DIN 17459 specifies technical delivery conditions for seamless circular tubes made from high temperature austenitic stainless steel as specified in table. 1. Such stainless steel tube are intended primarily to be used in high-pressure applications where elevated temperature and high mechanical stresses are involved (e.g. in the construction of pressure boilers, pressure vessels, pipelines, and in the chemical industry). Material Chemical composition (%) degignation number C Si Mn P S Ni Cr Mo Ni others X 6 CrNi 18 11 1.4948 0.04 to 0.08 ≤0.75 ≤2.0 0.035 0.015 17.0 to 19.0 – 10.0 to 12.0   X 3 CrNiN 18 11 1.4949 ≤0.04 ≤0.75 ≤2.0 0.035 0.015 0.10 to 0.18 17.0 to 19.0 0.50 to 0.60 9.5 to 11.5   X 8 CrNiTi 18 10 1.4941 0.04 to 0.10 ≤0.75 ≤2.0 0.035 0.015 17.0 to 18.5 – 9.5 to 11.5 Ti: ≥5 x %Cto ≤  0.80B: 0.0015 to 0.0050 X6CrNiMo 17 13 1.4919 0.04 to 0.08 ≤0.75 ≤2.0 0.035…

The table shown is based on the reference data presented in EN 10088-1. Only a sample of the information available is shown. This is intended to show the scope of information available through representative figures for the most commonly used stainless steel tube types. A separate table indicates some of the grades that have been grouped together.Physical Properties Table Steel Types (AISI) Density Modulus Expansion Conductivity Specific Heat Resistivity . . 20C 400C . . . . Ferritic stainless steels 410S 7700 220 195 10.5 30 460 0.60 430 7700 220 195 10.0 25 460 0.70 444 7700 220 195 10.4 23 430 0.8 Martensitic and precipitation hardening stainless steels 410 7700 215 190 10.5 30 460 0.60 440 7700 215 190 10.4 15 430 0.8 630 7800 200 170 10.9 16 500 0.71 Austenitic stainless steel 304 7900 200 172 16.0 15 500 0.73 316 8000 200 172 16.0 15 500 0.75 ‘6%Mo’ 8000…

ASTM A595 Standard Specification for Steel Tubes, Low-Carbon or High-Strength Low-Alloy, Tapered for Structural Use covers three grades of seam-welded, round, tapered steel tubes for structural use. Grades A and B are of low-carbon steel or high-strength low-alloy steel composition and Grade C is of weather-resistance steel composition. The tube steel shall be hot-rolled aluminum-semikilled or fine-grained killed sheet or plate manufactured by one or more of the following processes: open-hearth, basic-oxygen, or electric-furnace. The tubes shall be made from trapezoidal sheet or plate that is preformed and then seam welded. They shall be brought to final size and properties by roll compressing cold on a hardened mandrel. A tensile test shall be done to determine the yield strength and the ultimate tensile strength of the tubes. 1.1 This specification covers three grades of seam-welded, round, tapered steel tubes for structural use. Grades A and B are of low-carbon steel or high-strength low-alloy steel composition and Grade C…

ASTM A790 mencakup pipa baja tahan karat dupleks feritik / austenitik yang dilas tanpa sambungan dan jahitan lurus untuk layanan korosif umum, dengan penekanan khusus pada ketahanan terhadap retak korosi tegangan. Pipa harus dibuat dengan proses pengelasan tanpa sambungan atau otomatis, tanpa penambahan logam pengisi dalam operasi pengelasan. Analisis panas harus dilakukan untuk menentukan persentase elemen yang ditentukan. Uji tegangan, uji pengerasan, uji perataan, uji hidrostatik dan uji listrik tidak rusak harus dilakukan untuk memenuhi persyaratan yang ditentukan. Abstrak ini adalah ringkasan singkat dari standar yang direferensikan. Ini hanya bersifat informasi dan bukan bagian resmi dari standar; teks lengkap dari standar itu sendiri harus dirujuk untuk penggunaan dan penerapannya. Spesifikasi ini mencakup pipa baja tahan karat feritik / austenitik yang dilas tanpa sambungan dan jahitan lurus yang dimaksudkan untuk layanan korosif umum, dengan penekanan khusus pada ketahanan terhadap retak korosi tegangan. Baja ini rentan terhadap penggetasan jika digunakan dalam waktu lama pada suhu tinggi. Persyaratan tambahan opsional...

DSTU B A.3.2-12:2009 SSBP. Sistem ventilasi. Kaliper DSTU GOST 166:2009 (ISO 3599-76). Spesifikasi teknis (GOST 166-89 (ISO 3599-76), IDT) DSTU EN 473:2012 Kontrol non-invasif. Kualifikasi dan sertifikasi personel. Ketentuan umum (EN 473: 2008, IDT) DSTU 2680-94 Pipa canai mulus yang terbuat dari baja dan paduan. Terminologi dan identifikasi cacat permukaan DSTU 2841-94 (GOST 27809-95) Baja Chavun i. Metode analisis spektrografi DSTU 3124-95 Pipa yang terbuat dari baja dan paduan. Pengikatan dan persiapan sampel untuk gudang bahan kimia. Ketentuan dasar DSTU 4179-2003 Kaset bergetar logam. Keterampilan teknis (GOST 7502-98, MOD) DSTU GOST 6507: 2009 Mikrometer. Spesifikasi DSTU 7238: 2011 Sistem standar keselamatan. Buat zakhist kolektif untuk orang-orang yang bekerja. Klasifikasi Zagalni vimogi ta klasifikasi DSTU 7239:2011 Sistem standar keselamatan. Tetapkan zakhist individu. Klasifikasi Zagalni vimogi ta klasifikasi DSTU ISO 7438: 2005 Bahan logam. Pengujian untuk zgin (ISO 7438: 1985, IDT) DSTU ISO 8496-2002 Bahan logam. Terompet. Pengujian untuk menarik cincin dengan dua batang paralel (ISO 8496: 1988, IDT) DSTU GOST 12344: 2005 Baja paduan dan paduan tinggi. Metode untuk mendesain vugletsiu (GOST 12344-2003, ...

Inspeksi permukaan luar pipa dilakukan secara visual tanpa menggunakan alat pembesar. Permukaan dalam pipa dengan diameter dalam 70 mm atau lebih diperiksa dengan menggunakan periskop atau sistem video. Diperbolehkan untuk memeriksa permukaan bagian dalam pipa tanpa menggunakan instrumen, dengan menggunakan alat penerangan di kedua ujung pipa terhadap cahaya. Untuk pipa dengan diameter internal kurang dari 70 mm, serta pipa dengan diameter internal 70 mm atau lebih yang belum diperiksa dengan periskop, pabrikan menjamin bahwa permukaan internal pipa memenuhi persyaratan spesifikasi ini berdasarkan hasil yang memuaskan dari inspeksi ultrasonik 100%. Klasifikasi cacat dilakukan sesuai dengan DSTU 2680 (OST 14-82 [18]). Kedalaman cacat diperiksa setelah pengarsipan dan pengukuran selanjutnya. Dinding

Di bidang baja tahan karat, biasanya 304 disebut TP304, 304L disebut 304L, 316L disebut TP316L. Sebagai contoh: ASTM A312 TP304, ASME SA213 TP304L, ASME SA213 TP316L. Jadi, apa arti "TP"? TP adalah singkatan dari Tipe. Alasannya adalah AISI (Institut Besi dan Baja Amerika) mengklasifikasikan Baja Tahan Karat dalam Tipe. Untuk alasan yang sama, terkadang 304, 304, L316L, akan disebut AISI 304, AISI 304L, AISI 316L.

OD: 17.15 - 508mm (3/8 INCH hingga 20 INCH) WT: 0,5 - 60 mm, Jadwal 10-an, 20, 40-an, 40, 60, 80-an, 80, 100, 120, 140, 160, XXH.Kapasitas Produksi: 500 MT / Bulan Guanyu Tube adalah produsen khusus ASTM A312 TP304, ASTM A312 TP304L, ASTM A312 TP316, ASTM A312 TP316L, ASTM A312 TP321, ASTM A312 TP310S, ASTM A312 TP304 TP304L TP304H TP316 TP316L TP317L TP321 TP316Ti TP347 TP347H TP310S TP309S Pemasok Pipa Baja Tahan Karat. Ini dikeluarkan di bawah penunjukan tetap ASTM A312; angka yang segera mengikuti penunjukan menunjukkan tahun adopsi asli atau, dalam kasus revisi, tahun revisi terakhir. Angka dalam tanda kurung menunjukkan tahun persetujuan ulang terakhir. Tanda superskrip epsilon menunjukkan perubahan editorial sejak revisi atau persetujuan ulang terakhir. Ini mencakup pipa baja tahan karat austenitik tanpa sambungan, jahitan lurus, dan dilas dengan pengerjaan dingin untuk suhu tinggi dan layanan korosif umum. Ketika kriteria uji dampak untuk layanan suhu rendah akan ...

Komposisi Kimia ASTM A213 / ASME SA 213 317 317L 317LM 317LMN Baja Tahan Karat Kelas C Mn P Sulfur Si Cr Nikel Mo N Cu Berat % 317 S31700 18.00 11.00 3.00 Min. 0.08 2.00 0.045 0.030 1.00 20.00 15.00 4.00 Maks. 317L S31703 18,00 11,00 3,00 Min. 0,035 2,00 0,045 0,030 1,00 20,00 15,00 4,00 Maks. 317LM S31725 18.00 13.50 4.00 Min. 0,03 2,00 0,045 0,030 1,00 20,00 17,50 5,00 0,20 0,75 Maks. 317LMN S31726 17,00 13,50 4,00 0,10 Min. 0.03 2.00 0.045 0.030 1.00 20.00 17.50 5.00 0.20 0.75 Maks. EN 10216-5 1,4439 16,50 12,50 4,00 Min. 0,030 2,00 0,040 0,015 1,00 18,50 14,50 5,00 Maks. EN 10217-7 1,4438 17,50 13,00 3,00 Min. 0,030 2,00 0,045 0,030 1,00 19,50 16,00 4,00 Maks. Sifat Mekanis dari Tabung Baja Tahan Karat 317 317L Tabung Tarik ...

Komposisi Kimiawi ASME SA213 304 304L 304H dan EN 10216-5 1.4301 1.4307 1.4948 Grade - C Mn Si P S Cr Mo Ni N 304 / S30400 min.maks. -0,08 -2,0 -1,00 -0,045 -0,030 18,0-20,0 - 8,0-11,0 - EN 10216-5 1,4301 min.maks. -0,07 -2,0 -1,00 -0,040 -0,015 17,00-19,5 - 8,0-10,5 -0,11 304L / S30403 min.maks. -0,035 -2,0 -1,00 -0,045 -0,030 18,0-20,0 - 8,0-12,0 - EN 10216-5 1,4307 min.maks. -0,030 -2,0 -1,00 -0,040 -0,015 17,5-19,5 - 8,0-10,0 -0,11 304H / S30409 min.maks. 0,04-0,10 -2,0 -1,00 -0,045 -0,030 18,0-20,0 - 8,0-11,0 - EN 10216-5 1,4948 min.maks. 0,04-0,08 -2,0 -1,00 -0,035 -0,015 17,0-19,0 - 8,0-11,0 -0,11 Sifat Umum TP304L Komposisi Kimia TP304L Ketahanan terhadap Korosi TP304L Sifat Fisik TP304L Sifat Mekanik TP304L Pengelasan TP304L Perlakuan Panas TP304L Pembersihan Pipa dan Pipa304/304LN / 304H

Kami adalah produsen khusus ASME SA249 ASTM A249 TP304, ASTM A249 TP304L, ASTM A249 TP304H, ASTM A249 TP316, ASTM A249 TP316L, ASTM A249 TP316H, ASTM A249 TP316Ti, ASTM A249 TP321 TP321H, ASTM A249 TP309H TP309S, ASTM A249 TP310S TP 310H, ASTM A249 TP347 Tabung Dilas dan Pipa Dilas ASTM A249. Apa itu ASTM A249 ASME SA249? ASTM A249 menetapkan spesifikasi standar untuk tabung las dengan ketebalan dinding nomina dan tabung las yang dikerjakan dengan sangat dingin yang terbuat dari baja austenitik dengan berbagai tingkatan yang ditujukan untuk penggunaan seperti boiler, superheater, penukar panas, atau tabung kondensor. Analisis panas dan produk harus sesuai dengan persyaratan komposisi kimia untuk karbon, mangan, fosfor, belerang, silikon, kromium, nikel, molibdenum, nitrogen, tembaga, dan lainnya. Semua bahan harus dilengkapi dengan kondisi perlakuan panas sesuai dengan suhu larutan dan metode pendinginan yang diperlukan. ASTM A249 Benda Uji Tubing Ketika perlakuan panas akhir dalam tungku kontinu, jumlah ...

PT Test Standard International Organization for Standardization (ISO) ISO 3059, Pengujian tidak merusak - Pengujian penetrasi dan pengujian partikel magnetik - Melihat kondisi ISO 3452-1, Pengujian tidak merusak. Pengujian penetrasi. Bagian 1. Prinsip-prinsip umum ISO 3452-2, Pengujian tidak merusak - Pengujian penetran - Bagian 2: Pengujian bahan penetran ISO 3452-3, Pengujian tidak merusak - Pengujian penetran - Bagian 3: Blok uji referensi ISO 3452-4, Pengujian tidak merusak - Pengujian penetran - Bagian 4: Peralatan ISO 3452-5, Pengujian tidak merusak - Pengujian penetrasi - Bagian 5: Pengujian penetrasi pada suhu lebih tinggi dari 50 ° C ISO 3452-6, Pengujian tidak merusak - Pengujian penetrasi - Bagian 6: Pengujian penetrasi pada suhu lebih rendah dari 10 ° C ISO 10893-4: Pengujian tabung baja yang tidak merusak. Inspeksi penetran cair pada tabung baja tanpa sambungan dan yang dilas untuk mendeteksi ketidaksempurnaan permukaan. ISO 12706, Pengujian tidak merusak - Pengujian penetrasi - Kosakata ISO 23277, Pengujian pengelasan tidak merusak - Pengujian penetrasi pengelasan - Tingkat penerimaan Komite Eropa untuk Standardisasi (CEN) EN 1371-1, Pendirian - Inspeksi penetrasi cair ...

Apa itu ASTM A269 dan ASTM A312 / ASME SA312? Spesifikasi Standar ASTM A269 / A269M untuk Pipa Baja Tahan Karat Austenitik Seamless dan Dilas untuk Layanan Umum Spesifikasi Standar ASTM A312 / A312M untuk Pipa Baja Tahan Karat yang Dilas, Dilas, dan Pipa Baja Tahan Karat Austenitik yang Dikerjakan dengan Sangat Dingin StandardItem ASTM A213 ASTM A269 ASTM A312 Grade 304 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H 304 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H 304 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H Kekuatan Luluh (Mpa) ≥170 ； ≥205 ≥170 ； ≥205 ≥170 ； ≥205 Kekuatan Tarik (Mpa) ≥485 ； ≥515 ≥485 ； ≥515 ≥485 ； ≥515 Perpanjangan (%) ≥35 ≥35 ≥35 Uji Hidrostatis OD (mm) Tekanan maks (MPa) OD (mm) Tekanan maks (MPa) OD (mm) Tekanan maks (MPa) D <25.4, 7Mpa D <25,4, 7Mpa D≤88,9, 17MPa 25,4≤D <38,1, 10Mpa 25,4≤D <38,1, 10Mpa 38,1≤D <50,8, 14Mpa 38,1≤D <50,8, 14Mpa 50,8≤D <76.2, 17MPa 50.8≤D88.9, 19MPa 76.2≤D<127, 24MPa 76.2≤D<127, 24MPa D≥127, 31Mpa D≥127, 31Mpa P = 220.6t / D ...

C C Si Si Mn Mn P P S S Cr Cr Ni Ni Mo Mo N N Cu Cu Ti Ti Nb Nb min max min max min max min max min max min max DIN 17456 1.4301 0.00 0.070 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.00 8.00 10.50 DIN 17456 1.4306 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 18.00 20.00 10.00 12.00 DIN 17456 1.4311 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.50 8.50 11.50 DIN 17456 1.4541 0.00 0.080 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.00 9.00 12.00 ...

C C Si Si Mn Mn P P S S Cr Cr Ni Ni Mo Mo N N Cu Cu Ti Ti Nb Nb min max min max min max min max min max min max min max J3459 SUS304TP 0.00 0.080 0.00 1.00 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20.00 8.00 11.00 J3459 SUS304HP 0.040 0.100 0.00 0.75 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20.00 8.00 11.00 J3459 SUS304LTP 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20.00 9.00 13.00 J3459 SUS310STP 0.00 0.080 0.00 1.50 0.00 2.00 0.00 0.040 0.00 0.030 24.00 26.00 19.00 22.00 ...

Spesifikasi Standar ASTM B111 untuk Tabung Kondensor Seamless Tembaga dan Paduan Tembaga-Paduan Tembaga dan Stok FerruleASTM A213 / A213M Spesifikasi Standar untuk Boiler Baja Paduan Feritik dan Austenitik Seamless, Superheater, dan Tabung Penukar PanasASTM A269 / A269M Spesifikasi Standar untuk Pipa Baja Tahan Karat Austenitik Seamless dan Dilas untuk Layanan UmumASTM A249 - A249 / A249M Spesifikasi untuk Boiler Baja Austenitik Dilas, Superheater, Penukar Panas, dan Tabung KondensorASTM A179 - A179 / A179M - Spesifikasi untuk Tabung Penukar Panas Baja Karbon Rendah yang Ditarik Dingin dan Tabung KondensorASTM A214 - A214 / A214M Spesifikasi untuk Penukar Panas Baja Karbon yang Dilas dengan Resistansi Listrik dan Tabung KondensorASTM A851 - Spesifikasi A851 untuk Induksi Induksi Frekuensi Tinggi, Tabung Kondensor Tabung Kondensor Baja Austenitik yang Tidak Dilas Tabung KondensorKeuntungan tabung Stainless Steel dalam KondensorASTM Standar untuk Penukar Panas dan Tabung KondensorSpesifikasi Tabung KondensorKerugian tabung baja tahan karat pada kondensorMengapa kondensor harus menggunakan tabung baja tahan karat?Kondensor Sistem Uap Besar

Pengujian Toleransi Ukuran Kelas EN / UNS 1.4749 / S44600 EN ISO 1127Metrik: Tidak terstandarisasi = NSI/ASME B 36.19 EN ISO 1127 ASTM A213/A 450 1.4959/N08811 / N08810 ANSI/ASME B 36.19 Selesai dingin: ASTM B 407 Selesai panas: ASTM A999 Selesai dingin: ASTM B 407 Selesai panas: ASTM B 407 1.4835 / S30815 / 253MA1.4854 / S35315 / 353MA ANSI / ASE B 36.19 ASTM A999 ASTM A312 / A 999

Baja tahan karat adalah paduan berbasis besi yang biasanya mengandung setidaknya 11,5% kromium. Unsur-unsur lain, Nikel yang paling penting, dapat ditambahkan dalam kombinasi dengan kromium untuk mendapatkan sifat-sifat khusus. Baja tahan karat sangat tahan terhadap serangan korosif dan oksidasi pada suhu tinggi. secara umum, ketahanan korosi dan ketahanan oksidasi meningkat secara progresif, meskipun tidak secara proporsional, dengan peningkatan kandungan kromium. Pipa dan tabung baja tahan karat digunakan karena berbagai alasan: untuk menahan korosi dan oksidasi, untuk menahan suhu tinggi, untuk kebersihan dan biaya perawatan yang rendah, dan untuk menjaga kemurnian bahan yang bersentuhan dengan baja tahan karat. Karakteristik yang melekat pada pipa baja tahan karat memungkinkan desain sistem perpipaan dinding tipis tanpa takut akan kegagalan dini akibat korosi. Penggunaan pengelasan fusi untuk menyambung perpipaan semacam itu menghilangkan kebutuhan akan penguliran. Baja tahan karat tipe 304 adalah analisis yang paling banyak digunakan untuk aplikasi pipa dan pipa tahan korosi umum, digunakan dalam ...

Standar EN: EN Standar Eropa untuk Baja Tahan Karat Eropa Ringkasan Kelas Standar EN Eropa Standar Toleransi Dimensi Eropa untuk Baja Tahan Karat EN 10090 Komposisi Kimia Baja Katup BS 970 Komposisi Kimia Baja Tahan Karat BS 3100 1991 Komposisi Kimia Baja Tuang BS 3100 Komposisi Kimia Baja Tahan Karat BS 1449-2 Komposisi Kimia Baja Tahan Karat BS Aerospace S100 Komposisi Kimia Sifat Mekanik Komposisi Kimia BS Aerospace S500 Sifat Mekanik EN 10204 Sertifikat Uji untuk Baja Tahan Karat EN 10302 Komposisi Kimia Baja Penahan Mulur EN 10302 Sifat Mekanik Baja Penahan Mulur Toleransi terhadap EN 10296-2 Tabung Baja Tahan Karat yang Dilas EN 10296-2 Komposisi Kimia Baja Tahan Karat EN 10296-2 Tabung Baja Tahan Karat yang Dilas Sifat Mekanik Komposisi Kimia Baja Tahan Karat hingga EN 10297-2 EN 10297-2 Sifat Mekanik Tabung Baja Tahan Karat Toleransi terhadap EN 10297-2 untuk Tabung Baja Tahan Karat yang Mulus EN 10269 Sifat Mekanik Temperatur Kamar Baja Tahan Karat EN 10269 Peningkatan ...

Standar ASTM: Standar ASTM untuk Pipa Baja Karbon Stainless Steel Standar ASTM BS DIN Swedia ASTM B265 Titanium Alloy Properties ASTM B265 Titanium Alloy Komposisi Kimia ASTM B265 Titanium Alloy ASTM A48 Spesifikasi Standar untuk Coran Besi Abu-abu Pipa Baja Standar ASTM A53 Pipa Baja ASTM A53 Hitam Dilapisi Seng Dilapisi Seng Pipa Baja ASME SA53 Pipa Baja ASME SA53 Pipa Baja Tekanan Kerja Maksimum - ASTM A53 B Pipa Baja Karbon ASTM A 53 & ASTM A 106. Pipa Hitam Dilas dan Mulus Pipa Mulus dari Baja Karbon yang Dimaksudkan untuk Pengoperasian dengan Suhu Tinggi ASTM A105 Standar untuk Perpipaan Baja Karbon Forgins ASTM A106 Pipa Baja Karbon Layanan Suhu Tinggi ASTM A106 / A106M - 08 Spesifikasi Standar untuk Pipa Baja Karbon Mulus untuk Layanan Suhu TinggiLayanan Suhu Tinggi ASTM A134 Standar untuk Pipa Baja Las Busur Fusi Listrik ASTM A134 Spesifikasi Pipa Baja Las Busur Fusi Listrik ASTM A135 Standar untuk Pipa Baja Las Busur Resistansi Listrik ASTM A139 Spesifikasi Pipa Baja Las Busur Fusi Listrik ASTM A139 Standar Pipa Baja Las Busur Fusi Listrik ASTM A148 ...

Guanyu Tube adalah produsen khusus ASTM A269 TP304, ASTM A269 TP304L, ASTM A269 TP316, ASTM A269 TP316L, ASTM A269 Tubing di Cina. Kondisi pengiriman dalam Anil Cerah atau Pengawetan Anil dan Pemolesan Permukaan Luar. ASTM A269 Tubing terutama mencakup ASTM A269 TP316 Tabung Instrumentasi Baja Tahan Karat, ASTM A269 TP316L Tabung Instrumen Baja Tahan Karat, Tabung Hidrolik Baja Tahan Karat. ASTM A269 dikeluarkan dengan sebutan tetap ASTM A269, angka yang mengikuti penunjukan menunjukkan tahun adopsi asli atau, dalam kasus revisi, tahun revisi terakhir. Angka dalam tanda kurung menunjukkan tahun persetujuan ulang terakhir. Superskrip epsilon menunjukkan perubahan editorial sejak revisi atau persetujuan ulang terakhir. Spesifikasi ini mencakup nilai ketebalan dinding nominal, pipa baja tahan karat untuk layanan tahan korosi umum dan suhu rendah atau tinggi, seperti yang ditetapkan dalam Tabel 1. Ukuran dan ketebalan pipa yang biasanya dilengkapi dengan spesifikasi ini adalah 1/4 inci (6,4 mm) dengan diameter dalam dan ...

ASTM A269 dan ASTM A249 keduanya dapat diterapkan untuk Tabung dan Pipa Baja Tahan Karat yang Dilas. Spesifikasi Standar ASTM A249 / A249M untuk Boiler Baja Austenitik Dilas, Superheater, Penukar Panas, dan Tabung Kondensor. ASTM A269 / A269M Spesifikasi Standar untuk Pipa Baja Tahan Karat Austenitik yang Dilas dan Dilas untuk Layanan Umum. ASTM A249 ASTM A269 Grafik Perbandingan ASTM A249 ASTM A269 Spesifikasi ASTM A249 dan ASTM A269 adalah dua standar untuk tabung baja tahan karat Austenitik, ada persyaratan yang sama dalam hal teknis, juga memiliki beberapa perbedaan. Spesifikasi ASTM A249 ASTM 269 Pembuatan Tabung Dilas Dilas Dan Aplikasi Seamless BoilerSuperheaterHeat-ExchangerKondensor Ukuran Layanan Umum OD: maksimum 304,8 mmTebal Dinding: 0,4 - 8,1 mm Diameter Dalam: min.4 mm Ketebalan Dinding: 0,51 mm ASTM / ASME ASTM A249 / A249MASME SA249 ASTM A269 / A269M Uji Flange Uji Flange Uji Flange A249 VS A269 Ruang Lingkup Aplikasi Tabung las ASTM A249 adalah untuk boiler, pemanas super, penukar panas, sistem...

ASTM A789 ASME SA 789 S31803 S32205 S32101 S32750 S32760 S32304 S31500 S31260 Produsen Tabung Seamless

ASTM A213 ASME SA213 TP304 TP304L TP309S TP310S TP316L TP316Ti TP321 TP317L TP347H Tabung Penukar Panas

Spesifikasi Tabung Baja Tahan Karat Daftar Isi: Spesifikasi Tabung Baja Tahan Karat ASTM: Produk Besi dan Baja Pipa Baja, Tabung Baja, Perlengkapan ASTM A1016 Spesifikasi Standar untuk Persyaratan Umum untuk Baja Paduan Feritik, Baja Paduan Austenitik, dan Tabung Baja Tahan Karat ASTM A999 Spesifikasi Standar untuk Persyaratan Umum untuk Pipa Baja Paduan dan Baja Tahan Karat A 213 / A 213M Ketel baja paduan feritik dan austenitik tanpa sambungan, pemanas super, dan tabung penukar panas SA 240 / SA 240M Spesifikasi Standar untuk Pelat Baja Tahan Karat Kromium dan Kromium-Nikel, Lembaran, dan Strip untuk Bejana Bertekanan dan untuk Aplikasi Umum SA 249 / SA 249M Spesifikasi Standar untuk Boiler Baja Austenitik yang Dilas, Superheater, Penukar Panas, dan Tabung Kondensor A 268 / A 268M Pipa baja tahan karat feritik dan martensitik yang dilas dan mulus untuk layanan umum A 269 / A 269M Pipa baja tahan karat austenitik yang dilas dan mulus untuk layanan umum A 270 / A 270M Pipa baja tahan karat yang dilas dan...

ASTM B163 N02200 N02201 N04400 N06600 N06601 N06690 N08800 N08810 N08811 N08825 N08020 N06025 Tabung Paduan Nikel Tekuk U

Standar untuk tabung & pipa baja tahan karat tanpa sambungan: Katagori Standar HidraulikInstrumentasiPenukar panasPipa ASME / ANSIISO & metrikTemperatur TinggiStandar Spesifikasi Tabung Penukar PanasASME - American Society of Mechanical EngineersASME Spesifikasi Stainless SteelSpesifikasi Pipa Stainless SteelSpesifikasi Pipa Stainless SteelDuplex Spesifikasi Pipa Stainless SteelStandar Spesifikasi | Singkatan Istilah Teknis | Daftar Istilah Stainless Steel | Perkapalan Masyarakat Dunia | Nomor Telepon Internasional | Nomor Negara Telepon Internasional | Standar Dunia Nama Lengkap | Daftar Istilah Logam Baja | Format Dokumen Standar | Daftar Istilah Logam dan Rekayasa | Standar Istilah Galvanisasi Hot Dip Galvanizing: ASTM A269 vs A312 Perbedaan Antara ASTM A269 dan A312 Perbedaan Antara ASTM A213 dan ASTM A269 Perbedaan Antara ASTM A213 dan ASTM A312 Spesifikasi Incoloy 825 UNS N08825 Tabung Seamless OCTG Casing Coupling NACE MR0175 dan MR0103 Standar Standar Pipa Baja Karbon ASTM BS DIN Swedia EN 10095 Sifat Mekanis Baja Tahan Karat EN 10088-3 Pengerasan Martensitik dan Pengerasan Presipitasi Mekanis EN 10088-3 Sifat Mekanis Baja Tahan Karat Feritik EN 10088-2 Sifat Mekanis Baja Tahan Karat Martensitik EN 10088-2 Sifat Mekanis Baja Tahan Karat Feritik ...