 |
0.20 |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
5005 |
0.30 |
0.7 |
0.20 |
0.20 |
0.50-1.1 |
0.10 |
0.25 |
— |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
5050 |
0.40 |
0.7 |
0.20 |
0.10 |
1.1-1.8 |
0.10 |
0.25 |
— |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
5052 |
0.25 |
0.40 |
0.10 |
0.10 |
2.2-2.8 |
0.15-0.35 |
0.10 |
— |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
5252 |
0.08 |
0.10 |
0.10 |
0.10 |
2.2-2.8 |
— |
0.05 |
— |
0.03 |
0.10 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
5056 |
0.30 |
0.40 |
0.10 |
0.05-0.20 |
4.5-5.6 |
0.05-0.20 |
0.10 |
— |
0.05 |
0.15 |
Rem. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
5657 |
0.08 |
0.10 |
0.10 |
0.03 |
0.6-1.0 |
— |
0.05 |
— |
0.02 |
0.05 |
Rem. |
|
5182 |
0.20 |
0.35 |
0.15 |
0.20-0.50 |
4.0-5.0 |
0.10 |
0.25 |
0.10 |
0.05 |
0.15 |
Rem. |
|
6061 |
0.40-0.8 |
0.7 |
0.15-0.40 |
0.15 |
0.8-1.2 |
0.04-0.35 |
0.25 |
0.15 |
0.05 |
0.15 |
Rem. |
|
7075 |
0.40 |
0.50 |
1.2-2.0 |
0.30 |
2.1-2.9 |
0.18-0.28 |
5.1-6.1 |
0.20 |
0.05 |
0.15
|
Rem.
|
Rem.=Remainder
|