Hastelloy C276 Pipe Theoretical Internal Bursting Pressure Chart
Theoretical Internal Bursting Pressures (Barlow's Formula),Hastelloy C276 Pipes Theoretical Internal Bursting Pressure Table
| |
Schedule 5C |
Schedule 10S |
Schedule 40S |
Schedule 80S |
| Nominal Pipe Size |
Nominal O.D. (Inches) |
Wall (Inches) |
Pressure(PSI) |
Wall (Inches) |
Pressure (PSI) |
Wall (Inches) |
Pressure (PSI)> |
Wall (Inches) |
Pressure (PSI) |
| 1/8 |
.405 |
|
|
.049 |
18150 |
.068 |
25175 |
.095 |
35175 |
| 1/4 |
.540 |
|
|
.065 |
18050 |
.088 |
24450 |
.119 |
33050 |
| 3/8 |
.675 |
|
|
.065 |
14450 |
.091 |
20225 |
.126 |
28000 |
| 1/2 |
.84 |
.065 |
11600 |
.083 |
14825 |
.109 |
19475 |
.147 |
26250 |
| 3/4 |
1.05 |
.065 |
9275 |
.083 |
11850 |
.113 |
16150 |
.154 |
2200 |
| 1 |
1.315 |
.065 |
7425 |
.109 |
12450 |
.133 |
15175 |
.179 |
20425 |
| 1 1/4 |
1.66 |
.065 |
5875 |
.109 |
9850 |
.14 |
12650 |
.191 |
17250 |
| 1 1/2 |
1.900 |
.065 |
5125 |
.109 |
8600 |
.145 |
11450 |
.20 |
15800 |
| 2 |
2.375 |
.065 |
4100 |
.109 |
6875 |
.154 |
9750 |
.218 |
13775 |
| 2 1/2 |
2.875 |
.083 |
4325 |
.12 |
6250 |
.203 |
10600 |
.276 |
14400 |
| 3 |
3.5 |
.083 |
3550 |
.12 |
5150 |
.216 |
9250 |
|
|
| 3 1/2 |
4 |
.083 |
3100 |
.12 |
4500 |
.226 |
8475 |
|
|
| 4 |
4.5 |
.083 |
2750 |
.12 |
4000 |
.237 |
7900 |
|
|
| 5 |
5.563 |
.109 |
2950 |
.134 |
3625 |
.258 |
6950 |
|
|
| 6 |
6.625 |
.109 |
2475 |
.134 |
3050 |
.28 |
6350 |
|
|
| 8 |
8.625 |
.109 |
1900 |
.148 |
2575 |
322 |
5600 |
|
|
| 10 |
1.75 |
.134 |
1875 |
.165 |
2300 |
.365 |
5100 |
|
|
| 12 |
12.75 |
.156 |
1825 |
.18 |
2125 |
.375 |
4400 |
|
|
| 14 |
14 |
.156 |
1675 |
.188 |
2025 |
|
|
|
|
| 16 |
16 |
.165 |
1550 |
.188 |
1775 |
|
|
|
|
| 18 |
18 |
.165 |
1375 |
.188 |
1575 |
|
|
|
|
| 20 |
20 |
.188 |
1400 |
.218 |
1625 |
|
|
|
|
| 24 |
24 |
.218 |
1375 |
.25 |
1550 |
|
|
|
|
| 30 |
30 |
.25 |
1250 |
.312 |
1550 |
|
|
|
|
The bursting pressure information for reference only. TubingChina in not liable for any damages that may result from the use of this information.
|
|
|