Many pepole are thinking: sometimes we call pipes, sometimes we call them tubes. Both of them are with the same shape. And we are confused what’s pipe and what’s tube . More often than not, people guess it has something to do with the quality of the materials, but that’s got nothing to do with it. The difference between a pipe and a tube is how they are measured, and ultimately what they are used for. A pipe is a vessel – a tube is structural. A pipe is measured ID (Inside Diameter) – a tube is measured OD (Outside Diameter). How they are measured… Pipes are measured ID (inside diameter) or OD( outside diameter). Tubes are measured OD ( outside diameter) because they are structural. Pipes have a consistent ID regardless of wall thickness. In other words, a 1/2″ high pressure pipe may need a 2″ thick wall, but…

DIN 17459 specifies technical delivery conditions for seamless circular tubes made from high temperature austenitic stainless steel as specified in table. 1. Such stainless steel tube are intended primarily to be used in high-pressure applications where elevated temperature and high mechanical stresses are involved (e.g. in the construction of pressure boilers, pressure vessels, pipelines, and in the chemical industry). Material Chemical composition (%) degignation number C Si Mn P S Ni Cr Mo Ni others X 6 CrNi 18 11 1.4948 0.04 to 0.08 ≤0.75 ≤2.0 0.035 0.015 17.0 to 19.0 – 10.0 to 12.0   X 3 CrNiN 18 11 1.4949 ≤0.04 ≤0.75 ≤2.0 0.035 0.015 0.10 to 0.18 17.0 to 19.0 0.50 to 0.60 9.5 to 11.5   X 8 CrNiTi 18 10 1.4941 0.04 to 0.10 ≤0.75 ≤2.0 0.035 0.015 17.0 to 18.5 – 9.5 to 11.5 Ti: ≥5 x %Cto ≤  0.80B: 0.0015 to 0.0050 X6CrNiMo 17 13 1.4919 0.04 to 0.08 ≤0.75 ≤2.0 0.035…

Stainless steel structure welding and cutting is inevitable applications in stainless steel. Because the characteristics of stainless steel itself has, in comparison with carbon steel welding and cutting of stainless steel has its own particularity, and more in its heat affected zone of welded joints (HAZ) produce a variety of defects. Special attention when welding stainless steel physical properties. For example austenitic stainless steel is a low coefficient of thermal expansion and high-chromium stainless steel is 1.5 times; thermal conductivity of low carbon steel is about 1 / 3, and the high thermal conductivity of chromium stainless steel of low carbon steel is about 1 / 2 ; specific resistance is 4 times more low-carbon steel, and high chromium stainless steel is low carbon steel 3 times. These conditions coupled with the metal density, surface tension, magnetic and other conditions have an impact on the welding conditions. Martensitic stainless steel generally represented 13% Cr steel. It is the welding, the heat…

The table shown is based on the reference data presented in EN 10088-1. Only a sample of the information available is shown. This is intended to show the scope of information available through representative figures for the most commonly used stainless steel tube types. A separate table indicates some of the grades that have been grouped together.Physical Properties Table Steel Types (AISI) Density Modulus Expansion Conductivity Specific Heat Resistivity . . 20C 400C . . . . Ferritic stainless steels 410S 7700 220 195 10.5 30 460 0.60 430 7700 220 195 10.0 25 460 0.70 444 7700 220 195 10.4 23 430 0.8 Martensitic and precipitation hardening stainless steels 410 7700 215 190 10.5 30 460 0.60 440 7700 215 190 10.4 15 430 0.8 630 7800 200 170 10.9 16 500 0.71 Austenitic stainless steel 304 7900 200 172 16.0 15 500 0.73 316 8000 200 172 16.0 15 500 0.75 ‘6%Mo’ 8000…

Stainless steel have good strength and good resistance to corrosion and oxidation at elevated temperatures. Stainless steel are used at temperatures up to 1700° F for 304 and 316 and up to 2000 F for the high temperature stainless grade 309(S) and up to 2100° F for 310(S). Stainless steel is used extensively in heat exchanger, super-heaters, boiler, feed water heaters, valves and main steam lines as well as aircraft and aerospace applications. Figure 1 gives a broad concept of the hot strength advantages of stainless steel in comparison to low carbon unalloyed steel. Table 1 shows the short term tensile strength and yield strength vs temperature. Table 2 shows the generally accepted temperatures for both intermittent and continuous service. With time and temperature, changes in metallurgical structure can be expected with any metal. In stainless steel, the changes can be softening, carbide precipitation, or embrittlement. Softening or loss of strength occurs in the 300 series (304, 316, etc.) stainless steel…

Shell and tube heat exchanger consist of a series of stainless steel tube. One set of these tubes contains the fluid that must be either heated or cooled. The second fluid runs over the tubes that are being heated or cooled so that it can either provide the heat or absorb the heat required. A set of tubes is called the tube bundle and can be made up of several types of tubes: plain, longitudinally finned, etc. Shell and Tube heat exchangers are typically used for high pressure applications (with pressures greater than 30 bar and temperatures greater than 260°C. This is because the shell and tube heat exchangers are robust due to their shape. There are several thermal design features that are to be taken into account when designing the tubes in the shell and tube heat exchanger. These include: Tube diameter: Using a small tube diameter makes the heat exchanger both…

Standards | Stainless Steel Glossary | World Society Shipping | International Phone Country Number | World Standards Full Name | World Clock | Steel Metal Glossary | Standard Documents Format | Metals and Engineering Terms Glossary | Hot Dip Galvanizing Glossary Useful Tools Corrosion Temperature Surface Pressure Specification Hardness Properties Sizes Fabrication Selection of Stainless Steel Heat Heat Exchanger Heat Treatment Heat Transfer Aluminium Brass Copper Steel Grades Tool Steel Nickel Alloy Incoloy Grades Inconel Grades Monel Grades Hastelloy Grades

ASTM A595 Standard Specification for Steel Tubes, Low-Carbon or High-Strength Low-Alloy, Tapered for Structural Use covers three grades of seam-welded, round, tapered steel tubes for structural use. Grades A and B are of low-carbon steel or high-strength low-alloy steel composition and Grade C is of weather-resistance steel composition. The tube steel shall be hot-rolled aluminum-semikilled or fine-grained killed sheet or plate manufactured by one or more of the following processes: open-hearth, basic-oxygen, or electric-furnace. The tubes shall be made from trapezoidal sheet or plate that is preformed and then seam welded. They shall be brought to final size and properties by roll compressing cold on a hardened mandrel. A tensile test shall be done to determine the yield strength and the ultimate tensile strength of the tubes. 1.1 This specification covers three grades of seam-welded, round, tapered steel tubes for structural use. Grades A and B are of low-carbon steel or high-strength low-alloy steel composition and Grade C…

Foshan scrap stainless steel market price (yuan/ton) Change Broken stainless steel pipe (Ni7.4-7.6%) 11150-11350 -100 Stainless steel back Burden (Ni7.0-7.2%) 10150-10350 -100 304 Edge of domestic materials (Ni7.6-7.8%) 11500-11700 -100 316 Back to the Burden (Ni12%) 17100-17300 -100 201 Back to the Burden (Ni5%) 5350-5550 -50 430 Back to the Burden (Cr18%) 4100-4300 0 Shanghai Huadong Stainless steel tube scrap market price (yuan / ton) 　 304 Edge of domestic materials (Ni7.6-7.8%) 11850-12050 -100 316 Back to the Burden (Ni12%) 17300-17500 -100 USD1=RMB 7.31yuan Pipes Tubes Plates Bars Square Tubes Weight Calculation CalculatorConversion Calculator Calculation-Pressure|Weight|Temperature|Volume|LengthPipe Working Pressure CalculationMetals Weight Calculator Calculation Nomura Lowers 2010 Copper Price Forecast, Raises Gold, Nickel, Palladium Nickel base alloy | Special alloy steel Nickel futures up on spot demand, overseas trend November 3 Jinchuan cut the ex-factory price of Nickel BSEN ASTM British and American standards for tolerances, surface finish and testing of stainless steels Selection of…

Internal Pressure Calculation Results: ASME Code, Section VIII, Division 1, 2004 A-06 Elliptical Head From 10 To 20 SA-240 304 at 400 C Thickness Due to Internal Pressure [Tr]:= (P*(D+2*CA)*K)/(2*S*E-0.2*P) Appendix 1-4(c)= (35000.000*(58.0000+2*0.0000)*1.00)/(2*106.79*1.00-0.2*35000.000)= 9.8271 + 0.0000 = 9.8271 mm. Max. All. Working Pressure at Given Thickness [MAWP]:= (2*S*E*(T-Ca))/(K*(D+2*Ca)+0.2*(T-Ca)) per Appendix 1-4 (c)= (2*106.79*1.00*(12.0000))/(1.00*(58.0000+2*0.0000)+0.2*(12.0000))= 42431.543 KPa. Maximum Allowable Pressure, New and Cold [MAPNC]:= (2*Sa*E*T)/(K*D+0.2*T) per Appendix 1-4 (c)= (2*137.90*1.00*12.0000)/(1.00*58.0000+0.2*12.0000)= 54791.520 KPa. Actual stress at given pressure and thickness [Sact]: = (P*(K*(D+2*CA)+0.2*(T-CA)))/(2*E*(T-CA))= (35000.000*(1.00*(58.0000+2*0.0000)+0.2*(12.0000)))/(2*1.00*(12.0000))= 88.088 N./mm? Required Thickness of Straight Flange = 11.832 mm. Percent Elongation per UHA-44  (75*tnom/Rf)*(1-Rf/Ro)  75.630 % Cylindrical Shell From 20 To 30 SA-240 304 at 400 C Thickness Due to Internal Pressure [Tr]:= (P*(D/2+Ca))/(S*E-0.6*P) per UG-27 (c)(1)= (35000.000*(58.0000/2+0.0000))/(106.79*1.00-0.6*35000.000)= 11.8318 + 0.0000 = 11.8318 mm. Max. All. Working Pressure at Given Thickness [MAWP]:= (S*E*(T-Ca))/((D/2+Ca)+0.6*(T-Ca)) per UG-27 (c)(1)= (106.79*1.00*(12.0000))/((58.0000/2+0.0000)+0.6*12.0000)= 35398.691 KPa. Maximum Allowable Pressure, New and Cold [MAPNC]:= (SA*E*T)/(D/2+0.6*T) per UG-27 (c)(1)= (137.90*1.00*12.0000)/(58.0000/2+0.6*12.0000)= 45710.055 KPa. Actual stress at given pressure and…

ASTM A790 mencakup pipa baja tahan karat dupleks feritik / austenitik yang dilas tanpa sambungan dan jahitan lurus untuk layanan korosif umum, dengan penekanan khusus pada ketahanan terhadap retak korosi tegangan. Pipa harus dibuat dengan proses pengelasan tanpa sambungan atau otomatis, tanpa penambahan logam pengisi dalam operasi pengelasan. Analisis panas harus dilakukan untuk menentukan persentase elemen yang ditentukan. Uji tegangan, uji pengerasan, uji perataan, uji hidrostatik dan uji listrik tidak rusak harus dilakukan untuk memenuhi persyaratan yang ditentukan. Abstrak ini adalah ringkasan singkat dari standar yang direferensikan. Ini hanya bersifat informasi dan bukan bagian resmi dari standar; teks lengkap dari standar itu sendiri harus dirujuk untuk penggunaan dan penerapannya. Spesifikasi ini mencakup pipa baja tahan karat feritik / austenitik yang dilas tanpa sambungan dan jahitan lurus yang dimaksudkan untuk layanan korosif umum, dengan penekanan khusus pada ketahanan terhadap retak korosi tegangan. Baja ini rentan terhadap penggetasan jika digunakan dalam waktu lama pada suhu tinggi. Persyaratan tambahan opsional...

DSTU B A.3.2-12:2009 SSBP. Sistem ventilasi. Kaliper DSTU GOST 166:2009 (ISO 3599-76). Spesifikasi teknis (GOST 166-89 (ISO 3599-76), IDT) DSTU EN 473:2012 Kontrol non-invasif. Kualifikasi dan sertifikasi personel. Ketentuan umum (EN 473: 2008, IDT) DSTU 2680-94 Pipa canai mulus yang terbuat dari baja dan paduan. Terminologi dan identifikasi cacat permukaan DSTU 2841-94 (GOST 27809-95) Baja Chavun i. Metode analisis spektrografi DSTU 3124-95 Pipa yang terbuat dari baja dan paduan. Pengikatan dan persiapan sampel untuk gudang bahan kimia. Ketentuan dasar DSTU 4179-2003 Kaset bergetar logam. Keterampilan teknis (GOST 7502-98, MOD) DSTU GOST 6507: 2009 Mikrometer. Spesifikasi DSTU 7238: 2011 Sistem standar keselamatan. Buat zakhist kolektif untuk orang-orang yang bekerja. Klasifikasi Zagalni vimogi ta klasifikasi DSTU 7239:2011 Sistem standar keselamatan. Tetapkan zakhist individu. Klasifikasi Zagalni vimogi ta klasifikasi DSTU ISO 7438: 2005 Bahan logam. Pengujian untuk zgin (ISO 7438: 1985, IDT) DSTU ISO 8496-2002 Bahan logam. Terompet. Pengujian untuk menarik cincin dengan dua batang paralel (ISO 8496: 1988, IDT) DSTU GOST 12344: 2005 Baja paduan dan paduan tinggi. Metode untuk mendesain vugletsiu (GOST 12344-2003, ...

Inspeksi permukaan luar pipa dilakukan secara visual tanpa menggunakan alat pembesar. Permukaan dalam pipa dengan diameter dalam 70 mm atau lebih diperiksa dengan menggunakan periskop atau sistem video. Diperbolehkan untuk memeriksa permukaan bagian dalam pipa tanpa menggunakan instrumen, dengan menggunakan alat penerangan di kedua ujung pipa terhadap cahaya. Untuk pipa dengan diameter internal kurang dari 70 mm, serta pipa dengan diameter internal 70 mm atau lebih yang belum diperiksa dengan periskop, pabrikan menjamin bahwa permukaan internal pipa memenuhi persyaratan spesifikasi ini berdasarkan hasil yang memuaskan dari inspeksi ultrasonik 100%. Klasifikasi cacat dilakukan sesuai dengan DSTU 2680 (OST 14-82 [18]). Kedalaman cacat diperiksa setelah pengarsipan dan pengukuran selanjutnya. Dinding

Apa itu MW dan Apa itu AW? MW adalah ketebalan dinding minimum (min). Toleransi Ketebalan Dinding dalam (-0, +20%) untuk OD 1-1/2" [38.1mm] dan di bawahnya, dalam (-0, +22%) untuk OD di atas 1-1/2" [38.1mm]. AW adalah Ketebalan Dinding Rata-rata (rata-rata). Toleransi Ketebalan Dinding dalam (-10%, +10%) untuk OD 1-1/2 ″ [38,1mm] dan di bawahnya, dalam (-11%, +11%) untuk OD lebih dari 1-1/2 ″ [38,1mm]. Menurut ASME SA213 Variasi yang Diizinkan dari Ketebalan Dinding yang Ditentukan: 13.1 Variasi yang diizinkan dari ketebalan dinding minimum yang ditentukan harus sesuai dengan Spesifikasi A1016 / A1016M.13.2 Variasi yang diizinkan dari ketebalan dinding rata-rata yang ditentukan harus +/- 10 % dari ketebalan dinding rata-rata yang ditentukan untuk tabung yang dibentuk dingin dan, kecuali jika ditentukan lain oleh pembeli.

Baja tahan karat TP321 TP321H pada dasarnya terbuat dari baja tahan karat 304. Mereka berbeda dengan tambahan Titanium yang sangat kecil. Perbedaan nyata adalah kandungan karbonnya. Semakin tinggi kandungan karbon semakin besar kekuatan luluhnya. Baja tahan karat 321 memiliki keunggulan dalam lingkungan bersuhu tinggi karena sifat mekaniknya yang sangat baik. Dibandingkan dengan paduan 304, baja tahan karat 321 memiliki keuletan dan ketahanan yang lebih baik terhadap fraktur tegangan. Selain itu, 304L juga dapat digunakan untuk anti-sensitisasi dan korosi antar butir. Grade TP304L lebih mudah tersedia di sebagian besar bentuk produk, dan umumnya digunakan sebagai preferensi untuk 321 jika persyaratannya hanya untuk ketahanan terhadap korosi intergranular setelah pengelasan. Namun Tabung Baja Tahan Karat 304L memiliki kekuatan panas yang lebih rendah daripada tabung baja tahan karat 321 sehingga bukan pilihan terbaik jika persyaratannya adalah ketahanan terhadap lingkungan operasi di atas sekitar 500 ° C. Namun, 321 adalah yang jauh lebih baik ...

Apa faktor utama yang mempengaruhi harga tabung baja tahan karat? Kami menganalisis dari proses produksi, persyaratan inspeksi, bahan baku, dan faktor lainnya. 1. Proses produksi. Karena biaya produksi anil cerah yang lebih tinggi, harga tabung anil cerah akan lebih tinggi daripada harga tabung anil pengawetan. Karena kecepatan perlakuan panas dari tungku anil cerah lambat, jumlah tabung baja tahan karat yang melewatinya setiap kali lebih kecil, dan listrik tambahan serta amonia akan dikonsumsi. Karena ada lebih banyak lintasan produksi untuk tabung baja berdiameter kecil, maka harga tabung baja tahan karat berdiameter kecil akan lebih tinggi dari pada pipa baja tahan karat berdiameter besar. Selain itu, pemolesan tabung baja tahan karat dan tabung tikungan U juga akan menimbulkan biaya tambahan. 2. Persyaratan inspeksi Menurut persyaratan ASME SA213, Setiap tabung harus menjalani uji listrik tidak rusak atau uji hidrostatis. Ini...

Komponen utama baja tahan karat 904L: 20Cr-24Ni-4.3Mo-1.5Cu Grade - C Mn Si P S Cr Mo Ni Cu N ASTM A213N08904 904L min. maks. - 0,020 - 2,00 - 1,00 - 0,040 - 0,030 19,0 23,0 4,0 5,0 23,028,0 1,02,0 -0,10 EN 10216-5 1,4539 min. maks. - 0,020 - 2,00 - 0,70 - 0,030 - 0,010 19,0 21,0 4,0 5,0 24,026,0 1,22,0 -0,15 Baja tahan karat 904L N08904 adalah baja tahan karat austenitik paduan rendah karbon dan paduan tinggi yang dirancang untuk lingkungan dengan kondisi korosi yang keras. Ini memiliki ketahanan korosi yang lebih baik daripada 316L dan 317L, dan pada saat yang sama, ini memperhitungkan harga dan kinerja, dan sangat hemat biaya. Karena penambahan tembaga 1.5%, ia memiliki ketahanan korosi yang sangat baik untuk mengurangi asam seperti asam sulfat dan asam fosfat. Baja tahan karat super austenitik 904L juga memiliki ketahanan korosi yang sangat baik terhadap korosi tegangan, korosi sumuran dan korosi celah yang disebabkan oleh klorida ...

Menurut Jadwal Tarif Harmonisasi Amerika Serikat, (HTSUS), Bab 73. Kode HS Deskripsi Tarif 7304 4130 Tabung dan Pipa Baja Tahan Karat yang Ditarik Dingin, Profil Berongga, SeamlessOD kurang dari 19mm. 36% 7304 4160 OD lebih besar dari 19mm 36% 7304 4900 Batang Berongga Baja Tahan Karat 36%

Di bidang baja tahan karat, biasanya 304 disebut TP304, 304L disebut 304L, 316L disebut TP316L. Sebagai contoh: ASTM A312 TP304, ASME SA213 TP304L, ASME SA213 TP316L. Jadi, apa arti "TP"? TP adalah singkatan dari Tipe. Alasannya adalah AISI (Institut Besi dan Baja Amerika) mengklasifikasikan Baja Tahan Karat dalam Tipe. Untuk alasan yang sama, terkadang 304, 304, L316L, akan disebut AISI 304, AISI 304L, AISI 316L.

OD: 17.15 - 508mm (3/8 INCH hingga 20 INCH) WT: 0,5 - 60 mm, Jadwal 10-an, 20, 40-an, 40, 60, 80-an, 80, 100, 120, 140, 160, XXH.Kapasitas Produksi: 500 MT / Bulan Guanyu Tube adalah produsen khusus ASTM A312 TP304, ASTM A312 TP304L, ASTM A312 TP316, ASTM A312 TP316L, ASTM A312 TP321, ASTM A312 TP310S, ASTM A312 TP304 TP304L TP304H TP316 TP316L TP317L TP321 TP316Ti TP347 TP347H TP310S TP309S Pemasok Pipa Baja Tahan Karat. Ini dikeluarkan di bawah penunjukan tetap ASTM A312; angka yang segera mengikuti penunjukan menunjukkan tahun adopsi asli atau, dalam kasus revisi, tahun revisi terakhir. Angka dalam tanda kurung menunjukkan tahun persetujuan ulang terakhir. Tanda superskrip epsilon menunjukkan perubahan editorial sejak revisi atau persetujuan ulang terakhir. Ini mencakup pipa baja tahan karat austenitik tanpa sambungan, jahitan lurus, dan dilas dengan pengerjaan dingin untuk suhu tinggi dan layanan korosif umum. Ketika kriteria uji dampak untuk layanan suhu rendah akan ...

Menurut ASME B36.10 dan ASME B 36.19. Hasil bobot berdasarkan Hitung "Bobot = 0,02507 × T (D - T)". ASTM A312 TP316L Schdule | ASTM A312 TP316L Weight | ASTM A312 TP316 Size NPS DN ODinch ODmm SCH5Smm SCH10Smm SCH10mm SCH20mm SCH30mm STDmm SCH40Smm SCH40mm SCH60mm XSmm SCH80Smm SCH80mm SCH80mm SCH100mm SCH120mm SCH140mm SCH160mm XXSmm 1/8 6 0.405 10.3 1.24 1.24 1.45 1.73 1.73 1.73 2.41 2.41 2.41 kg/m 0.282 0.282 0.322 0.372 0.372 0.372 0.372 0.477 0.477 0.477 1/4 8 0.540 13.7 1.65 1.65 1.85 2.24 2.24 2.24 3.02 3.02 3.02 kgs/m 0.498 0.498 0.498 0.550 0.644 0.644 0.644 0.644 0.809 0.809 0.809 3/8 10 0.675 17.1 1.65 1.65 ...

Menurut ASME B36.10 dan ASME B 36.19. Hasil berat berdasarkan Hitung "Berat = 0,02491 × T (D - T)". ASTM A312 TP304 Schdule | ASTM A312 TP304 Berat | ASTM A312 TP304 Ukuran. ASTM A312 TP304 TP304L TP304H TP321 TP321H Ukuran dan Berat Pipa Baja Tahan Karat NPS DN ODinch ODmm SCH5Smm SCH10Smm SCH10mm SCH20mm SCH30mm STDmm SCH40Smm SCH40mm SCH60mm XSmm SCH80Smm SCH80mm SCH80mm SCH100mm SCH120mm SCH140mm SCH160mm XXSmm 1/8 6 0.405 10.3 1.24 1.24 1.45 1.73 1.73 1.73 1.73 2.41 2.41 2.41 kg/m 0.280 0.280 0.320 0.369 0.369 0.369 0.369 0.369 0.474 0.474 0.474 1/4 8 0.540 13.7 1.65 1.65 1.85 2.24 2.24 2.24 2.24 3.02 3.02 3.02 kg/m 0.495 0.495 0.546 0.639 0.639 0.639 0.803 0.803...

Peringkat Tekanan Kerja Tabung ASTM A213 Peringkat Tekanan Kerja OD inci Ave. Dinding inci Kekuatan Luluh Min (PSI) Kekuatan Tarik Min (PSI) Tekanan Ledakan Teoritis * (PSI) Tekanan Kerja (PSI) 25% dari Titik Leleh Teoritis Ledakan ** (PSI) Tekanan Runtuh *** (PSI) 0.250 0.020 30.000 75.000 14.286 3.571 5.714 4.416 0.250 0.020 30.000 75.000 14.286 3.571 5.714 4.416 0.250 0.020 30.000 75.000 14.286 3.571 5.714 4.416250 0.028 30,000 75,000 21,649 5,412 8,660 5,967 0.250 0.035 30,000 75,000 29,167 7,292 11,667 7,224 0.250 0.049 30,000 75,000 48,355 12,089 19,342 9,455 0.250 0.065 30,000 75,000 81,250 20,313 32,500 11,544 0.375 0.020 30,000 75,000 8,955 2,239 3,582 3,029 0.375 0.028 30,000 75,000 13,166 3,292 5,266 4,145 0.375 0.035 30,000 75,000 17,213 4,303 6,885 5,077 0.375 0.049 30,000 75,000 26,534 6,634 10,614 6,816 0.375 0.065 30,000 75,000 39,796 9,949 15,918 8,597 0.500 0.020 30,000 75,000 6,522 1,630 2,609 2,201 0.500 0.028 30,000 75,000 9,459 2,365 3,784 3,172 0.500 0.035 30,000 75,000 12,209 3,052 4,884 3,906 0.500 0.049 30,000 75,000 18,284 4,571 7,313...

Banyak aplikasi farmasi dan bioteknologi yang mengharuskan permukaan kontak produk dipoles dengan listrik. Oleh karena itu, kemampuan untuk memberikan permukaan yang dipoles listrik berkualitas tinggi adalah properti material yang penting. Baja tahan karat dupleks 2205 dapat dipoles dengan listrik hingga hasil akhir 0,38 mikron atau lebih baik, hasil akhir yang memenuhi atau melampaui persyaratan permukaan akhir standar ASME BPE untuk permukaan yang dipoles listrik. Meskipun baja tahan karat dupleks 2205 dapat dengan mudah memenuhi persyaratan permukaan akhir industri farmasi dan bioteknologi, permukaan baja tahan karat 2205 yang dipoles dengan listrik tidak secerah permukaan baja tahan karat 316L yang dipoles dengan listrik. Perbedaan ini disebabkan oleh laju pelarutan logam yang sedikit lebih tinggi dari fase ferit dibandingkan dengan fase austenit selama pemolesan listrik. Permukaan | Tabung Pemoles | Tinjauan Kekasaran Tabung | Tabung Anil Cerah | Standar Kekasaran China USA | EDM | Pembanding Kekasaran EDM | Pembersihan Pasca Pengelasan | Pembersihan Tabung | Metode Pembersihan | Bagan Konversi Kekasaran | Jenis Permukaan Akhir Tabung | Perawatan Perawatan Baja Tahan Karat | Standar Inggris-Amerika untuk Toleransi Pengujian Permukaan Akhir | Catatan Permukaan Akhir | Parameter Tekstur Permukaan | Mengukur Permukaan Akhir | Permukaan Akhir ...

Karakteristik Pemesinan Baja Tahan Karat 2205 Pemesinan baja tahan karat dupleks 2205 mirip dengan 316L, tetapi masih ada beberapa perbedaan. Operasi pembentukan dingin harus mempertimbangkan kekuatan yang lebih tinggi dan sifat pengerasan kerja yang lebih tinggi dari baja tahan karat dupleks. Peralatan pembentuk mungkin memerlukan kapasitas beban yang lebih tinggi, dan dalam operasi pembentukan, baja tahan karat 2205 akan menunjukkan ketahanan yang lebih tinggi daripada baja tahan karat austenitik standar. Kekuatan yang lebih tinggi dari baja tahan karat dupleks 2205 membuatnya lebih sulit untuk dikerjakan daripada 316L. Pengelasan baja tahan karat dupleks 2205 dapat menggunakan metode pengelasan baja tahan karat 316L. Namun, masukan panas dan suhu interpass harus dikontrol dengan ketat untuk mempertahankan rasio fase austenit-ferit yang diinginkan dan menghindari pengendapan fase intermetalik yang merugikan. Sejumlah kecil nitrogen dalam gas las membantu menghindari masalah ini. Saat melakukan kualifikasi prosedur pengelasan untuk baja tahan karat dupleks, metode yang umum digunakan adalah...

Komposisi Kimia ASTM A213 / ASME SA 213 317 317L 317LM 317LMN Baja Tahan Karat Kelas C Mn P Sulfur Si Cr Nikel Mo N Cu Berat % 317 S31700 18.00 11.00 3.00 Min. 0.08 2.00 0.045 0.030 1.00 20.00 15.00 4.00 Maks. 317L S31703 18,00 11,00 3,00 Min. 0,035 2,00 0,045 0,030 1,00 20,00 15,00 4,00 Maks. 317LM S31725 18.00 13.50 4.00 Min. 0,03 2,00 0,045 0,030 1,00 20,00 17,50 5,00 0,20 0,75 Maks. 317LMN S31726 17,00 13,50 4,00 0,10 Min. 0.03 2.00 0.045 0.030 1.00 20.00 17.50 5.00 0.20 0.75 Maks. EN 10216-5 1,4439 16,50 12,50 4,00 Min. 0,030 2,00 0,040 0,015 1,00 18,50 14,50 5,00 Maks. EN 10217-7 1,4438 17,50 13,00 3,00 Min. 0,030 2,00 0,045 0,030 1,00 19,50 16,00 4,00 Maks. Sifat Mekanis dari Tabung Baja Tahan Karat 317 317L Tabung Tarik ...

ASTM A213 347/347H / 347HFG Tabung Baja Tahan Karat Komposisi Kimia Kelas 347 347H 347HFG Penunjukan UNS S34700 S34709 S34710 Karbon (C) Maks. 0,08 0,04-0,10 0,06-0,10 Mangan (Mn) Maks. 2.00 2.00 2.00 Fosfor (P) Maks. 0.04 0.04 0.04 Belerang (S) Maks. 0.03 0.03 0.03 Silikon (Si) Maks. 0.75 0.75 0.75 Kromium (Cr) 17.0-20.0 17.0-20.0 17.0-20.0 Nikel (Ni) 9.0-13.0 9.0-13.0 9.0-13.0 Molibdenum (Mo) - - Nitrogen (N) - - - Besi (Fe) Bal. Bal. Bal. Unsur-unsur lain Cb + Ta = 10xC-1.0 Cb + Ta = 8xC-1.0 Nb + Ta = 8xC-1.0 347 347H 347HFG Baja Tahan Karat Sifat Mekanis Kekuatan Tarik Kekuatan Tarik Kekuatan Luluh Kekuatan Luluh Kekuatan Luluh Paduan UNS Spesifikasi MPa ksi MPa ksi Perpanjangan dalam 2 inci (min.) % HarndessHBW 347 S34700 ASTMA213 515 75 205 30 35 192 347H S34709 ASME SA 213 515 75 205 30 35 192 347HFG S34710 - 550 80 205 30 35 192 347 347H 347HFG Sifat Fisik Baja Tahan Karat Paduan UNSDesign Densitas kgs/dm³ Modulus Elastisitas (x106 psi) Rata-rata ...

ASME SA213 TP310S TP310H Komposisi Kimia Kelas UNS Penunjukan C Mn P S Si Cr Ni S31002 0,02 maks 2,0 maks 0,020 maks 0,015 maks 0,15 maks 24,0 - 26,0 19,0 - 22,0 310S S31008 0,08 maks 2,0 maks 0.045 maks 0.030 maks 1.00 maks 24.0 - 26.0 19.0 - 22.0 310H S31009 0.04-0.10 2.0 maks 0.045 maks 0.030 maks 1.00 maks 24.0 - 26.0 19.0 - 22.0 Sifat Mekanik Baja Tahan Karat TP310S TP310H 1. Sifat Mekanik Pipa Baja Tahan Karat 310S pada Suhu Kamar TP310H TP310H TP310S TP310S Tipikal Minimum Tipikal Minimum Kekuatan Tarik Minimum, MPa 645 515 595 515 Tegangan Luluh (0,2 % offset), MPa 355 205 295 205 Perpanjangan (Persen dalam 50mm) 52 35 35 35 35 Kekerasan (Rockwell) - 90 HRB Maks - 90 HRB Maks Sifat Fisik Baja Tahan Karat 310S Paduan UNS Spek. Berat Jenis Massa Jenis g / cm³ Modulus Elastisitas (x106 psi) Koefisien Rata-rata ...

ASME SA 213 TP 316 / TP 316L EN 10216-5 1.4401 1.4404 Komposisi Kimia Kelas TP316 TP 316L 1.4401 1.4404 Peruntukan UNS S31600 S31603 Karbon (C) Maks. 0,08 0,035 0,07 0,030 Mangan (Mn) Maks. 2.00 2.00 2.00 2.00 Fosfor (P) Maks. 0.045 0.045 0.040 0.040 Belerang (S) Maks. 0.030 0.030 0.015 0.015 Silikon (Si) Maks. 1.00 1.00 1.00 1.00 1.00 Kromium (Cr) 16.0 - 18.0 16.0 - 18.0 16.5 - 18.5 16.5 - 18.5 Nikel (Ni) 10.0 - 14.0 10.0 - 14.0 10.0 - 13.0 10.0 - 13.0 Molibdenum (Mo) 2.0 - 3.0 2.0 - 3.0 2.0 - 2.5 2.0 - 2.5 Nitrogen (N) Maks. - 0,015 0,015 Sisa Besi (Fe) Sisa Sisa Sisa Sisa Sisa Unsur Lain - - - - * Kandungan karbon maksimum 0,04% dapat diterima untuk tabung yang ditarik Sifat Umum 316 316L Tabung Baja Tahan Karat Tautan Terkait 316L Komposisi Kimia 316L Ketahanan terhadap Korosi 316L Sifat Fisik 316L Sifat Mekanik 316L Oksidasi ...

Komposisi Kimiawi ASME SA213 304 304L 304H dan EN 10216-5 1.4301 1.4307 1.4948 Grade - C Mn Si P S Cr Mo Ni N 304 / S30400 min.maks. -0,08 -2,0 -1,00 -0,045 -0,030 18,0-20,0 - 8,0-11,0 - EN 10216-5 1,4301 min.maks. -0,07 -2,0 -1,00 -0,040 -0,015 17,00-19,5 - 8,0-10,5 -0,11 304L / S30403 min.maks. -0,035 -2,0 -1,00 -0,045 -0,030 18,0-20,0 - 8,0-12,0 - EN 10216-5 1,4307 min.maks. -0,030 -2,0 -1,00 -0,040 -0,015 17,5-19,5 - 8,0-10,0 -0,11 304H / S30409 min.maks. 0,04-0,10 -2,0 -1,00 -0,045 -0,030 18,0-20,0 - 8,0-11,0 - EN 10216-5 1,4948 min.maks. 0,04-0,08 -2,0 -1,00 -0,035 -0,015 17,0-19,0 - 8,0-11,0 -0,11 Sifat Umum TP304L Komposisi Kimia TP304L Ketahanan terhadap Korosi TP304L Sifat Fisik TP304L Sifat Mekanik TP304L Pengelasan TP304L Perlakuan Panas TP304L Pembersihan Pipa dan Pipa304/304LN / 304H

Kami adalah produsen khusus ASME SA249 ASTM A249 TP304, ASTM A249 TP304L, ASTM A249 TP304H, ASTM A249 TP316, ASTM A249 TP316L, ASTM A249 TP316H, ASTM A249 TP316Ti, ASTM A249 TP321 TP321H, ASTM A249 TP309H TP309S, ASTM A249 TP310S TP 310H, ASTM A249 TP347 Tabung Dilas dan Pipa Dilas ASTM A249. Apa itu ASTM A249 ASME SA249? ASTM A249 menetapkan spesifikasi standar untuk tabung las dengan ketebalan dinding nomina dan tabung las yang dikerjakan dengan sangat dingin yang terbuat dari baja austenitik dengan berbagai tingkatan yang ditujukan untuk penggunaan seperti boiler, superheater, penukar panas, atau tabung kondensor. Analisis panas dan produk harus sesuai dengan persyaratan komposisi kimia untuk karbon, mangan, fosfor, belerang, silikon, kromium, nikel, molibdenum, nitrogen, tembaga, dan lainnya. Semua bahan harus dilengkapi dengan kondisi perlakuan panas sesuai dengan suhu larutan dan metode pendinginan yang diperlukan. ASTM A249 Benda Uji Tubing Ketika perlakuan panas akhir dalam tungku kontinu, jumlah ...

ASME SA 213 TP321 321H vs EN 10216-5 1.4541 Komposisi Kimia Kelas 321 321H EN 10216-5 1.4541 Penunjukan UNS S32100 S32109 Karbon (C) Maks. 0.08 0.04-0.10 0.08 Mangan (Mn) Maks. 2.00 2.00 2.00 2.00 Fosfor (P) Maks. 0,045 0,045 0,040 Belerang (S) Maks. 0,03 0,03 0,015 Silikon (Si) Maks. 1.00 1.00 1.00 Kromium (Cr) 17.0-20.0 17.0-20.0 17.0-19.0 Nikel (Ni) 9.0-12.0 9.0-12.0 9.0-12.0 Molibdenum (Mo) - - Nitrogen (N) - - Besi (Fe) Bal. Bal. Bal. Unsur-unsur lain Ti = 5 (C + N) hingga 0,70% Ti = 4 (C + N) hingga 0,70% Ti = 5 (C + N) hingga 0,70% Sifat UmumKomposisi KimiaKetahanan terhadap KorosiSifat FisikSifat MekanikPerlakuan PanasPembuatanTahan Oksidasi Suhu TinggiPerilaku Oksidasi Tabung Baja Tahan Karat Tipe 321321 S32100 Tabel Perbandingan Komposisi Kimia Perbedaan antara Baja Tahan Karat 321 dan 347

ASTM A213 321 321H 347 347H Komposisi Kimia Kelas 321 321H 347 347H Penunjukan UNS S32100 S32109 S34700 S34709 Karbon (C) Maks. 0.08 0.04-0.10 0.08 0.04-0.10 Mangan (Mn) Maks. 2.00 2.00 2.00 2.00 2.00 Fosfor (P) Maks. 0.045 0.045 0.04 0.04 Belerang (S) Maks. 0,03 0,03 0,03 0,03 Silikon (Si) Maks. 1.00 1.00 0.75 0.74 Kromium (Cr) 17.0-20.0 17.0-20.0 17.0-20.0 17.0-20.0 Nikel (Ni) 9.0-12.0 9.0-12.0 9.0-13.0 9.0-13.0 Molibdenum (Mo) - - - - Nitrogen (N) - - - - Besi (Fe) Bal. Bal. Bal. Bal. Unsur-unsur lain Ti = 5 (C+N) hingga 0,70% Ti = 4 (C+N) hingga 0,70% Cb + Ta = 10xC-1.0 Cb + Ta = 10xC-1.0 Keterbatasan pada 321 adalah titanium tidak dapat berpindah dengan baik pada busur temperatur tinggi, sehingga tidak direkomendasikan sebagai bahan habis pakai pengelasan. Dalam hal ini, grade 347 lebih disukai - niobium melakukan tugas stabilisasi karbida yang sama tetapi dapat ditransfer melintasi busur pengelasan. Oleh karena itu, grade 347 adalah bahan habis pakai standar untuk pengelasan 321. Kelas...

Pelapisan nikel tanpa listrik pada bagian baja tahan karat (poros penggerak, bagian penyambung, bagian yang bergerak, dll.) Dapat meningkatkan keseragaman dan pelumasan sendiri pada pelapisan, yang lebih baik daripada pelapisan kromium. Namun, pelapisan nikel tanpa listrik pada baja tahan karat sering kali menghasilkan ikatan yang tidak memuaskan antara lapisan pelapisan dan substrat karena perlakuan awal yang buruk, yang telah menjadi masalah mendesak dalam produksi aktual. Proses aslinya: pemolesan mekanis → penghilang lemak pelarut organik → penghilang lemak kimiawi → pencucian air panas → penghilang lemak elektrokimiawi → pencucian air panas → pencucian air dingin → pencucian air dingin → pencucian air dingin → 20%HCl (50 ℃) → pencucian air dingin → pelapisan flash Nikel → pelapisan nikel tanpa listrik. Kerugian dari proses asli: efek penggunaan HCL saja untuk menghilangkan skala oksida tidak baik; pelapisan nikel flash dengan bentuk yang rumit mempengaruhi keseragaman pelapisan nikel tanpa listrik karena cakupannya yang buruk; proses yang lebih lama dapat menyebabkan permukaan baja tahan karat yang baru teroksidasi kembali. Film; larutan pelapisan nikel flash mudah mencemari larutan pelapisan nikel kimiawi, ...

1. Perbedaan Komposisi Kimia: 316L adalah baja tahan karat karbon sangat rendah, sedangkan baja tahan karat 316 adalah baja tahan karat karbon rendah, bukan baja tahan karat karbon sangat rendah. Grade - C Mn Si P S Cr Mo Ni N TP316L min.max. -0.035 -2.0 -1.00 -0.045 -0.030 16.0-18.0 - 10.0-14.0 - 316 min.maks. -0.08 -2.0 -1.00 -0.040 -0.030 16.0-18.0 - 10.0-14.0 - 2. Berbeda dalam Kekuatan Luluh dan Kekuatan Tarik Menurut ASME SA213, untuk Kekuatan Tarik, TP316L 485 menit (N / MM2), 316 515 menit (N / MM2).untuk Kekuatan Luluh, TP316L 170 menit (N / MM2), 316 205 menit (N / MM2). Perbandingan Rentang Komposisi Baja Tahan Karat TP316Pemilihan Baja Tahan Karat 316L untuk Rakitan Filter Gas Semikonduktor Kemurnian TinggiPipa Tabung Piring Batang Tabung Persegi Kalkulator Penghitungan Berat Tabung Kalkulator Penghitungan Tekanan Kerja Pipa Kalkulator Penghitungan Berat Logam 316L Komposisi Kimia 316L Ketahanan terhadap Korosi316L Sifat Fisik316L Sifat Mekanik316L Ketahanan Oksidasi316L Perlakuan Panas316L Fabrikasi

TP304 setara dengan 06Cr19Ni10 (standar GB baru 304), 304 setara dengan 0Cr18Ni9 (standar GB lama 304). Dari segi harga, TP304 juga sekitar USD 65 lebih mahal dari 304 (per metrik ton) Apa kandungan elemennya? Perbedaan utama antara 304 dan TP304 adalah kandungan kromiumnya. Kandungan kromium TP304 lebih tinggi, mencapai lebih dari 18, sehingga ketahanan korosi dan harganya sedikit lebih tinggi daripada GB 304. Oleh karena itu, harga TP304 lebih mahal dari 304, dan bahan-bahannya adalah sebagai berikut: Grade - C Mn Si P S Cr Mo Ni N TP304 min.max. -0.08 -2.0 -1.00 -0.045 -0.030 18.0-20.0 - 8.0-11.0 - 304 min.maks. -0.08 -2.0 -1.00 -0.040 -0.015 17.00-19.5 - 8.0-10.5 - Sifat UmumKomposisi KimiaKetahanan terhadap KorosiKetahanan terhadap PanasSifat FisikSifat MekanikPengelasanPengelasanPengolahan PanasPembersihan304 / 304L / 304LN / 304H Tubing dan PipaBaja Tahan Karat "L" "H" GradePerbedaan antara 304H dan 347HDPerbedaan Antara 304 304L dan 321304 ...

Benda Uji ASTM A312 / ASME SA312 ASTM A269 ASTM A213 / ASME SA213 atau ASTM A213 / A269 Uji Kekuatan Tarik Lot≤100Pcs, 1Pcs Per LotLot>100Pcs, 2 Pcs Per Lot tidak ada persyaratan Lot≤50Pcs, 1Pcs Per LotLot>50Pcs, 2 Pcs Per Lot Uji Kekerasan tidak ada persyaratan 2 Pcs 2 Pcs Uji Pembakaran 5% dari Setiap Lot tidak ada persyaratan Setiap ujung dari satu tabung yang sudah jadi Uji Perataan tidak ada persyaratan 1 Pcs setiap ujung tabung yang sudah jadi Uji Intergranular sesuai pesanan sesuai pesanan sesuai pesanan sesuai pesanan Ukuran Butir 304H / 321H / 316H / 347H tidak ada persyaratan 304H / 321H / 316H / 347H Uji Arus Eddy atau Uji Hidrostatik alternatif alternatif alternatif alternatif alternatif Uji Ultrasonik sesuai pesanan sesuai pesanan sesuai pesanan

Bentuk Material Jenis Diskontinuitas Waktu Penetrasi yang Dapat Dicuci dengan Air* Coran Aluminium Porositas, Penutupan Dingin 5 hingga 15 menit Ekstrusi Aluminium, Tempa Laps NR** Lasan Aluminium Kurang Fusi, Porositas 30 Aluminium Semua Retak, Retak Lelah 30, tidak direkomendasikan untuk retak fatik Porositas Coran Magnesium Porositas, Penutupan Dingin 15 Ekstrusi Magnesium, Tempa Laps tidak direkomendasikan Lasan Magnesium Kurang Fusi, Porositas 30 Magnesium Semua Retak, Retak Lelah 30, tidak direkomendasikan untuk retak fatik Porositas Coran Baja, Penutupan Dingin 30 Ekstrusi Baja, Putaran Tempa tidak direkomendasikan Las Baja Kurang Fusi, Porositas 60 Baja Semua Retak, Retak Fatik 30, tidak direkomendasikan untuk retak fatik Porositas Coran Kuningan & Perunggu, Penutup Dingin 10 Ekstrusi Kuningan & Perunggu, Lap Tempa tidak direkomendasikan Bagian Brazing Kuningan & Perunggu Kurangnya Fusi, Porositas 15 Kuningan & Perunggu Semua Retak 30 Plastik Kuningan & Perunggu Semua Retak 5 hingga 30 Kaca Semua Retak 5 hingga 30...

PT Test Standard International Organization for Standardization (ISO) ISO 3059, Pengujian tidak merusak - Pengujian penetrasi dan pengujian partikel magnetik - Melihat kondisi ISO 3452-1, Pengujian tidak merusak. Pengujian penetrasi. Bagian 1. Prinsip-prinsip umum ISO 3452-2, Pengujian tidak merusak - Pengujian penetran - Bagian 2: Pengujian bahan penetran ISO 3452-3, Pengujian tidak merusak - Pengujian penetran - Bagian 3: Blok uji referensi ISO 3452-4, Pengujian tidak merusak - Pengujian penetran - Bagian 4: Peralatan ISO 3452-5, Pengujian tidak merusak - Pengujian penetrasi - Bagian 5: Pengujian penetrasi pada suhu lebih tinggi dari 50 ° C ISO 3452-6, Pengujian tidak merusak - Pengujian penetrasi - Bagian 6: Pengujian penetrasi pada suhu lebih rendah dari 10 ° C ISO 10893-4: Pengujian tabung baja yang tidak merusak. Inspeksi penetran cair pada tabung baja tanpa sambungan dan yang dilas untuk mendeteksi ketidaksempurnaan permukaan. ISO 12706, Pengujian tidak merusak - Pengujian penetrasi - Kosakata ISO 23277, Pengujian pengelasan tidak merusak - Pengujian penetrasi pengelasan - Tingkat penerimaan Komite Eropa untuk Standardisasi (CEN) EN 1371-1, Pendirian - Inspeksi penetrasi cair ...

Apa itu ASTM A269 dan ASTM A312 / ASME SA312? Spesifikasi Standar ASTM A269 / A269M untuk Pipa Baja Tahan Karat Austenitik Seamless dan Dilas untuk Layanan Umum Spesifikasi Standar ASTM A312 / A312M untuk Pipa Baja Tahan Karat yang Dilas, Dilas, dan Pipa Baja Tahan Karat Austenitik yang Dikerjakan dengan Sangat Dingin StandardItem ASTM A213 ASTM A269 ASTM A312 Grade 304 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H 304 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H 304 304L 304H 304N 304LN316 316L 316Ti 316N 316LN321 321H 310S 310H 309S317 317L 347 347H Kekuatan Luluh (Mpa) ≥170 ； ≥205 ≥170 ； ≥205 ≥170 ； ≥205 Kekuatan Tarik (Mpa) ≥485 ； ≥515 ≥485 ； ≥515 ≥485 ； ≥515 Perpanjangan (%) ≥35 ≥35 ≥35 Uji Hidrostatis OD (mm) Tekanan maks (MPa) OD (mm) Tekanan maks (MPa) OD (mm) Tekanan maks (MPa) D <25.4, 7Mpa D <25,4, 7Mpa D≤88,9, 17MPa 25,4≤D <38,1, 10Mpa 25,4≤D <38,1, 10Mpa 38,1≤D <50,8, 14Mpa 38,1≤D <50,8, 14Mpa 50,8≤D <76.2, 17MPa 50.8≤D88.9, 19MPa 76.2≤D<127, 24MPa 76.2≤D<127, 24MPa D≥127, 31Mpa D≥127, 31Mpa P = 220.6t / D ...

Pipa baja tahan karat melengkung ke arah panjang, dan tingkat kelengkungannya disebut tingkat kelengkungan (Kelurusan). Kelengkungan yang ditentukan dalam standar umumnya dibagi menjadi dua jenis berikut: A. Kelengkungan lokal: Gunakan penggaris lurus satu meter untuk bersandar pada tikungan maksimum pipa baja tahan karat, dan ukur tinggi akor (mm), yang merupakan nilai kelengkungan lokal. Satuannya adalah mm/m, dan ekspresinya adalah 2,5 mm/m. . Metode ini juga cocok untuk kelengkungan ujung tabung. B. Kelengkungan total dari panjang total: Gunakan tali tipis untuk mengencangkan dari kedua ujung pipa, ukur tinggi akor maksimum (mm) pada tikungan pipa baja, lalu ubah menjadi persentase panjang (dalam meter), yaitu panjang pipa baja tahan karat Kelengkungan panjang penuh arah. Misalnya: panjangnya ...

Pada penampang pipa baja tahan karat, terdapat fenomena bahwa diameter luarnya tidak sama, yaitu ada diameter luar maksimum dan minimum yang tidak harus tegak lurus satu sama lain. Perbedaan antara diameter luar maksimum dan diameter luar minimum adalah Ovality (atau kebulatan). Untuk mengontrol ovalitas, beberapa standar pipa baja tahan karat menetapkan toleransi ovalitas yang diijinkan, yang umumnya ditetapkan tidak melebihi 80% dari toleransi diameter luar (diterapkan setelah negosiasi antara pemasok dan pembeli). Standar persyaratan umum untuk pipa baja tahan karat adalah ASTM A999. Toleransi di bawah OD pada semua ukuran adalah -0,031 ". Toleransi berlebih meningkat dengan ukuran OD tetapi untuk kisaran 1-1 / 2 hingga 4 NPS, toleransi plus juga 0,031 ". Kelonggaran toleransi ovalitas tambahan diizinkan untuk pipa dengan ketebalan dinding tipis yang ditentukan ...

Ketebalan dinding pipa baja tahan karat tidak bisa sama di semua tempat, dan ada ketebalan dinding yang secara obyektif tidak sama pada penampang melintang dan badan pipa memanjang, yaitu ketebalan dinding yang tidak rata. Untuk mengontrol ketidakseragaman ini, beberapa standar pipa baja tahan karat seperti ASTM A312, ASTM A999 menetapkan indeks yang diijinkan untuk ketebalan dinding yang tidak rata, yang umumnya ditentukan untuk tidak melebihi 80% dari toleransi ketebalan dinding (diterapkan setelah negosiasi antara pemasok dan pembeli). ASTM A269 Toleransi Layanan Umum Dilas dan Mulus, Toleransi Inci, Toleransi Inci, Toleransi Inci, Toleransi Inci, Ukuran Inci OD, Inci Ovality Dinding2 x Tol, In. Panjang Potong (b), Dalam. Kurang dari 1/2 ± 0,005 ± 15% - +1/8-0 Lebih dari 1/2 hingga 1-1 / 2 ± 0,005 ± 10% -0,065 +1/8-0 Lebih dari 1-1 / 2 hingga 3-1 / 2 ± 0,010 ± 10% -0,095 +3/16-0 Lebih dari 3-1 / 2 hingga 5-1 / 2 ± 0,015 ± 10% -0,150 +3/16-0 Lebih dari 5-1 / 2 hingga 8 ± 0,030 ± 10% - +3/16-0 Referensi Terkait:Berat BajaMetode Perhitungan Kepadatan Baja Tahan KaratMenghitung ...

Panjang pengiriman juga disebut panjang yang dibutuhkan oleh pengguna atau panjang pesanan. Standar ini memiliki peraturan berikut tentang panjang pengiriman: A. Panjang normal / Panjang Acak (juga disebut panjang tidak tetap): Setiap tabung baja tahan karat yang panjangnya berada dalam kisaran panjang yang ditentukan oleh standar dan tidak memiliki persyaratan panjang tetap disebut panjang normal. Misalnya, standar pipa baja tahan karat struktural menetapkan: pipa baja canai panas (diekstrusi, diperluas) 3000mm ~ 12000mm; pipa baja yang ditarik dingin (digulung) 2000mm ~ 10500mm. B. Panjang Tetap: Panjang tetap harus berada dalam kisaran panjang yang biasa, yang merupakan dimensi panjang tetap tertentu yang disyaratkan dalam kontrak. Namun, tidak mungkin untuk memotong panjang panjang tetap absolut dalam operasi aktual, sehingga standar menetapkan nilai deviasi positif yang diijinkan untuk panjang panjang tetap. Ambil contoh standar pipa baja tahan karat struktural: Tingkat hasil produksi dengan panjang tetap ...

Penyimpangan Dalam proses produksi, karena ukuran sebenarnya sulit untuk memenuhi persyaratan ukuran pipa nominal, yaitu seringkali lebih besar atau lebih kecil dari ukuran nominal, maka standar menetapkan bahwa ada perbedaan antara ukuran sebenarnya dan ukuran nominal pipa baja tahan karat. Perbedaan positif disebut deviasi positif, dan perbedaan negatif disebut deviasi negatif. Toleransi Standar menetapkan bahwa jumlah nilai absolut dari deviasi positif dan negatif pipa baja tahan karat disebut toleransi, juga disebut "zona toleransi". Untuk ketebalan dinding kami memiliki dua pilihan, Ketebalan Dinding Minimum dan Ketebalan Dinding Rata-rata. Perbedaan Spesifikasi Standar memiliki permintaan toleransi yang berbeda. Terutama ditentukan dalam ASTM A999 atau ASTM A1016 atau EN 10216-5 Referensi Terkait: Jadwal PipaUkuran Tabung Baja Tahan KaratASME B36.10M - 2015 Pipa Baja Tempa Dilas dan MulusASME B36.19M - Pipa Baja Tahan Karat...

A. Ukuran Pipa Nominal: Ini adalah ukuran nominal yang ditentukan dalam standar seperti ASME B36.10m, ASME B36.19m, ukuran ideal yang diharapkan oleh pengguna dan produsen, dan ukuran pesanan yang ditentukan dalam kontrak. B. Ukuran Pipa Aktual: Ini adalah ukuran aktual yang diperoleh selama proses produksi, yang seringkali lebih besar atau lebih kecil dari ukuran nominal. Fenomena lebih besar atau lebih kecil dari ukuran nominal ini disebut deviasi. Referensi Terkait:Jadwal PipaUkuran Tabung Baja Tahan KaratASME B36.10M Pipa Baja Tempa Dilas dan MulusASME B36.19M Jadwal Pipa Baja Tahan KaratUkuran PengukurUkuran Pipa NominalUkuran Pipa Baja Tahan KaratUkuran Lembaran LogamUkuran Pipa Baja Tahan KaratUkuran Tabung Baja Tahan Karat Bagan Pipa Standar ANSIBagan inci ke mmBWG - Birmingham Wire GaugeA.S.W.G. American Standard Wire GaugeToleransi Pengukur dari Stainless SteelTabel Konversi Temperatur, Panjang, Massa, TekananNPS-Nominal-Ukuran-Pipa dan DN - Nominal DiameterToleransi ISO Untuk PengencangBagan Toleransi ISOTabel Toleransi ISOProses Pemesinan yang terkait dengan Tingkat Toleransi ISO ITTabel Berat Ketebalan Baja Tahan Karat...

Karena kekuatan baja Duplex yang tinggi, biasanya memungkinkan untuk menghemat material, seperti mengurangi ketebalan dinding pipa. Ambil contoh penggunaan SAF2205 dan SAF2507. SAF2205 cocok untuk digunakan di lingkungan yang mengandung klorin. Bahan ini cocok untuk penyulingan minyak atau media proses lainnya yang dicampur dengan klorida. SAF2205 sangat cocok untuk penukar panas yang menggunakan larutan berair yang mengandung klorin atau air payau sebagai media pendingin. Bahan ini juga cocok untuk larutan asam sulfat encer dan asam organik murni dan campurannya. Seperti: pipa minyak di industri minyak dan gas alam: desalinasi minyak mentah di kilang minyak, pemurnian gas yang mengandung belerang, peralatan pengolahan air limbah; sistem pendingin yang menggunakan air payau atau larutan yang mengandung klor. Dibandingkan dengan baja tahan karat austenitik 1) Kekuatan luluh lebih dari dua kali lipat dari baja tahan karat austenitik biasa, dan memiliki ketangguhan plastik yang cukup untuk ...

C C Si Si Mn Mn P P S S Cr Cr Ni Ni Mo Mo N N Cu Cu Ti Ti Nb Nb min max min max min max min max min max min max DIN 17456 1.4301 0.00 0.070 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.00 8.00 10.50 DIN 17456 1.4306 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 18.00 20.00 10.00 12.00 DIN 17456 1.4311 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.50 8.50 11.50 DIN 17456 1.4541 0.00 0.080 0.00 1.00 0.00 2.00 0.00 0.045 0.00 0.015 17.00 19.00 9.00 12.00 ...

C C Si Si Mn Mn P P S S Cr Cr Ni Ni Mo Mo N N Cu Cu Ti Ti Nb Nb min max min max min max min max min max min max min max J3459 SUS304TP 0.00 0.080 0.00 1.00 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20.00 8.00 11.00 J3459 SUS304HP 0.040 0.100 0.00 0.75 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20.00 8.00 11.00 J3459 SUS304LTP 0.00 0.030 0.00 1.00 0.00 2.00 0.00 0.040 0.00 0.030 18.00 20.00 9.00 13.00 J3459 SUS310STP 0.00 0.080 0.00 1.50 0.00 2.00 0.00 0.040 0.00 0.030 24.00 26.00 19.00 22.00 ...

Pipa baja tahan karat dan Tabung Baja Tahan Karat adalah bahan yang umum digunakan, dan banyak digunakan pada peralatan dan komponen mekanis yang membutuhkan kinerja keseluruhan yang baik (ketahanan terhadap korosi dan sifat mampu bentuk). Untuk mempertahankan ketahanan korosi yang melekat pada baja tahan karat, baja harus mengandung lebih dari 18% kromium dan lebih dari 8% nikel. Pipa seamless stainless steel diproduksi sesuai dengan ASTM A312 dan Tabung Baja Tahan Karat diproduksi sesuai dengan ASTM A213 / ASME SA213 Jika diameter bagian dalam pipa baja tahan karat lebih besar dari 26mm, maka kekerasan dinding bagian dalam pipa dapat diuji dengan penguji kekerasan Rockwell atau permukaan Rockwell. Solusi pipa baja tahan karat anil dengan diameter bagian dalam tabung baja tahan karat di atas 6.0mm dan ketebalan dinding di bawah 13mm dapat menggunakan penguji kekerasan Webster W-B75, yang sangat cepat dan mudah untuk diuji, dan ...