Grades d'acier inoxydable austénitique Types
Types d'acier inoxydable austénitique
| Chine GB | Code numérique unifié ISO | ASTM / ASME Grade | Code UNS | Code EN | Entreprise Commercial Grade |
| 06Cr19Ni10 | S30408 | 304 | S30400 | 1.4301 | - |
| 07Cr19Ni10 | S30409 | 304H | S30409 | 1.4948 | - |
| 022Cr19Ni10 | S30403 | 304L | S30403 | 1.4307 | - |
| 022Cr19Ni10N | S30453 | 304LN | S30453 | 1.4311 | - |
| - | - | Super304 | S30432 | - | Super304H(NSSMC) |
| 06Cr18Ni11Ti | S32168 | 321 | S32100 | 1.4541 | - |
| 07Cr18Ni11Ti | S32169 | 321H | S32109 | 1.494 | - |
| 06Cr17Ni12Mo2 | S31608 | 316 | S31600 | 1.4401 | - |
| 022Cr17Ni12Mo2 | S31603 | 316L | S31603 | 1.4404 | - |
| 022Cr17Ni12Mo2N | S31653 | 316LN | S31653 | 1.4406 | - |
| 06Cr17Ni12Mo3Ti | S31668 | 316Ti | S31635 | 1.4571 | - |
| 00Cr17Ni14Mo2 | 316LMoD/316LUG | S31603 | 1.4435 | - | |
| 022Cr19Ni13Mo3 | S31703 | 317L | S31703 | 1.4438 | - |
| 022Cr19Ni16Mo5N | S31723 | 317LMN | S31725 | 1.4439 | - |
| 06Cr25Ni20 | S31008 | 310S | S31008 | 1.4845 | - |
| 00Cr19Ni11 | - | 304L | S30403 | 1.4307 | 3RE12(Sandvik) |
| - | - | 310L | S31002 | 1.4335 | 2RE10(Sandvik) |
| 20Cr25Ni20 | S31020 | 310H | S31009 | 1.4821 | |
| 16Cr25Ni20Si2 | S38340 | 314 | - | 1.4841 | |
| 022Cr25Ni22Mo2N | S31053 | 310MoLN | S31050 | 1.4466 | 2RE69(Sandvik) |
| - | - | 310HCbN | S31042 | - | HR3C(NSSMC) |
| 07Cr18Ni11Nb | S34749 | 347H | S34709 | 1.4942 | - |
| - | - | 347HFG | S34710 | - | - |
| 015Cr21Ni26M5Cu2 | S31782 | 904L | N08904 | 1.4539 | 2RK65(Sandvik) |
| 015Cr20Ni18Mo6CuN | S31252 | S31254 | S31254 | 1.4547 | 254SMO(Sandvik) |
| 00Cr20Ni24Mo6N | - | N08367 | N08367 | - | AL6XN, AL6XN plus(ATI) |
| 00Cr21Ni25Mo6CuN | - | N08926 | N08926 | 1.4529 | - |
| 015Cr24Ni22Mo8Mn3CuN | S32652 | S32654 | S32654 | 1.4652 | 654SMO(Outokumpu) |
| 00Cr22Ni27Mo7CuN | - | S31277 | S31277 | - | - |
Composition de l'acier inoxydable austénitique
| ASME | AISI UNS | FR | JIS | Cmax | Cr | Ni | Mo | Cu | Autres |
| TP 304 | S30400 | 1.4301 | SUS 304 | 0.08 | 18.0 | 8.0 | |||
| TP 304 L | S30403 | 1.4307 | SUS 304L | 0.035 | 18.0 | 8.0 | |||
| TP 304H | S30403 | 1.4948 | SUS 304H | 0.04-0.1 | 18.0 | 8.0 | |||
| TP 321 | S32100 | 1.4541 | SUS 321 | 0.080 | 17.0 | 9.0 | 5(C+N)<Ti< 0.7 | ||
| TP 321H | S32100 | 1.4878 | SUS 321 | 0.04-0.1 | 17.0 | 9.0 | 4(C+N)<Ti< 0.7 | ||
| TP 347 | S3470 | 1.4550 | SUS 347 | 0.08 | 17.0 | 9.0 | 10×C<Nb<1,10 | ||
| TP 347H | S34709 | SUS 347 | 0.04-0.1 | 17.0 | 9.0 | 8×C<Nb<1,10 | |||
| TP 316 | S31600 | 1.4401 | SUS 316 | 0.08 | 16.0 | 10.0 | 2.0 | ||
| TP 316L | S31603 | 1.4404 | SUS 316L | 0.035 | 16.0 | 10.0 | 2.0 | ||
| TP 316H | S31609 | SUS 316H | 0.04-0.1 | 16.0 | 10.0 | 2.0 | |||
| TP 316 Ti | S31635 | 1.4571 | SUS 316Ti | 0.08 | 16.0 | 10.0 | 2.0 | N:0.10 min 5(C+N)<Ti< 0,7 | |
| TP 317 | S31700 | 1.4438 | SUS 317L | 0.08 | 18.0 | 11.0 | 3.0 | ||
| TP 317L | 31703 | 1.4438 | SUS 317L | 0.035 | 18.0 | 11.0 | 3.0 | ||
| TP 309S | S30908 | 1.4833 | SUS 309S | 0.08 | 22.0 | 12.0 | |||
| TP 310 | S31000 | 1.4841 | SUS 310 | 0.08 | 24.0 | 19.0 | |||
| TP 310S | S31008 | 1.4845 | SUS 310S | 0.08 | 24.0 | 19.0 | |||
| TP 310H | S31009 | 1.4845 | SUS 310H | 0.04-0.10 | 24.0 | 19.0 | |||
| TP 904L | N08904 | 1.4539 | SUS 904L | 0.020 | 19.0> | 23.0 | 4.0 | 1.00-2.00 |
Références connexes :
Acier inoxydable austénitique
Acier inoxydable superaustenitique
Grades d'acier inoxydable austénitique Types
Acier inoxydable austénitique pour fixations en bois
Propriétés magnétiques de l'acier inoxydable austénitique
Tableau de comparaison des nuances d'acier inoxydable austénitique
Durcissement superficiel de l'acier inoxydable austénitique à l'azote
Effet de la composition de l'acier austénitique et du traitement thermique
Comparaison de la résistance et de la vulnérabilité des aciers austénitiques et duplex
Traitement thermique de détente pour l'acier inoxydable austénitique
Mesure du mécanisme de l'écrouissage de l'acier austénitique
Effet de la composition sur la perméabilité magnétique de l'acier austénitique
Effet du travail à froid et du traitement thermique de l'acier inoxydable austénitique